Hydroxyapatite (HAp)—[Ca₁₀ (PO₄)₆(OH) ₂] has a similar chemical composition to bone material, making it the main mineral supplement in bone-making. Due to its high biocompatibility, hydroxyapatite is widely used in the repair of bone deficiencies and in the production of dental or orthopedic implants. In this research, hydroxyapatite nanopowder was synthesized using a hydrothermal technique. Fourier Transform Infrared Spectroscopy (FTIR) and transmission electron microscopy (TEM) were used to investigate the chemical structure and morphology of the synthesized hydroxyapatite powder. X-ray diffraction (XRD) was used to evaluate the phase analysis of HAp nanopowder. In addition, bioactivity HAp assessment was conducted by scanning electron microscopy (SEM) attached with Energy Dispersive X-Ray Spectroscopy (EDX) analysis. Response Surface Methodology (RSM) with central composite design (CCD) was used in order to determine the optimal conditions for yield, size, and crystallinity. Three independent variables (pH, temperature, and hydrothermal treatment time) were investigated. The yield was observed to increase in alkaline conditions; pH showed the greatest influence on the yield, size, and crystallinity of the synthesized hydroxyapatite, based on Analysis of Variance. The results of bioactivity evaluation are showed high bioactivity due to the formation of apatite on the surface of the synthesized nanopowder.

Nanosilica was surface modified with polyaniline and incorporated into polyurethane to form a polymer matrix capable of entrapping a liquid electrolyte and functioning as quasi-solid-state electrolyte in the dye-sensitized solar cells. The effect on the S−PANi distribution, surface morphology, thermal stability, gel content, and structural change after varying the PEG molecular weight of the polyurethane matrix was analyzed. Quasi-solid-state electrolytes were prepared by immersing the polyurethane matrix into a liquid electrolyte and the polymer matrix absorbency, conductivity, and ion diffusion were investigated. The formulated quasi-solid-state electrolytes were applied in dye-sensitized solar cells and their charge recombination, photovoltaic performance, and lifespan were measured. The quasi-solid-state electrolyte with a PEG molecular weight of 2000 gmol⁻¹ (PU−PEG 2000) demonstrated the highest light-to-energy conversion efficiency, namely, 3.41%, with an open-circuit voltage of 720 mV, a short-circuit current of 4.52 mA cm⁻², and a fill factor of 0.63.

The utilization of vegetable oil in the production of polymeric material has gained interest due to its proven ability to replace nonrenewable petroleum sources, as it is readily modified via chemical reaction to produce polyol and subsequently for polyurethane production. Jatropha oil (JO), a second-generation feedstock, is one of the suitable candidates for polyester polyol synthesis because it contains a high percentage of unsaturated fatty acids. In this study, jatropha-based polyester polyols (JOLs) with different hydroxyl values were successfully synthesized via a two-step method: epoxidation followed by oxirane ring-opening reaction. Ring-opening reagents; methanol, ethanol, and isopropanol were used to produce polyol with hydroxyl number of 166, 180, and 189 mg/KOH, respectively. All the synthesized JOLs exhibited a Newtonian to shear thinning behavior in the measured shear rate ranges from 10 to 1000 s⁻¹ at 25 °C. The viscosity of a JOL ring-opened with methanol, isopropanol, and ethanol was 202, 213, and 666 mPa·s, respectively, at 20 °C and 100 s⁻¹, which is within the range of commercially available polyols. Successively, the JOLs were reacted with isophorone diisocyanate (IPDI) to produce polyurethane prepolymer by utilizing 2,2-dimethylol propionic acid (DMPA) as an emulsifier. The prepolymer was then dispersed in water to produce a waterborne polyurethane dispersion. Colloidal stability of the jatropha-based polyurethane dispersions (JPUDs) were investigated by particle size analysis. A JPUD with a small particle size in the range of 6.39 to 43.83 nm was obtained, and the trend was associated with the soft segment of the polyol in the formulation. The zeta potentials of the JPUs ranged from −47.01 to −88.9 mV, indicating that all synthesized JPUs had high dispersity and stability. The efficient synthesis procedure, low cost, and excellent properties of the resulting product are thought to offer an opportunity to use jatropha oil as a sustainable resource for polyester polyol preparation.

Recently, composite scaffolding has found many applications in hard tissue engineering due to a number of desirable features. In this present study, hydroxyapatite/bioglass (HAp/BG) nanocomposite scaffolds were prepared in different ratios using a hydrothermal approach. The aim of this research was to evaluate the adhesion, growth, viability, and osteoblast differentiation behavior of human Wharton’s-jelly-derived mesenchymal stem cells (hWJMSCs) on HAp/BG in vitro as a scaffold for application in bone tissue engineering. Particle size and morphology were investigated by TEM and bioactivity was assessed and proven using SEM analysis with hWJMSCs in contact with the HAp/BG nanocomposite. Viability was evaluated using PrestoBlue^TM assay and early osteoblast differentiation and mineralization behaviors were investigated by ALP activity and EDX analysis simultaneously. TEM results showed that the prepared HAp/BG nanocomposite had dimensions of less than 40 nm. The morphology of hWJMSCs showed a fibroblast-like shape, with a clear filopodia structure. The viability of hWJMSCs was highest for the HAp/BG nanocomposite with a 70:30 ratio of HAp to BG (HAp70/BG30). The in vitro biological results confirmed that HAp/BG composite was not cytotoxic. It was also observed that the biological performance of HAp70/BG30 was higher than HAp scaffold alone. In summary, HAp/BG scaffold combined with mesenchymal stem cells showed significant potential for bone repair applications in tissue engineering.