Purpose: To evaluate the accuracy of computer-aided dental implant positions obtained with mucosal-supported templates as compared to Three-Dimensional (3D) planning. Materials and methods: One-hundred implants were inserted into 14 edentulous patients using the All-on-4/6 protocol after surgical virtual planning with RealGUIDE, 3DIEMME, and Geomagic software. After 6 months, three-dimensional neck (V) and apex (S) spatial coordinates of implants and angle inclination displacements as compared to virtual plans were evaluated. Results: The S maxilla coordinates revealed a significant discrepancy between clinical and virtual implant positions (p-value = 0.091). The V coordinates showed no significant differences (p-value = 0.71). The S (p-value = 0.017) and V (p-value = 0.038) mandible coordinates showed significant discrepancies between the clinical and virtual positions of the screws. Implant evaluation showed a 1-mm in average of the horizontal deviation in the V point and a 1.6-mm deviation in the S point. A mean 5° angular global deviation was detected. The multivariate permutation test of the S (p-value = 0.02) confirmed the difference. Greater errors in the mandible were detected as compared to the maxilla, and a higher S discrepancy was found in the posterior jaw compared to the anterior section of both the mandible and maxilla. Conclusions: Computer-aided surgery with mucosal-supported templates is a predictable procedure for implant placement. Data showed a discrepancy between the actual dental implant position as compared to the virtual plan, but this was not statistically significant. However, the horizontal and angle deviations detected indicated that flap surgery should be used to prevent implant positioning errors due to poor sensitivity and accuracy in cases of severe jaw atrophy.

Aim: The purpose of the study was the evaluation of the esthetic and physical changes produced on colored titanium Grade 5 (Ti6Al4V) laser treated surfaces to be used in implant dentistry for esthetic success. Materials and methods: Colored titanium surfaces were obtained with laser treatment. The physical and topographic properties were evaluated by stereo, light, and electron microscopy and profilometric analyses. L*a*b* colorimetric coordinates were measured by spectrometry, and the superficial chemical characteristics were evaluated by energy dispersive X-ray analysis. Results: Within the complete palette of titanium colors, pinks (P1-P2), incarnadine (I), and white (W) obtained by laser were selected. The topography, texture, hues, saturation, roughness, and porosity of the samples were compared with those of machined (M) and sand-blasted and etched (SBAE) control surfaces. P1, P2, and I, similar in hue and roughness (Ra ≅ 0.5 μm), had a microgroove spacing of 56 μm and a decreasing porosity. The W sample with a “checkerboard” texture and a light color (L* 96.31) was similar to the M samples (Ra = 0.32 μm), but different from SBAE (Ra = 1.41 μm, L* 65.47). Discussion: The aspects of hard and soft tissue could result in an esthetic failure of the dental implant by showing the dark color of the fixture or abutment. The two different pinks and incarnadine surfaces showed favorable esthetic and physical features to promote dental implant success even in the maxillary anterior area with gingival recession, asymmetry, and deficiency. Conclusion: Titanium colored laser surfaces represent a valid alternative to those currently traditionally obtained and interesting and potential perspectives in the management of dental implants’ esthetic failure.

Alveolar ridge preservation (ARP) is a well-documented procedure to maintain bone volume after tooth extraction in order to place implants. However, at the end of the healing process, the residual biomaterial that is not reabsorbed remains embedded in the bone over time. Ribose cross-linked biomaterials demonstrated their ability to promote osteoconduction and complete resorption. The aim of this study was to evaluate the histological healing pattern of a novel ribose cross-linked collagen sponge used as a grafting material left exposed in human sockets at the time of tooth extraction. On a single patient, non-restorable lower first molars were extracted on both sides, and a ribose cross-linked collagen sponge was placed bilaterally in the cavities and left uncovered at the end of the surgery. After six months, core biopsies were taken immediately prior to implant placement; after the sample preparation, a histological analysis was performed. The results are very promising for substitution with newly formed bone and the amount of residual material. Ribose cross-linked collagen sponge could represent a valid alternative to conventional biomaterials for ARP procedures with no need for flap advancement and/or the addition of a membrane to cover the graft, reducing the invasiveness, complexity, and costs of the treatment.