This research aims to study the effect of the dosage of anhydrous sodium metasilicate activator on the long-term properties of fly ash-based one-part alkali-activated binders (OPAAB) cured at ambient conditions. Powdered sodium metasilicate activator was utilized in the range of 8–16% by weight of the fly ash in producing the OPAAB. The properties examined are hardened density, compressive strength, flexural strength, water absorption, efflorescence formation, and microstructural analysis. The experimental result revealed that the binders exhibited excellent long-term strength properties. The compressive strength of the OPAAP is well correlated with its hardened density. The pastes were found to exhibit good soundness characteristics over the long-term. The absorption of water decreases with an increase in the activator dosage from 8–12%, and beyond that, the water absorption relatively remains the same. Field emission scanning electron microscope (FESEM) micrograph revealed uniformly formed solid matrices with the micro-crack present were observed in the samples. The larger pore size promotes the crystallization of the resulting hydrate substances (N, C)-A-S-H gel. The initial dissolution of the OPAAP occurred within the first 30 min. At longer age of curing, mixtures with a higher dosage of powdered activator tend to absorb less water. Strength properties beyond 28 days are considered as the long-term strength.

Deep beams are more susceptible to shear failure, and therefore reparation is a crucial for structural reinforcements. Shear failure is structural concrete failure in nature. It generally occurs without warning; however, it is acceptable for the beam to fail in bending but not in shear. The experimental study presented the structural behavior of the deep beams of reinforced concrete (RC) that reinforces the web openings with externally connected carbon fiber reinforced polymer (CFRP) composite in the shear zone. The structural behavior includes a failure mode, and cracking pattern, load deflection responses, stress concentration and the reinforcement factor were investigated. A total of nine reinforced concrete deep beams with openings strengthened with CFRP and one control beam without an opening have been cast and tested under static four-point bending load till failure. The experimental results showed that the increase the size of the opening causes an increase in the shear strength reduction by up to 30%. Therefore, the larger the openings, the lower the capability of load carriage, in addition to an increase in the number of CFRP layers that could enhance the load carrying capacity. Consequently, utilization of the CFRP layer wrapping technique strengthened the shear behavior of the reinforced concrete deep beams from about 10% to 40%. It was concluded that the most effective number of CFRP layers for the deep beam with opening sizes of 150 mm and 200 mm were two layers and three layers, respectively.

The objective of this research was to determine the durability of an engineered cementitious composite (ECC) incorporating crumb rubber (CR) and graphene oxide (GO) with respect to resistance to acid and sulphate attacks. To obtain the mix designs used for this study, response surface methodology (RSM) was utilized, which yielded the composition of 13 mixes containing two variables (crumb rubber and graphene oxide). The crumb rubber had a percentage range of 0–10%, whereas the graphene oxide was tested in the range of 0.01–0.05% by volume. Three types of laboratory tests were used in this study, namely a compressive test, an acid attack test to study its durability against an acidic environment, and a sulphate attack test to examine the length change while exposed to a sulphate solution. Response surface methodology helped develop predictive responsive models and multiple objectives that aided in the optimization of results obtained from the experiments. Furthermore, a rubberized engineered cementitious composite incorporating graphene oxide yielded better chemical attack results compared to those of a normal rubberized engineered cementitious composite. In conclusion, nano-graphene in the form of graphene oxide has the ability to enhance the properties and overcome the limitations of crumb rubber incorporated into an engineered cementitious composite. The optimal mix was attained with 10% crumb rubber and 0.01 graphene oxide that achieved 43.6 MPa compressive strength, 29.4% weight loss, and 2.19% expansion. The addition of GO enhances the performance of rubberized ECC, contributing to less weight loss due to the deterioration of acidic media on the ECC. It also contributes to better resistance to changes in the length of the rubberized ECC samples.

Digitalization in the construction sector is a need of the modern world. Not only the infrastructure, but also the quality of life, is improved by the digital transformation in the construction sector. Digital technologies are being widely used in construction. The impacts of implementing digital technology on transformation in the construction industry, however, have not yet been thoroughly understood. Considering this aspect of the construction industry, this study reviews the articles in the field of digitalization of various segments in the construction industry. In this manner, the Scopus database was considered to gather the relevant articles based on the keywords (((“Digitalization” OR “Digitalisation”) OR “Reforms”) AND “Construction” AND “Energy”). These keyword combinations provided a list of 126 articles and, following the protocol of Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA), the number was reduced to 35. The review showed that the major targeted areas in the construction sector based on digital transformation are smart construction, optimization of energy, sustainable environment, wireless technology, and economic and architectural growth in which the role of Building Information Modelling (BIM) and prefabricated construction is noteworthy. The involvement of digitalization in numerous fields has improved quality of life. It increases production and has the potential to automate the industry more effectively. This study shows how the adoption of digital technology has improved comprehension and laid the foundation for a digital transformation in the construction industry.

Engineered cementitious composite (ECC) was discovered as a new substitute of conventional concrete as it provides better results in terms of tensile strain, reaching beyond 3%. From then, more studies were done to partially replace crumb rubber with sand to achieve a more sustainable and eco-friendlier composite from the original ECC. However, the elastic modulus of ECC was noticeably degraded. This could bring potential unseen dangerous consequences as the fatigue might happen at any time without any sign. The replacement of crumb rubber was then found to not only bring a more sustainable and eco-friendlier result but also increase the ductility and the durability of the composite, with lighter specific gravity compared to conventional concrete. This study investigated the effects of crumb rubber (CR) and graphene oxide (GO) toward the deformable properties of rubberized ECC, including the compressive strength, elastic modulus, Poisson’s ratio, and drying shrinkage. Central composite design (CCD) was utilized to provide 13 reasonable trial mixtures with the ranging level of CR replacement from 0–30% and that of GO from 0.01–0.08%. The results show that GO increased the strength of the developed GO-RECC. It was also found that the addition of CR and GO to ECC brought a notable improvement in mechanical and deformable properties. The predicted model that was developed using response surface methodology (RSM) shows that the variables (compression strength, elastic modulus, Poisson’s ratio, and drying shrinkage) rely on the independent (CR and GO) variables and are highly correlated.

Crumb rubber (CR) from scrap tires is used as a partial replacement of fine aggregates in cement paste. This promotes the sustainable development of the environment, economy, and society, as waste tires are non-biodegradable and flammable. They occupy large landfill areas and are breeding grounds for mosquitoes and rodents. Inclusion of CR in mortar leads to several improvements on the mixture properties such as ductility, toughness, and impact resistance. However, it exhibits lower strengths and Modulus of Elasticity (ME). Therefore, to promote the use of mortar containing CR, it is vital to improve its mechanical strength. Past studies proved that nano-silica (NS) improves the strength of concrete due to the physico-chemical effects of NS. This study aims to examine the mechanical properties of crumb rubber mortar containing nano-silica (NS-CRM) and to develop models to predict these properties using Response Surface Methodology (RSM). Two variables were considered, CR as partial replacement to sand by volume (0%, 7.5%, 15%), and NS as partial replacement to cement by weight (0%, 2.5%, 5%). The results demonstrated a significant improvement in the mechanical properties of CRM when incorporating NS, and the models developed using RSM were acceptable with a 2% to 3% variation.