This paper assesses the aspects related to sustainability of polymer composites, focusing on the two main components of a composite, the matrix and the reinforcement/filler. Most studies analyzed deals with the assessment of the composite performance, but not much attention has been paid to the life cycle assessment (LCA), biodegradation or recyclability of these materials, even in those papers containing the terms “sustainable” (or its derivate words), “green” or “eco”. Many papers claim about the sustainable or renewable character of natural fiber composites, although, again, analysis about recyclability, biodegradation or carbon footprint determination of these materials have not been studied in detail. More studies focusing on the assessment of these composites are needed in order to clarify their potential environmental benefits when compared to other types of composites, which include compounds not obtained from biological resources. LCA methodology has only been applied to some case studies, finding enhanced environmental behavior for natural fiber composites when compared to synthetic ones, also showing the potential benefits of using recycled carbon or glass fibers. Biodegradable composites are considered of lesser interest to recyclable ones, as they allow for a higher profitability of the resources. Finally, it is interesting to highlight the enormous potential of waste as raw material for composite production, both for the matrix and the filler/reinforcement; these have two main benefits: no resources are used for their growth (in the case of biological materials), and fewer residues need to be disposed.

This paper summarises the results obtained from the characterisation of giant reed (Arundo donax L.) plant and fibres. The research is part of a project developed in the Macaronesia region, of which the aim is to demonstrate the feasibility of using biomass from invasive plant species in the composites sector as a way of financing control campaigns and habitats conservation labours. An experimental procedure for the extraction of fibre bundles from this plant was developed, and the material obtained was characterised in terms of chemical composition, thermogravimetry and infrared spectra to evaluate its potential application in the production of polymeric composite materials as a strategy for the valorisation of residual biomass from this invasive species in Macaronesia. Thermoplastic matrix composites with fibre content up to 40 wt.% were produced and their mechanical properties under tensile, flexural and impact loading were determined. No references on the preparation of composite materials with polyolefin matrices and giant reed fibres have been found. Results obtained from mechanical tests show a good performance of the manufactured composites, with a significant increase in both flexural and tensile stiffness; the flexural modulus is almost tripled for PE-based composites and rises to 88% with respect to PP matrix. The ultimate flexural strength and the tensile and flexural yield strength are kept at acceptable values compared to neat polymer materials, although ultimate tensile strength and impact resistance are significantly affected when natural fibres are added.

Some studies have evaluated the use of Opuntia as reinforcement for polymeric matrices, obtaining good results in energy absorption tests and increasing the tensile elastic modulus. However, no studies focusing on the previous characterisation of the fibres and their treatment to improve compatibility with polymeric matrices have been found. This work analyses the chemical composition of Opuntia maxima (OM) and Opuntia dillenii (OD) cladodes and fibre, studying how different treatments influence it. AOAC 2000 methods were used to determine non-structural components and the Van Soest method was used to estimate structural components. Surface characteristics of the samples were also evaluated by Fourier Transform Infrared Spectroscopy (FTIR). Opuntia fibre presented higher cellulose (50–66%) and lignin (6–14%) content and lower hemicellulose (8–13%) content than Opuntia cladodes (9–14% cellulose, 20–50% hemicellulose, 1–4% lignin). Despite the variability of lignocellulosic materials, OD cladodes treated with water and acetic acid achieved an increase in the structural components. Alkaline fibre treatment removed pectin and hemicellulose from the fibre surface, slightly increasing the cellulose content. Future research should evaluate whether the treated Opuntia fibre can improve the mechanical properties of reinforced polymer.

Opuntia spp. is a plant widely distributed in the world that has traditionally been used in the food sector. Alternatively to the conventional uses of this plant, this work gives an overview of current knowledge about Opuntia fiber, focusing on several papers which have reinforced polymer matrices with this species. Opuntia cladodes are formed by a network of fibers with a hexagonal reticular hierarchical structure, which is believed to be responsible for their mechanical properties. Opuntia fiber has a cellulose content about 50% and a density (1.54 g/cm³) similar to conventional fibers such as abaca (1.5 g/cm³), jute (1.3 g/cm³) and sisal (1.5 g/cm³). Matrices such as polylactic acid (PLA) and polypropylene (PP) have been reinforced with Opuntia fibers and with ground cladodes, mainly by compression molding, increasing the tensile elastic modulus up to 135%. Opuntia fibers also offer good properties against energy absorption, being adequate for the design of lightweight materials with these characteristics. Further studies should be undertaken in order to establish the appropriate parameters to optimize fiber extraction, improve fiber-matrix compatibility and determine a general trend despite the plant own variability.

This paper focuses on the use of castor oil plant (Ricinus communis) as filler in rotomolded parts using polyethylene (PE) and polylactic acid (PLA) as polymer matrixes. The vegetable shredded material was used in 5 and 10% weight following a dry blending procedure and then rotomolded to obtain cube test parts. This material was characterized to determine its chemical composition, thermal stability, and structure. The NaOH-treated material shows reduced hemicellulose content and higher thermal stability. Obtained composite materials were characterized in terms of mechanical (tensile, flexural, and impact) and thermal properties, morphology, and bio-disintegration behavior. The use of Ricinus as filler in rotomolded PE composite decreases, in general terms, mechanical properties of neat PE, while no significant changes in thermal or bio-disintegration properties are found. On the contrary, PLA composites show higher tensile strength and similar Young's modulus than the matrix, although with reduced flexural and impact properties. Alkali-treated Ricinus material produces parts with higher porosity and thus, lower mechanical properties than composites with untreated material. Finally, the incorporation of this vegetal material modifies to a great extent the thermal properties of the PLA matrix. The bio-disintegration rate increases due to the use of fibers, probably because of the higher moisture absorption of composites.