This paper reports the findings of the effect of elevated temperature on the compressive strength and durability properties of crumb rubber engineered cementitious composite (CR-ECC). The CR-ECC has been tested for its compressive strength and chemical resistance test against acid and sulphate attack. Different proportions of crumb rubber (CR) in partial replacement to the fine aggregate and polyvinyl alcohol (PVA) fiber have been utilized from 0 to 5% and 0 to 2%. The experiments were designed based on a central composite design (CCD) technique of response surface methodology (RSM). After 28 days curing, the samples were preconditioned and exposed to high temperatures of 100 °C, 200 °C, 300 °C, 400 °C, 500 °C, 600 °C, 700 °C, 800 °C, 900 °C, and 1000 °C for one hour. Although the residual compressive strength of CR-ECC was negatively affected by elevated temperature, no explosive spalling was noticed for all mixes, even at 1000 °C. Results indicated that CR-ECC experiences slight weight gain and a reduction in strength when exposed to the acidic environment. Due to the reduced permeability, CR-ECC experienced less effect when in sulphate environment. The response models were generated and validated by analysis of variance (ANOVA). The difference between adjusted R-squared and predicted R-squared values for each model was less than 0.2, and they possess at least a 95% level of confidence.

Waste tire and fly ash (FA) are two waste materials whose disposal and rapid rate of accumulation are among the pressing sources of concern and threat to the environment. Although much research exists on the use of these materials in cementitious composites, very little literature is available on the effectiveness of combining them in high volumes for concrete production. This work aimed to utilize crumb rubber (CR) from waste tires as a partial replacement of fine aggregate at 15%, 22.25%, and 30% by volume, and high-volume fly ash (HVFA) replacement of cement at 50%, 60%, and 70% (by weight of cementitious materials) to produce high-volume fly ash–crumb rubber concrete (HVFA–CRC). Using the central composite design (CCD) option of the response surface methodology (RSM), 13 mixes were produced with different combinations and levels of the CR and FA (the input factors) on which the responses of interest (compressive, flexural, and tensile strengths) were experimentally investigated. Furthermore, the composite influence of CR and HVFA on the workability of the concrete was assessed using the slump test. The results showed a decline in the mechanical properties with increasing replacement levels of the CR and HVFA. However, up to 22.25% and 60% of CR and HVFA replacements, respectively, produced a structural HVFA–CRC with a compressive strength of more than 20 MPa at 28 days. Response predictive models were developed and validated using ANOVA at a 95% confidence level. The models had high R² values ranging from 95.26 to 97.74%. Multi-objective optimization was performed and validated with less than 5% error between the predicted and experimental responses.

Producing high-strength self-compacting concrete (SCC) requires a low water-cement ratio (W/C). Hence, using a superplasticizer is necessary to attain the desired self-compacting properties at a fresh state. The use of low W/C results in very brittle concrete with a low deformation capacity. This research aims to investigate the influence of crumb rubber (CR), fly ash (FA), and nanosilica (NS) on SCC’s workability and mechanical properties. Using response surface methodology (RSM), 20 mixes were developed containing different levels and proportions of FA (10–40% replacement of cement), CR (5–15% replacement of fine aggregate), and NS (0–4% addition) as the input variables. The workability was assessed through the slump flow, T₅₀₀, L-box, and V-funnel tests following the guidelines of EFNARC 2005. The compressive, flexural, and tensile strengths were determined at 28 days and considered as the responses for the response surface methodology (RSM) analyses. The results revealed that the workability properties were increased with an increase in FA but decreased with CR replacement and the addition of NS. The pore-refining effect and pozzolanic reactivity of the FA and NS increased the strengths of the composite. Conversely, the strength is negatively affected by an increase in CR, however ductility and deformation capacity were significantly enhanced. Response surface models of the mechanical strengths were developed and validated using ANOVA and have high R² values of 86–99%. The optimization result produced 36.38%, 4.08%, and 1.0% for the optimum FA, CR, and NS replacement levels at a desirability value of 60%.

Despite the excellent ductility and energy absorption properties of engineered cementitious composites (ECCs), a low modulus of elasticity and excessive drying shrinkage remain some of its major disadvantages. With the current trend in the application of nanotechnology in cementitious composites research, the effect of graphene oxide (GO) on the properties of ECCs is yet to be fully investigated, despite its promising results in ordinary cement paste, mortar, and concrete. ECCs need extensive material tailoring to provide the required mechanical characteristics and controlled fracture size with strain-hardening behavior. Striking a balance between these crucial hardened aspects of ECC without compromising any desired properties is a challenge. Hence, the main aim of the study reported in this paper is to use the response surface methodology (RSM) multi-objective optimization technique to identify an appropriate GO content via the weight of cement and also the volume fraction of polyvinyl alcohol (PVA) fiber as input variables that positively impact ECCs’ properties. Using RSM’s central composite design (CCD), 13 mixtures of various combinations of the variables (GO: 0.05%, 0.065%, 0.08%; PVA: 1%, 1.5%, 2%) were developed. Six responses were studied, including compressive strength, direct tensile strength, tensile capacity, flexural strength, modulus of elasticity, Poisson’s ratio, and drying shrinkage. Moreover, the microstructural properties of the composites were assessed using field-emission scanning electron microscopy (FESEM) and mercury intrusion porosimetry (MIP). The outcomes revealed that all the properties of ECCs were significantly enhanced by adding an optimum amount of 0.05% GO and 1–1.5% PVA fiber volume fractions. A maximum increase in 30%, 35%, 49%, and 33.9% in the compressive strength, direct tensile strength, flexural strength, and modulus of elasticity, respectively, of the mixes with 0.05% GO addition was recorded. It is demonstrated that the use of 0.05% GO as a nanoscale particle can provide good outputs for the construction industry.

Graphene oxide-modified rubberized engineered cementitious composite (GO-RECC) is attracting the attention of researchers because of the reported benefits of the GO and crumb rubber (CR) on the strength and deformation properties of the composite. While it is well established that GO negatively affects the workability of cementitious composites, its influence on the attainment of the desired self-compacting (SC) properties of ECC has not yet been thoroughly investigated, especially when combined with crumb rubber (CR). In addition, to simplify the number of trial mixes involved in designing SC-GO-RECC, there is a need to develop and optimize the process using Design of Experiment (DOE) methods. Hence, this research aims to investigate and model using response surface methodology (RSM), the combined effects of the GO and CR on the SC properties of ECC through the determination of T₅₀₀, slump flow, V-funnel, and L-box ratio of the SC-GORECC as the responses, following the European Federation of National Associations Representing for Concrete (EFNARC) 2005 specifications. The input factors considered were the GO by wt.% of cement (0.02, 0.04, 0.06, and 0.08) and CR as a replacement of fine aggregate by volume (5, 10, and 15%). The results showed that increasing the percentages of GO and CR affected the fresh properties of the SC-GORECC adversely. However, all mixes have T₅₀₀ of 2.4 to 5.2 s, slump flow of 645 to 800 mm, V-funnel time of 7.1 to 12.3 s, and L-box ratio (H2/H1) of 0.8 to 0.98, which are all within acceptable limits specified by EFNARC 2005. The developed response prediction models were well fitted with R² values ranging from 91 to 99%. Through the optimization process, optimal values of GO and CR were found to be 0.067% and 6.8%, respectively, at a desirability value of 1.0.