The adsorption technique is widely used in water purification, and its efficiency can be significantly improved by target-specific adsorbent design. Research on iodine and its ion removal from water has attracted a great deal of interest due to increased concentrations in the environment and acute toxic effects, e.g., in human thyroid cells. In this work, the iodide removal performance of two high-surface-area resorcinol–formaldehyde-based carbon aerogels was studied under acidic conditions. The BET surface area was 790 m²/g (RF_ac) and 375 m²/g (RMF-GO), with a corresponding micropore ratio of 36 and 26%, respectively. Both aerogels showed outstanding adsorption capacity, exceeding the reported performance of other carbons and Ag-doped materials. Owing to its basic nature, the RMF-GO carbon aerogel showed higher I⁻ capacity, up to 97 mg/g, than the acidic RF_ac, which reached a capacity of 82 mg/g. The surface chemistry of the aerogels also played a distinct role in the removal. In terms of kinetics, RF_ac removed 60% of the iodide ions and RMF-GO 30% within 8 h. The removal kinetics was of the first order, with a half-life of 1.94 and 1.70 h, respectively.

In this paper we report the synthesis of a N, S co-doped metal free carbon cryogel obtained from a marine biomass derived precursor using urea as nitrogen source. Natural carrageenan intrinsically contains S and inorganic salt. The latter also serves as an activating agent during the pyrolytic step. The overall 11.6 atomic % surface heteroatom concentration comprises 5% O, 4.6% N and 1% S. The purified and annealed final carbon (CA) has a hierarchical pore structure of micro-, meso- and macropores with an apparent surface area of 1070 m²/g. No further treatment was applied. The gas adsorption potential of the samples was probed with H₂, CO₂ and CH₄, while the electrocatalytic properties were tested in an oxygen reduction reaction. The atmospheric CO₂ and CH₄ storage capacity at 0 °C in the low pressure range is very similar to that of HKUST-1, with the CO₂/CH₄ selectivity below 20 bar, even exceeding that of the MOF, indicating the potential of CA in biogas separation. The electrocatalytic behavior was assessed in an aqueous KOH medium. The observed specific gravimetric capacitance 377 F/g was exceeded only in B, N dual doped and/or graphene doped carbons from among metal free electrode materials. The CA electrode displays almost the same performance as a commercial 20 wt% Pt/C electrode. The oxygen reduction reaction (ORR) exhibits the 4-electron mechanism. The 500-cycle preliminary stability test showed only a slight increase of the surface charge.

In this article, the secondary electron-emission properties of both vertically and laterally inhomogeneous samples are discussed. To study the effect of surface coverage, the total electron-emission yield of tungsten and niobium samples was measured as a function of primary electron energy and oxide thickness. A method is suggested to avoid charging difficulties during AES measurements of samples that consist of both metal and various insulator parts.