In this paper, the thermal decomposition of crystalline Al(OH)₃ was studied over the temperature range of 260–400 °C for particles with a size between 10 and 150 µm. The weight losses and thermal effects occurring in each of the dehydration process were assessed using thermogravimetry (TG) and differential scanning calorimetry (DSC) thermal analysis. X-ray diffraction (XRD) patterns, refined by the Rietveld method, were used for mineral phase identification, phase composition analysis, and crystallinity degree determination. Moreover, the particle size distributions and their corresponding D10, D50, and D90 numeric values were determined with a laser analyzer. We observed a strong relationship between the calcination temperature, the initial gibbsite grade particle size, and the crystallinity of the resulting powders. Hence, for all endothermic effects identified by DSC, the associated temperature values significantly decreased insofar as the particle dimensions decreased. When the gibbsite was calcined at a low temperature, we identified small amounts of boehmite phase along with amorphous new phases and unconverted gibbsite, while the powders calcined at 400 °C gradually yielded a mixture of boehmite and crystalized γ-Al₂O₃. The crystallinity % of all phase transition products declined with the increase in particle size or temperature for all the samples.

Aluminum hydroxide is an essential material for the industrial production of ceramics (especially insulators and refractories), desiccants, absorbents, flame retardants, filers for plastics and rubbers, catalysts, and various construction materials. The calcination process of Al(OH)₃ first induces dehydration and, finally, results in α-Al₂O₃ formation. Nevertheless, this process contains various intermediary steps and has been proven to be complicated due to the development of numerous transitional alumina. Each step of the investigation is vital for the entire process because the final properties of materials based on aluminum trihydroxide are determined by their phase composition, morphology, porosity, etc. In this paper, five dried, milled, and size-classified aluminum hydroxide specimens were thermally treated at 260, 300, and 400 °C; then, they were studied in order to identify the effects of temperature on their properties, such as particle morphology, specific surface area, pore size, and pore distribution. The major oxide compounds identified in all samples were characteristic of bauxite—namely, Al₂O₃ * 3H₂O, SiO₂, Fe₂O₃, Na₂O, and CaO. Particles with smaller sizes (<10 µm = 76.28%) presented the highest humidity content (~5 wt.%), while all samples registered a mass loss of ~25 wt.% on ignition at 400 °C. The identified particles had the shapes of hexagonal or quasi-hexagonal platelets and resulted in large spherulitic concretions. The obtained results suggest that ceramic powders calcined at 400 °C should be used for applications as adsorbents or catalysts due to their high specific area of about 200–240 m²/g and their small pore width (3–3.5 nm).

In this paper, we studied the scandium adsorption from aqueous solutions on the surface of low-temperature-activated alumina products (GDAH). The GDAH samples are industrially manufactured, coming from the Bayer production cycle of the Sierra Leone bauxite as aluminium hydroxide, and further, by drying, milling, classifying and thermally treating up to dehydroxilated alumina products at low temperature. All experiments related to hydroxide aluminium activation were conducted at temperature values of 260, 300 and 400 °C on samples having the following particle sizes: <10 µm, 20 µm, <45 µm and <150 µm, respectively. The low-temperature-activated alumina products were characterised, and the results were published in our previous papers. In this paper, we studied the scandium adsorption process on the above materials and related thermodynamic and kinetic studies.

The purpose of this study was to examine the utilization of 0–45 μm aluminum hydrate fraction (gibbsite) manufactured by Alum SA Tulcea, as a precursor in the hydrothermal synthesis process of nanosize boehmite from gibbsite suspensions. Furthermore, the use of the produced material as adsorbent of lanthanum (III) ions was investigated using aqueous solutions. Thermogravimetric analysis (TG), Fourier Transform InfraRed Spectroscopy (FT-IR), Wide-Angle X-Ray Scattering (WAXS), and atomic force microscopy (AFM) were used to demonstrate the preparation of the required material. Additionally, the material point of zero charge (pHpzc) and material specific surface (using BET approach) were evaluated. By conducting adsorption studies, the specific parameters for the lanthanum adsorption process were evaluated. The effects of pH, the ratio of adsorbent material to La(III) quantity from aqueous solution, contact time, and La(III) initial concentration were also assessed. Based on the obtained experimental data, it was proved that the maximum adsorption capacity of 97.7 mg/g was obtained for a solid:liquid ratio = 0.1 g:25 mL, pH between 3 and 6, temperature of 298 K, and contact time of 90 min. The studied adsorption process is most effectively described by the Sips model, suggesting an intricate interaction among the adsorbent material and La (III) ions. The prepared adsorbent exhibited a good desorption capacity (higher than 93%) when 20% HCl was used for desorption.