This article is aimed to study the effect of laser treatment of AISI 304 stainless steel on the corrosion resistance and chemical composition of the surface layer. The samples were irradiated using two quite different laser sources: IPG Yb:glass fibre laser (τ = 230 ns, λ = 1062 nm) and Trumpf TruMicro Series 2020 fiber laser (τ = 260 fs–20 ps, λ = 1030 nm) that is, in both the long and ultra-short pulse duration regime. It allowed the observation of completely different microstructures and chemical composition of the surface layer. In this study, the morphology of the samples was accessed using both Keyence digital microscope and Olympus Lext 5000 profilometer. The corrosion resistance was examined in 3% NaCl solution using both potentiodynamic measurement and Electrochemical Impedance Spectroscopy. In order to examine the change in chemical composition of the surface layer, the X-ray photoelectron spectroscopy study was performed. Results show that the use of a long laser pulse contributes to the formation of a thin, tight, rich in chromium passive layer, which significantly improves corrosion resistance in comparison to the reference sample. Different behaviour is observed after irradiation with an ultra-short pulse duration laser.

In this research we subjected samples of poly(L-lactide) (PLLA) extruded film to ultraviolet (193 nm ArF excimer laser) radiation below the ablation threshold. The modified film was immersed in Simulated Body Fluid (SBF) at 37 °C for 1 day or 7 days to obtain a layer of apatite ceramic (CaP) coating on the modified PLLA surface. The samples were characterized by means of optical profilometry, which indicated an increase in average roughness (Ra) from 25 nm for the unmodified PLLA to over 580 nm for irradiated PLLA incubated in SBF for 1 day. At the same time, the water contact angle decreased from 78° for neat PLLA to 35° for irradiated PLLA incubated in SBF, which suggests its higher hydrophilicity. The obtained materials were investigated by means of cell response fibroblasts (3T3) and macrophage-like cells (RAW 264.7). Properties of the obtained composites were compared to the unmodified PLLA film as well as to the UV-laser irradiated PLLA. The activation of the PLLA surface by laser irradiation led to a distinct increase in cytotoxicity, while the treatment with SBF and the deposition of apatite ceramic had only a limited preventive effect on this harmful impact and depended on the cell type. Fibroblasts were found to have good tolerance for the irradiated and ceramic-covered PLLA, but macrophages seem to interact with the substrate leading to the release of cytotoxic products.

We present a comparison of the influence of the conditioning temperature of microspheres made of medical grade poly(L-lactide) (PLLA) and polylactide with 4 wt % of D-lactide content (PLA) on the thermal and structural properties. The microspheres were fabricated using the solid-in-oil-in-water method for applications in additive manufacturing. The microspheres were annealed below the glass transition temperature (T_g), above T_g but below the onset of cold crystallization, and at two temperatures selected from the range of cold crystallization corresponding to the crystallization of the α’ and α form of poly(L-lactide), i.e., at 40, 70, 90, and 120 °C, in order to verify the influence of the conditioning temperature on the sinterability of the microspheres set as the sintering window (SW). Based on differential scanning calorimetry measurements, the SWs of the microspheres were evaluated with consideration of the existence of cold crystallization and reorganization of crystal polymorphs. The results indicated that the conditioning temperature influenced the availability and range of the SWs depending on the D-lactide presence. We postulate the need for an individual approach for polylactide powders in determining the SW as a temperature range free of any thermal events. We also characterized other core powder characteristics, such as the residual solvent content, morphology, particle size distribution, powder flowability, and thermal conductivity, as key properties for successful laser sintering. The microspheres were close to spheres, and the size of the microspheres was below 100 µm. The residual solvent content decreased with the increase of the annealing temperature. The thermal conductivities were 0.073 and 0.064 W/mK for PLA and PLLA microspheres, respectively, and this depended on the spherical shape of the microspheres. The wide angle X-ray diffraction (WAXD) studies proved that an increase in the conditioning temperature caused a slight increase in the crystallinity degree for PLLA microspheres and a clear increase in crystallization for the PLA microspheres.

In this paper, the impact of thin Au–Sn layers morphology on the formation of laser-induced alloy nanoparticles (ANPs) is investigated. Also, the changes in composition observed over time in thin films are analysed. The influence of deposition rate and elemental composition was studied. The tests were performed on five sets of samples of varying atomic ratios of Au–Sn and film thickness, for which the optical parameters were measured with the spectroscopic ellipsometry technique (SE). The samples were dewetted with a nanosecond Yb:glass fibre laser. All fabricated surfaces were analysed using scanning electron microscopy (SEM). Moreover, the chemical composition of obtained structures was analysed using X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM).

This paper presents the impact of the initial surface finish of commonly used AISI 304 stainless steel on its corrosion resistance before and after being treated with laser radiation. Three distinct surface preparations were examined: brushed, 2B cold-rolled, and polished. All samples were irradiated using a Yb3+:glass laser system of nanosecond pulse duration in an air environment. As a result of laser irradiation, thin oxide layers were formed on the steel surface. Our previous work showed that these layers may significantly increase the corrosion resistance of cold-rolled stainless steel compared to untreated samples. This work expands upon these findings by exploring the effect of laser irradiation on brushed and polished surfaces, keeping the steel’s chemical composition the same so we could focus mainly on how the surface finish influences corrosion. The results demonstrate that the corrosion behavior is correlated with surface roughness and yet modified by laser-induced oxidation. For brushed and cold-rolled samples, the corrosion current density reached a minimum at a laser fluence of 40 J/cm2, corresponding to the highest polarization resistance. Meanwhile, polished samples (which have the lowest initial roughness) did not show much improvement after irradiation. The conducted studies showed a significant influence of surface roughness on corrosion and a change in this resistance as a result of laser annealing of the surface.

Comparison of the influence of conditioning temperature of microspheres made of medical grade poly(L-lactide) (PLLA) and polylactide with 4wt.% of D-lactide content (PLA), on its thermal and structural properties is presented. The microspheres were fabricated by solid-in-oil-in-water method for application in additive manufacturing. The microspheres were annealed below glass transition temperature (Tg), above Tg but below onset of cold crystallization, and at two temperatures selected from the range of cold crystallization corresponding to crystallization of α’ and α form of poly(L-lactide) respectively, i.e., at 40°C, 70°C, 90°C and 120°C, in order to verify the influence of conditioning temperatures on sinterability of microspheres set as sintering window (SW). Based on differential scanning calorimetry measurements SW of microspheres were evaluated with consideration of existence of cold crystallization and reorganization of crystal polymorph. The results indicate that the conditioning temperature influence on availability and range of SW that depending on the D-lactide presence. We postulate the need for an individual approach for polylactide powders in determining the SW as a temperature range free of any thermal events. Moreover, other core powder characteristic, such as residual solvent content, morphology, particle size distribution, powder flowability and thermal conductivity, as a key property for successful laser sintering, are characterized. The microspheres are close to sphere and the size of microspheres are below 100 µm. Residual solvents content decreases with the increase of annealing temperature. The thermal conductivity is 0.073 W/mK and 0.064 W/mK for PLA and PLLA microspheres, respectively, and it depends on the spherical shape of the microspheres. Furthermore, the WAXD studies prove that an increase in the conditioning temperature causes a slight increase in crystallinity degree for PLLA microspheres and clear increase in crystallization for PLA microspheres.