Kenaf (Hibiscus cannabinus L.) is one of the most investigated and industrially applied natural fibers for polymer composite reinforcement. However, relatively limited information is available regarding its epoxy composites. In this work, both thermal and chemical properties were, for the first time, determined in kenaf fiber reinforced epoxy matrix composites. Through XRD analysis, a microfibrillar angle of 7.1° and crystallinity index of 44.3% was obtained. The FTIR analysis showed the functional groups normally found for natural lignocellulosic fibers. TMA analysis of the composites with 10 vol% and 20 vol% of kenaf fibers disclosed a higher coefficient of thermal expansion. The TG/DTG results of the epoxy composites revealed enhanced thermal stability when compared to plain epoxy. The DSC results corroborated the results obtained by TGA, which indicated a higher mass loss in the first stage for kenaf when compared to its composites. These results might contribute to kenaf fiber composite applications requiring superior performance.

Several industry sectors have sought to develop materials that combine lightness, strength and cost-effectiveness. Natural lignocellulosic natural fibers have demonstrated to be efficient in replacing synthetic fibers, owing to several advantages such as costs 50% lower than that of synthetic fibers and promising mechanical specific properties. Polymeric matrix composites that use kenaf fibers as reinforcement have shown strength increases of over 600%. This work aims to evaluate the performance of epoxy matrix composites reinforced with kenaf fibers, by means of dynamic-mechanical analysis (DMA) and ballistic test. Through DMA, it was possible to obtain the curves of storage modulus (E′), loss modulus (E″) and damping factor, Tan $\delta$, of the composites. The variation of E′ displayed an increase from 1540 MPa for the plain epoxy to 6550 MPa for the 30 vol.% kenaf fiber composites, which evidences the increase in viscoelastic stiffness of the composite. The increase in kenaf fiber content induced greater internal friction, resulting in superior E″. The Tan $\delta$ was considerably reduced with increasing reinforcement fraction, indicating better interfacial adhesion between the fiber and the matrix. Ballistic tests against 0.22 caliber ammunition revealed similar performance in terms of both residual and limit velocities for plain epoxy and 30 vol.% kenaf fiber composites. These results confirm the use of kenaf fiber as a promising reinforcement of polymer composites for automotive parts and encourage its possible application as a ballistic armor component.

The constant concern about environmental issues has led to the growth of researches about eco-friendly materials. Among them, the natural lignocellulosic fibers have already presented their potential in place of petroleum-based synthetics. However, a relevant number of studies still have to deal with their disadvantages, such as the weak bond on the matrices for a composite performance and limited thermal performance. Thus, the present study analyzes a combination of alkaline treatment and graphene oxide coating in hemp fibers, an NLF applied in several products but with few investigations in engineering applications. The hemp fibers were thermally characterized with thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The GO-coating was evidenced by the Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy. Changes in crystallinity were presented by X-ray diffraction (XRD). It was observed an increase of about 4% to 11% of the crystallinity after the alkaline treatment. The thermal stability rose about 13°C in the 10 wt% NaOH-treated and GO-coated fibers, and a change of about 3.5°C was detected for the glass transition temperature. The GO-coating effect was also evidenced by changes in Raman spectra and FTIR curves and was visually detected in the scanning electron microscope (SEM).

The environmental impact of petroleum-based materials in driving climate change has stimulated growing interest in natural lignocellulosic fibers (NLFs) as reinforcements for polymeric matrices. NLFs exhibit specific mechanical properties that, in some cases, rival those of synthetic fibers such as aramid, carbon, and glass. Among the wide variety of NLFs, kenaf has been extensively investigated in applications including textiles, construction, and furniture, owing to its long-established global cultivation. Previous studies have also demonstrated its potential as a reinforcement in polymeric matrices for engineering applications, including ballistic protection. In this context, the present work reports, for the first time, on the tensile and dynamic impact toughness of epoxy matrix composites reinforced with 10, 20, and 30 vol% kenaf fibers. The tensile toughness, defined as the area under the stress–strain curve up to fracture, ranged from 9.36 kJ/m² at 10 vol% to 52.30 kJ/m² at 30 vol% fiber content—representing a three- to tenfold increase compared to the neat epoxy matrix. In Izod impact tests, the composites containing 30 vol% kenaf fibers absorbed 22 times more energy than the neat epoxy, rising from 1.8 to 38.8 kJ/m². On average, the tensile toughness values exceeded those of the corresponding dynamic impact toughness. Scanning electron microscopy revealed the fracture morphology and highlighted the influence of the fibers under both toughness conditions.

An increasing interest in the use of sustainable materials as reinforcements in polymer composites is observed, including for ballistic helmets used by the military forces. Typical examples are natural lignocellulosic fibers (NLFs), applied as reinforcement of lightweight, economical, and environmentally friendly composites compared to synthetic fibers such as glass, carbon, and aramid. Their physical and mechanical properties vary according to the origin and characteristics of the fibers, influencing their applications. Hybridization enhances the properties of composites, leading to the investigation of various reinforcement materials. The present study characterizes aluminum, as well as fabrics of flax, a NLF, and aramid, combined with high-density polyethylene (HDPE), as the composite matrix using fourier transform infrared spectroscopy (FTIR), x-ray diffraction (XRD), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC) for possible application as hybrid composites. In the FTIR analysis, the materials presented functional groups compatible with those described in the literature. Additionally, aramid and HDPE showed higher crystallinity values of approximately 69% and 83%, respectively. From TGA and DSC results, it was possible to determine the individual working temperature of the materials, which was about 200 °C, and consider it for the possible composites. These findings are compatible with the requirements for ballistic helmets associated with radiological protections.