This study collected basic information and conducted waste composition surveys to identify the present management condition of construction and demolition waste (CDW) landfills in Hanoi of Vietnam and to characterize waste composition and grain size distribution of CDW dumped at landfills. Basic information on seven CDW landfills under operation or closed/abandoned was collected, and the waste composition and the grain size distributions of dumped CDW at two landfills were investigated. Results showed that only one landfill site is currently under operation in Hanoi. Sanitary conditions of investigated landfills were relatively good without dumping of hazardous waste. Illegal dumping of domestic waste from residents, however, could be observed more or less at all sites due to an unclear boundary between dumping and surrounding areas. To improve current management of CDW landfills, a suitable recording system of accepted/dumped CDW and technical support for site managers are required as well as the implementation plan for developing and renovating landfills. Based on the results of the waste composition survey, the major components of dumped CDW were “Concrete”, “Clay bricks”, and “Soil-like”, and the sum of these materials reached >80% of the total. Grain size distributions of “Concrete” ranged from 10–600 mm and of “Clay bricks” ranged from 10–300 mm. Technical recommendations to examine a potential availability of dumped “Concrete” and “Clay bricks” as a base material in road construction are summarized from the viewpoints of segregation from “Soil-like” and impurities, grading of “Concrete” and “Clay bricks”, mechanical properties and environmental safety, and economic feasibility. The findings in this study raise challenges and perspectives to establish sound CDW management and to promote sustainable development of CDW recycling in Vietnam.

The improper treatment of landfill leachates is one of the major problems associated with waste landfilling and causes serious environmental pollution at waste landfill sites and their surroundings. To develop a suitable landfill leachate treatment system and to minimize the risk of environmental pollution, it is important to characterize seasonal and temporal variations of landfill leachates. This study investigated the leachate quality of the Nam Son waste landfill in Hanoi, Vietnam in 2017–2019 and characterized the potential risks of landfill leachate using a leachate pollution index (LPI). The results of this study showed that the seasonal and temporal variation of the overall LPI during the monitoring period was small and in the range of 20–25 (values 2.5 times higher than the maximum permissible limits of Vietnam National Technical Regulation on Industrial Wastewater). The LPI sub-indices attributed to organic and inorganic pollutants were major components of the LPI. Especially, the annually averaged values of LPI of inorganic pollutants were 7.7 times higher than the maximum permissible limits, suggesting that the treatment of inorganic pollutants, such as ammonium-nitrogen (NH₄⁺–N) and total nitrogen (TN), is highly required at Nam Son landfill to prevent environmental pollution surrounding the landfill site.

Reinforced concrete bridges were visually surveyed in Japan, Thailand, and Vietnam to study the deterioration caused by internal steel corrosion under different climates, focusing on the concrete cover depth. Spalling or cracking arising from corrosion is likely where water is supplied. According to prior studies and our surveys, a concrete cover depth of more than 40 mm was found to prevent spalling, regardless of environmental conditions and structure age. Because water supply at steel is a key corrosion factor, it was hypothesised that under natural conditions, the water penetration in concrete would remain at a depth of approximately 40 mm. Our laboratory study examined water penetration under drying and wetting conditions. The results also suggested that under periodic rainfall conditions, the threshold of water penetration was not exceeded. The numerical study indicated maximum moisture evaporation to facilitate oxygen diffusion occurred at a depth of approximately 30–40 mm unless the concrete was exposed to continuous drying for more than one month. It was experimentally and numerically concluded that an adequate cover depth of greater than 40 mm could inhibit moisture and oxygen penetration at the steel, which supported the survey findings of cover depth effect on a high resistance to corrosion-induced deterioration despite an increase in service life.

Cool road pavements contribute to mitigating urban heat islands. To evaluate the heat balance in paved surfaces and to select appropriate road construction materials that help suppress heat islands, an accurate understanding of heat transport parameters such as thermal conductivity (λ) and heat capacity (HC) is important. Recycled aggregates from construction and demolition waste, including scrap construction materials and industrial by-products, are often used for road construction; however, λ and HC of recycled aggregates especially for roadbeds are not fully understood. This study involved a series of laboratory tests to measure λ and HC of recycled concrete and clay brick aggregates (<40 mm) and their mixtures with autoclaved aerated concrete grains (<2 mm) under varied moisture conditions. The measured λ and HC increased with increasing volumetric water content (θ). Closed-form models for estimating λ(θ) were proposed using normalized thermal conductivity (λ_e) and effective saturation (S_e). The new λ_e(S_e) models performed well for the measured data compared to previously proposed models and would be useful to evaluate λ of recycled aggregates for roadbed materials.

The construction industry is one of the key industries with high potential for the circular economy; the promotion of reuse and recycling of construction and demolition waste (CDW) is essential for sustainable urban development. In this study, a series of compaction, California bearing ratio, saturated hydraulic conductivity, and particle breakage tests of well– and poor–graded mixtures of recycled clay brick aggregates (RCBs) and recycled concrete aggregates (RCAs) with maximum aggregate diameters of 19, 25, and 37.5 mm were carried out to examine the practical application of those mixtures to unbound roadbed materials in Vietnam. The experimental results suggest that the maximum amount of RCBs added to RCAs should be less than 30% when applied to unbound roadbed materials. In addition, it was found that the mixing proportions of RCBs and RCAs and the maximum aggregate diameter, gradation of aggregates, and initial moisture condition control the saturated hydraulic conductivity. Further, the particle breakage characteristics under compaction were carefully examined, and it was found that the percentage increment/decrement, as well as a newly introduced method of estimating the mixing proportions of RCAs and RCBs in the fine fraction (<2.36 mm), is effective in understanding the mechanism of particle breakage of RCA and RCB mixtures.