Improving the long-term stability of perovskite solar cells is critical to the deployment of this technology. Despite the great emphasis laid on stability-related investigations, publications lack consistency in experimental procedures and parameters reported. It is therefore challenging to reproduce and compare results and thereby develop a deep understanding of degradation mechanisms. Here, we report a consensus between researchers in the field on procedures for testing perovskite solar cell stability, which are based on the International Summit on Organic Photovoltaic Stability (ISOS) protocols. We propose additional procedures to account for properties specific to PSCs such as ion redistribution under electric fields, reversible degradation and to distinguish ambient-induced degradation from other stress factors. These protocols are not intended as a replacement of the existing qualification standards, but rather they aim to unify the stability assessment and to understand failure modes. Finally, we identify key procedural information which we suggest reporting in publications to improve reproducibility and enable large data set analysis.

The organic photovoltaics field is maturing and reaching a technology readiness level where the focus is on developing large scale fabrication methods. In this light, fully inkjet printed organic solar cells were demonstrated. Inkjet printing allows direct patterning of all the layers, including the electrodes, offering full freedom of design without the use of masks or structuring by hardware. The semitransparent front and back electrodes consist of PEDOT:PSS and conductive Ag fingers, avoiding the use of ITO. The inkjet printing of six functional layer demonstrated minimal losses in performance as compared to the lab-scale standard, spin coated devices. All-inkjet printed large area (>1 cm²) organic solar cells with power conversion efficiency of 4.1% deposited from environmentally friendly solvents in an air atmosphere are demonstrated for the first time. Organic solar cells were fabricated using industrial scale (512 nozzles) printheads, compatible with R2R technology. To prove the great advantage of inkjet printing as a digital technology allowing freedom of forms and designs, large area organic solar cells with different artistic shapes were demonstrated. Reported results confirm that inkjet printing has high potential for the processing of OPV, allowing quick changes in design as well as the materials.

The number of publications on perovskite solar cells (PSCs) continues to grow exponentially. Although the efficiency of PSCs has exceeded 25.5%, not every research laboratory can reproduce this result or even pass the border of 20%. Unfortunately, it is not always clear which dominating mechanism is responsible for the performance drop. Here, a simple method of light intensity analysis of the JV parameters is developed, allowing an understanding of what the mechanisms are that appear in the solar cell and limit device performance. The developed method is supported by the drift‐diffusion model and is aimed at helping in the explanation of parasitic losses from the interface or bulk recombination, series resistance, or shunt resistance in the perovskite solar cell. This method can help not only point toward the dominating of bulk or interface recombination in the devices but also determine which interface is more defective. A detailed and stepwise guidance for such a type of light intensity analysis of JV parameters is provided. The proposed method and the conclusions of this study are supported by a series of case studies, showing the effectiveness of the proposed method on real examples.