Reduced-activativon ferritic/martensitic (RAFM) steels are prospective structural materials for fission/fusion nuclear applications because their radiation and swelling resistance outperforms their austenitic counterparts. In radiation environments with a high production rate of helium, such as fusion or spallation applications, these materials suffer from non-negligible swelling due to the inhibited recombination between vacancy and interstitial-type defects. In this work, swelling in helium-implanted Eurofer 97 steel is investigated with a focus on helium production rates in a wide range of helium/dpa ratios. The results show virtually no swelling incubation period preceding a steady-state swelling of about 2 × 10⁻⁴%/He-appm/dpa. A saturation of swelling above 5000 He-appm/dpa was observed and attributed to helium bubbles becoming the dominant sinks for new vacancies and helium atoms. Despite a relatively low irradiation temperature (65 ± 5 °C) and a rather high concentration of helium, transmission electron microscope (TEM) results confirmed a microstructure typical of ferritic/martensitic steels exposed to radiation environments with high production rates of helium.

Positron annihilation spectroscopy (PAS) is widely recognized as a powerful characterization technique in all types of radiation damage studies in nuclear materials. In the past, fission reactor irradiation of reactor pressure vessel (RPV) steels was a primary aim in most studies, while today’s applications of PAS in this field are centered around ion implantation experiments in advanced structural materials. These experiments use hydrogen, helium, heavy ions, and their combination to simulate various radiation environments of future nuclear reactors or nuclear research facilities. The spectrum of ion energies used ranges from a few tens of keV to tens or even hundreds of MeV in proton irradiation or spallation neutron source irradiation experiments. The variety of ion energies, irradiation temperatures, and other experimental conditions poses a major challenge to researchers, who often fail to successfully incorporate the lessons learned from their research. In this paper, we review and supplement recent PAS studies in which structural materials irradiated under a variety of irradiation conditions were investigated using positron annihilation spectroscopy. It summarizes the most important conclusions and lessons learned from the application of PAS in accelerator-based irradiation experiments.

In the present study, graphene oxide foils 10 μm thick have been irradiated in vacuum using same charge state (one charge state) ions, such as protons, helium and oxygen ions, at the same energies (3 MeV) and fluences (from 5 × 10¹¹ ion/cm² to 5 × 10¹⁴ ion/cm²). The structural changes generated by the ion energy deposition and investigated by X-ray diffraction have suggested the generation of new phases, as reduced GO, GO quantum dots and graphitic nanofibers, carbon nanotubes, amorphous carbon and stacked-cup carbon nanofibers. Further analyses, based on Rutherford Backscattering Spectrometry and Elastic Recoil Detection Analysis, have indicated a reduction of GO connected to the atomic number of implanted ions. The morphological changes in the ion irradiated GO foils have been monitored by Transmission Electron, Atomic Force and Scanning Electron microscopies. The present study aims to better structurally, compositionally and morphologically characterize the GO foils irradiated by different ions at the same conditions and at very low ion fluencies to validate the use of GO for radiation detection and propose it as a promising dosimeter. It has been observed that GO quantum dots are produced on the GO foil when it is irradiated by proton, helium and oxygen ions and their number increases with the atomic number of beam gaseous ion.

Structural materials of the new generation of nuclear reactors, fission as well as fusion, must often cope with high production rates of transmutation helium. Their testing hence requires either a powerful source of fast neutrons or a high-fluence ion-irradiation facility providing sufficient amounts of high-energy helium to investigate its effect on the material. Most ion irradiation studies, however, concentrate on basic effects such as defect evolution or bubble swelling in narrow near-surface regions modified by ion bombardment. Studies on bulk samples with a relatively thick implanted region, which would enable, for instance, micromechanical testing, are underrepresented. This gap might be filled by high-fluence multi-energy ion irradiations modifying several tens of micrometres of the investigated substrate. High-energy ion accelerators providing reasonable currents with energies of tens of MeV are rarely employed in such studies due to their scarcity or considerable beamtime costs. To contribute to this field, this article reports a unique single-beam He implantation experiment aimed at obtaining quasi-uniform displacement damage across >60 μm with the He/dpa ratio roughly one order of magnitude above the typical spallation neutron target irradiation conditions. Some technical aspects of this irradiation experiment, along with recent developments and upgrades at the 6 MV Tandetron accelerator of the Slovak university of technology in Bratislava, are presented.