Application of hydrophobic coatings, such as carnauba wax nanoemulsions, combined with natural antimicrobials, has been demonstrated to be an effective solution in extending the shelf life of fruits. The present study evaluated the effectiveness of carnauba wax nanoemulsion (CWN) coatings containing free or encapsulated with β-cyclodextrin (β-CD) essential oils of Syzigium aromaticum (CEO) and Mentha spicata (MEO) for the post-harvest conservation of papaya fruit. The chemical composition of the essential oils (EOs) was analyzed using GC-MS. Subsequently, coatings incorporating free and encapsulated EOs were prepared and applied to papaya fruit. Fruit was evaluated for post-harvest quality parameters during 15 days of storage. Clove essential oil presented as main compounds eugenol (89.73%), spearmint and carvone (68.88%), and limonene (20.34%). The observed reduction in weight loss in coated fruit can be attributed to the formation of a physical barrier provided by the coating. Compared to the control group, which experienced the highest weight loss of 24.85%, fruit coated with CWN and CWN-MEO:β-CD exhibited significantly lower weight loss percentages of only 5.78% and 7.5%, respectively. Compared to the control group, which exhibited a release of ethylene at a rate of 1.3 µg kg⁻¹ h⁻¹, fruit coated with CWN, CWN-MEO:β-CD, and CWN-MEO coatings demonstrated a lower ethylene release rate at 0.7 µg kg⁻¹ h⁻¹. Although the physical-chemical properties of papayas, including pH, Brix, titratable acidity, color, and texture, remained largely unchanged during storage with the coatings, analysis of incidence and severity of papaya post-harvest deterioration revealed that coatings containing essential oils effectively acted as antifungals in the fruit. Microscopy images showed that CWN and CWN-MEO:β-CD coatings are more uniform compared to the others. The edible coatings, especially CWN and CWN-MEO: β-CD, can act as antimicrobial coatings on papaya fruit, increasing their conservation during post-harvest storage.

In this study, a potential hard tissue substitute was mimicked using collagen/mangosteen porous scaffolds. Collagen was extracted from Tilapia fish skin and mangosteen from the waste peel of the respective fruit. Sodium trimetaphosphate was used for the phosphorylation of these scaffolds to improve the nucleation sites for the mineralization process. Phosphate groups were incorporated in the collagen structure as confirmed by their attenuated total reflection Fourier transform infrared (ATR-FTIR) bands. The phosphorylation and mangosteen addition increased the thermal stability of the collagen triple helix structure, as demonstrated by differential scanning calorimetry (DSC) and thermogravimetry (TGA) characterizations. Mineralization was successfully achieved, and the presence of calcium phosphate was visualized by scanning electron microscopy (SEM). Nevertheless, the porous structure was maintained, which is an essential characteristic for the desired application. The deposited mineral was amorphous calcium phosphate, as confirmed by energy dispersive X-ray spectroscopy (EDX) results.

In this study, chitosan and collagen (Ch: Col)-based materials containing curcumin (Cur) as a bioactive compound were developed for wound-healing purposes. The effects of incorporating curcumin and increasing its concentration on both the rheological properties of the formed solutions and the morphological and thermal properties of the three-dimensional scaffolds obtained from them were evaluated. Rheology showed that the presence of curcumin resulted in solutions with a solid-like behavior (G’ > G″), higher collagen denaturation temperatures, and higher viscosities, favoring their use as biomaterials for wound healing. A greater cross-linking effect was observed at higher curcumin concentrations, possibly between the amino groups from both polymers and the hydroxyl and keto groups from the polyphenol. Such cross-linking was responsible for the delay in the onset of degradation of the scaffolds by 5 °C, as revealed by thermogravimetric analysis. Moreover, the pore diameter distribution profile of the scaffolds changed with increasing curcumin concentration; a greater number of pores with diameters between 40 and 60 µm was observed for the scaffold with the highest curcumin content (50 mg), which would be the most suitable for the proposed application. Thus, the materials developed in this study are presented as promising biomaterials for their biological evaluation in tissue regeneration.