The road performance and temperature-regulating properties of asphalt binders modified with novel polyethylene glycol (PEG)/porous silica (PS) form-stabilized phase-change materials (PEG/PS-fs-PCMs) were studied. PS and PEG were used as the supporting substance and PCMs. The results showed that PEG/PS-fs-PCMs could maintain a maximum weight percentage of 70% without leakage, at temperatures as high as 90 °C. The PEG/PS-fs-PCMs exhibited stable chemical structures, excellent thermal stability, high heat storage density, and suitable phase-change temperature. Based on conventional physical tests, the addition of PEG/PS-fs-PCMs can increase the viscosity and the degree of hardness of asphalt binders; thus, achieving an excellent comprehensive performance of the modified asphalt binder depends on determining the optimal dosage of PEG/PS-fs-PCMs. Additionally, incorporating PEG/PS-fs-PCM particles into the asphalt binder can enhance its ability to withstand permanent deformation at elevated temperatures, while PEG/PS-fs-PCMs mainly act as a filler, weakening the cohesive force of the asphalt molecules, and preventing the ductility of asphalt from expansion, according to DSR and BBR tests. Moreover, the use of PEG/PS-fs-PCMs can enhance the heat transfer properties of the asphalt binders, resulting in an improved temperature regulation performance. However, the accumulation of PEG/PS-fs-PCM particles on asphalt binders can negatively impact the storage stability of the modified asphalt binders, because of the difference in density between the two materials.

The purpose of this paper, based on the amount of ultraviolet (UV) radiation in different areas of China, was to give the corresponding measures to prevent UV aging of asphalt. In this paper, based on the average annual amount of UV radiation in China in the past 30 years and the characteristics of UV aging of asphalt, the climatic zoning of UV radiation of asphalt in China was proposed. A variety of base asphalts and styrene–butadiene–styrene block copolymer (SBS) modified asphalts were selected to carry out a UV radiation test, and the relationship between UV radiation amount and viscosity, low-temperature performance, and the rheological properties of asphalt were studied. The equivalent aging indexes of asphalt during UV radiation were selected, the UV aging equation of asphalt was proposed, and the equivalent UV aging relationship among different UV climate zones was established. The prevention and control strategies of UV aging of asphalt among different zones were proposed, and the above theory was verified using a trial road. The main conclusions in the paper are presented: The climate zoning of asphalt UV radiation in China can be divided into three zones: zone I with an annual UV radiation less than or equal to 69.4 kW·h/m² in the last 30 years; zone II with an annual UV radiation of 69.4~81.4 kW·h/m² in the last 30 years; zone III with an annual UV radiation more than or equal to 81.4 kW·h/m² in the last 30 years. The greater the amount of UV radiation, the greater the loss rate of penetration and ductility. For the same kind of asphalt, there is a relatively stable functional relationship between the loss rate and the amount of UV radiation. The results also show that UV radiation changes the proportion of viscous and elastic components in asphalt, showing that the proportion of viscous components decreases and the proportion of elastic components increases. The penetration loss rate and ductility loss rate of asphalt can be used as equivalent UV aging indexes of asphalt. Under the same outdoor UV irradiation time, for asphalt to achieve the same technical performance as zone I, the anti-UV ability of zone II needs to be improved by more than 5%, and that of zone III needs to be improved by more than 10%. Engineering practice has proved that the zoning established in this paper and the corresponding UV control measures are basically reasonable.