Improving the long-term stability of perovskite solar cells is critical to the deployment of this technology. Despite the great emphasis laid on stability-related investigations, publications lack consistency in experimental procedures and parameters reported. It is therefore challenging to reproduce and compare results and thereby develop a deep understanding of degradation mechanisms. Here, we report a consensus between researchers in the field on procedures for testing perovskite solar cell stability, which are based on the International Summit on Organic Photovoltaic Stability (ISOS) protocols. We propose additional procedures to account for properties specific to PSCs such as ion redistribution under electric fields, reversible degradation and to distinguish ambient-induced degradation from other stress factors. These protocols are not intended as a replacement of the existing qualification standards, but rather they aim to unify the stability assessment and to understand failure modes. Finally, we identify key procedural information which we suggest reporting in publications to improve reproducibility and enable large data set analysis.

The operational stability of perovskite solar cells (PSCs) remains a limiting factor in their commercial implementation. We studied the long-term outdoor stability of ITO/SnO₂/Cs_0.05((CH₃NH₃)_0.15(CH(NH₂)₂)_0.85)_0.95PbI_2.55Br_0.45/spiro-OMeTAD/Au cells, as well as the dynamics of their degradation, under simulated sunlight indoors and their recovery in the dark. The extent of overall degradation was found to depend on processes occurring both under illumination and in the dark, i.e., during the daytime and nighttime, with the dynamics varying with cell aging. Full recovery of efficiency in the dark was observed for cells at early degradation stages. Further cell degradation resulted in recovery times much longer than one night, appearing as irreversible degradation under real operational conditions. At later degradation stages, very different dynamics were observed: short-circuit current density and fill factor exhibited a pronounced drop upon light turn-off but strong improvement under subsequent illumination. The interplay of reversible and irreversible degradation processes with different recovery dynamics was demonstrated to result in changes in the cell’s diurnal PCE dependence during its operational lifespan under real sunlight conditions.

The development of hybrid organic–inorganic halide perovskite solar cells (PSCs) that combine high performance and operational stability is vital for implementing this technology. Recently, reversible improvement and degradation of PSC efficiency have been reported under illumination–darkness cycling. Quantifying the performance and stability of cells exhibiting significant diurnal performance variations is challenging. We report the outdoor stability measurements of two types of devices showing either reversible photo-degradation or reversible efficiency improvement under sunlight. Instead of the initial (or stabilized) efficiency and T₈₀ as the figures of merit for the performance and stability of such devices, we propose using the value of the energy output generated during the first day of exposure and the time needed to reach its 20% drop, respectively. The latter accounts for both the long-term irreversible degradation and the reversible diurnal efficiency variation and does not depend on the type of process prevailing in a given perovskite cell.