In this work, we study the influence of reduced graphene oxide (rGO) on the morphology and chemistry of highly porous N,S-doped carbon cryogels. Simultaneously, we propose an easily upscalable route to prepare such carbons by adding graphene oxide (GO) in as-received suspended form to the aqueous solution of the ι-carrageenan and urea precursors. First, 1.25–5 wt% GO was incorporated into the dual-doped polymer matrix. The CO₂, CO, and H₂O emitted during the thermal treatments resulted in the multifaceted modification of the textural and chemical properties of the porous carbon. This facilitated the formation of micropores through self-activation and resulted in a substantial increase in the apparent surface area (up to 1780 m²/g) and pore volume (up to 1.72 cm³/g). However, adding 5 wt% GO led to overactivation. The incorporated rGO has an ordering effect on the carbon matrix. The evolving oxidative species influence the surface chemistry in a complex way, but sufficient N and S atoms (ca. 4 and >1 at%, respectively) were preserved in addition to the large number of developing defects. Despite the complexity of the textural and chemical changes, rGO increased the electrical conductivity monotonically. In alkaline oxygen reduction reaction (ORR) tests, the sample with 1.25 wt% GO exhibited a 4e⁻ mechanism and reasonable stability, but a higher rGO content gradually compromised the performance of the electrodes. The sample containing 5 wt% GO was the most sensitive under oxidative conditions, but after stabilization it exhibited the highest gravimetric capacitance. In Li-ion battery tests, the coulombic efficiency of all the samples was consistently above 98%, indicating the high potential of these carbons for efficient Li-ion insertion and reinsertion during the charge–discharge process, thereby providing a promising alternative for graphite-based anodes. The cell from the 1.25 wt% GO sample showed an initial discharge capacity of 313 mAh/g, 95.1% capacity retention, and 99.3% coulombic efficiency after 50 charge–discharge cycles.

In this paper we report the synthesis of a N, S co-doped metal free carbon cryogel obtained from a marine biomass derived precursor using urea as nitrogen source. Natural carrageenan intrinsically contains S and inorganic salt. The latter also serves as an activating agent during the pyrolytic step. The overall 11.6 atomic % surface heteroatom concentration comprises 5% O, 4.6% N and 1% S. The purified and annealed final carbon (CA) has a hierarchical pore structure of micro-, meso- and macropores with an apparent surface area of 1070 m²/g. No further treatment was applied. The gas adsorption potential of the samples was probed with H₂, CO₂ and CH₄, while the electrocatalytic properties were tested in an oxygen reduction reaction. The atmospheric CO₂ and CH₄ storage capacity at 0 °C in the low pressure range is very similar to that of HKUST-1, with the CO₂/CH₄ selectivity below 20 bar, even exceeding that of the MOF, indicating the potential of CA in biogas separation. The electrocatalytic behavior was assessed in an aqueous KOH medium. The observed specific gravimetric capacitance 377 F/g was exceeded only in B, N dual doped and/or graphene doped carbons from among metal free electrode materials. The CA electrode displays almost the same performance as a commercial 20 wt% Pt/C electrode. The oxygen reduction reaction (ORR) exhibits the 4-electron mechanism. The 500-cycle preliminary stability test showed only a slight increase of the surface charge.

S and N double-doped high surface area biomass-derived carbons were obtained from marine biomass-derived ι-carrageenan. Adding carbon nanoparticles (CNPs), namely graphene oxide (GO) or carbon nanotubes (CNTs), in the early stage of the synthesis leads to a modified porous texture and surface chemistry. The porous textures were characterized by N₂ (−196.15 °C) and CO₂ (0 °C) isotherms. The best GO- and CNT-added carbons had an apparent surface area of 1780 m²/g and 1170 m²/g, respectively, compared to 1070 m²/g for the CNP-free matrix. Analysis of the Raman spectra revealed that CNT was more efficient in introducing new defects than GO. Based on XPS, the carbon samples contain 2–4.5 at% nitrogen and 1.1 at% sulfur. The Dubinin–Radushkevich (DR) and Henry models were used to assess the strength of the interactions between various gases and the surface. The N₂/H₂ and CO₂/CH₄ selectivities were estimated with ideal adsorbed solution theory (IAST). While the CNPs, particularly GO, had a remarkable influence on the porous texture and affected the surface chemistry, their influence on the separation selectivity of these gases was more modest.

High surface area carbon was obtained from -carrageenan – urea cryogels doped with 1.25 – 5 wt% graphene oxide (GO). Incorporation of GO resulted in multifaceted modification in the textural and chemical properties of the carbon cryogel. The thermal decomposition of GO facilitated the formation of micropores resulted in a substantial increase in the apparent surface area (up to 1780 m2/g). The annealing at 1000 °C removed part of the heteroatoms but left behind a high number of defects. While the volatile thermal degradation products of GO affected the porous texture and the surface chemistry in a complex way, its reduced residue resulted in a gradually increasing electrical conductivity. The influence of GO was studied in oxygen reduction reaction (ORR) and in Li-ion storage application. GO affected the electron transfer mechanism in the ORR tests and challenged the stability of the electrodes. Even if the electrode has been stabilized under oxygen-free conditions, later may undergo destabilization processes during the ORR. The 5 wt% GO doped sample was the most sensitive under oxidative conditions, but finally it exhibited the highest capacitance. In the Li-ion battery tests the coulombic efficiency of all the samples was consistently above 98 %, indicating the great potential of such carbons for efficient Li-ion insertion and reinsertion during the charge – discharge process, thereby providing a promising alternative for graphite-based anodes. The cell from the 1.25% sample showed an initial discharge capacity of 313 mAh/g, 95.1 % capacity retention and 99.3 % coulombic efficiency after 50 charge – discharge cycles.

Tackling global warming and the consequent climate change in our planet is of urgent importance to our society. Renewable biomass derived carbons have been studied as promising adsorbents, but marine biomass derived carbons have not been explored extensively. S and N double-doped porous carbons were obtained from a marine biomass related precursor. Adding carbon nanoparticles (CNP) graphene oxide (GO), or carbon nanotubes (CNTs), in an early stage of the synthesis leads to a modified porous texture and surface chemistry. The carbons retained 2-4.5 at% nitrogen and 1.1 at% sulfur. The best GO and CNT added carbons had an apparent surface area 1780 m2/g and 1170 m2/g, respectively, compared to 1070 m2/g of the CNP-free matrix. The Dubinin-Radushkevich (DR) and Henry models were used to assess the strength of the interactions between various gases and the surface. The N2/H2 and CO2/CH4 selectivities were estimated with ideal adsorbed solution theory (IAST). While the CNPs, particularly GO, had a remarkable effect both on the porous texture and the surface chemistry, their influence on selectivity is more modest.