From the lanthanide group, part of the rare earth elements (REEs), lanthanum is one of the most important elements given its application potential. Although it does not have severe toxicity to the environment, its increased usage in advanced technologies and medical fields and scarce natural reserves point to the necessity also of recovering lanthanum from diluted solutions. Among the multiple methods for separation and purification, adsorption has been recognized as one of the most promising because of its simplicity, high efficiency, and large-scale availability. In this study, a xerogel based on silicon and iron oxides doped with zinc oxide and polymer (SiO₂@Fe₂O₃@ZnO) (SFZ), obtained by the sol–gel method, was considered as an adsorbent material. Micrography indicates the existence of particles with irregular geometric shapes and sizes between 16 μm and 45 μm. Atomic force microscopy (AFM) reveals the presence of dimples on the top of the material. The specific surface area of the material, calculated by the Brunauer–Emmet–Teller (BET) method, indicates a value of 53 m²/g, with C constant at a value of 48. In addition, the Point of Zero Charge (pH_pZc) of the material was determined to be 6.7. To establish the specific parameters of the La(III) adsorption process, static studies were performed. Based on experimental data, kinetic, thermodynamic, and equilibrium studies, the mechanism of the adsorption process was established. The maximum adsorption capacity was 6.7 mg/g, at a solid/liquid ratio = 0.1 g:25 mL, 4 < pH < 6, 298 K, after a contact time of 90 min. From a thermodynamic point of view, the adsorption process is spontaneous, endothermic, and occurs at the adsorbent–adsorbate interface. The Sips model is the most suitable for describing the observed adsorption process, indicating a complex interaction between La(III) ions and the adsorbent material. The material can be reused as an adsorbent material, having a regeneration capacity of more than 90% after the first cycle of regeneration. The material was reused 3 times with considerable efficiency.

The purpose of this study was to examine the utilization of 0–45 μm aluminum hydrate fraction (gibbsite) manufactured by Alum SA Tulcea, as a precursor in the hydrothermal synthesis process of nanosize boehmite from gibbsite suspensions. Furthermore, the use of the produced material as adsorbent of lanthanum (III) ions was investigated using aqueous solutions. Thermogravimetric analysis (TG), Fourier Transform InfraRed Spectroscopy (FT-IR), Wide-Angle X-Ray Scattering (WAXS), and atomic force microscopy (AFM) were used to demonstrate the preparation of the required material. Additionally, the material point of zero charge (pHpzc) and material specific surface (using BET approach) were evaluated. By conducting adsorption studies, the specific parameters for the lanthanum adsorption process were evaluated. The effects of pH, the ratio of adsorbent material to La(III) quantity from aqueous solution, contact time, and La(III) initial concentration were also assessed. Based on the obtained experimental data, it was proved that the maximum adsorption capacity of 97.7 mg/g was obtained for a solid:liquid ratio = 0.1 g:25 mL, pH between 3 and 6, temperature of 298 K, and contact time of 90 min. The studied adsorption process is most effectively described by the Sips model, suggesting an intricate interaction among the adsorbent material and La (III) ions. The prepared adsorbent exhibited a good desorption capacity (higher than 93%) when 20% HCl was used for desorption.