This paper compares the mechanical properties of different natural fiber composites produced by rotational molding as a way of waste valorization from campaigns to control invasive plant species in Macaronesia. Rotomolded parts produced with polymeric matrices (polyethylene) and filled with up to 20% by weight of cellulosic fibers obtained from Arundo donax L., Pennisetum setaceum, and Ricinus communis plants were characterized in terms of tensile, flexural, and impact strength. It was found that the sieving of natural fibers allowed for their introduction in higher loadings, from 10 (for un-sieved material) to 20%; fiber size greatly affected the mechanical properties of the final parts, although some combinations were proven not to reduce the mechanical properties of the neat resin. This study is a first approach to the valorization of residues obtained from periodic campaigns of the control of invasive species performed by public authorities, usually at the local level. It is important to highlight that the main objective of this research did not focus on economically profitable activity; instead, it was focused on the reduction of wastes to be disposed from ecosystem maintenance actions and the investment of potential income into preservation policies.

This paper summarises the results obtained from the characterisation of giant reed (Arundo donax L.) plant and fibres. The research is part of a project developed in the Macaronesia region, of which the aim is to demonstrate the feasibility of using biomass from invasive plant species in the composites sector as a way of financing control campaigns and habitats conservation labours. An experimental procedure for the extraction of fibre bundles from this plant was developed, and the material obtained was characterised in terms of chemical composition, thermogravimetry and infrared spectra to evaluate its potential application in the production of polymeric composite materials as a strategy for the valorisation of residual biomass from this invasive species in Macaronesia. Thermoplastic matrix composites with fibre content up to 40 wt.% were produced and their mechanical properties under tensile, flexural and impact loading were determined. No references on the preparation of composite materials with polyolefin matrices and giant reed fibres have been found. Results obtained from mechanical tests show a good performance of the manufactured composites, with a significant increase in both flexural and tensile stiffness; the flexural modulus is almost tripled for PE-based composites and rises to 88% with respect to PP matrix. The ultimate flexural strength and the tensile and flexural yield strength are kept at acceptable values compared to neat polymer materials, although ultimate tensile strength and impact resistance are significantly affected when natural fibres are added.

Some studies have evaluated the use of Opuntia as reinforcement for polymeric matrices, obtaining good results in energy absorption tests and increasing the tensile elastic modulus. However, no studies focusing on the previous characterisation of the fibres and their treatment to improve compatibility with polymeric matrices have been found. This work analyses the chemical composition of Opuntia maxima (OM) and Opuntia dillenii (OD) cladodes and fibre, studying how different treatments influence it. AOAC 2000 methods were used to determine non-structural components and the Van Soest method was used to estimate structural components. Surface characteristics of the samples were also evaluated by Fourier Transform Infrared Spectroscopy (FTIR). Opuntia fibre presented higher cellulose (50–66%) and lignin (6–14%) content and lower hemicellulose (8–13%) content than Opuntia cladodes (9–14% cellulose, 20–50% hemicellulose, 1–4% lignin). Despite the variability of lignocellulosic materials, OD cladodes treated with water and acetic acid achieved an increase in the structural components. Alkaline fibre treatment removed pectin and hemicellulose from the fibre surface, slightly increasing the cellulose content. Future research should evaluate whether the treated Opuntia fibre can improve the mechanical properties of reinforced polymer.