Citric acid (CA) can be found naturally in fruits and vegetables, particularly citrus fruit. CA is widely used in many fields but its usage as a green modifying agent and binder for wood is barely addressed. Esterification is one of the most common chemical reactions applied in wood modification. CA contains three carboxyl groups, making it possible to attain at least two esterification reactions that are required for crosslinking when reacting with the hydroxyl groups of the cell wall polymers. In addition, the reaction could form ester linkages to bring adhesivity and good bonding characteristics, and therefore CA could be used as wood binder too. This paper presents a review concerning the usage of CA as a wood modifying agent and binder. For wood modification, the reaction mechanism between wood and CA and the pros and cons of using CA are discussed. CA and its combination with various reactants and their respective optimum parameters are also compiled in this paper. As for the major wood bonding component, the bonding mechanism and types of wood composites bonded with CA are presented. The best working conditions for the CA in the fabrication of wood-based panels are discussed. In addition, the environmental impacts and future outlook of CA-treated wood and bonded composite are also considered.

Lignosulfonate features sulfonate groups, which makes it soluble in water and hence, suitable for a wide range of applications. However, its characterization is challenging because of its limited solubility in organic solvents. Thus, this study investigated the chemical and thermal characteristics of ion-exchanged sodium lignosulfonate (Na-LS) and compared it with those of industrial kraft lignin derived from softwood and hardwood. The results demonstrated that the ion exchange successfully converted Na-LS to lignosulfonic acid (H-LS), as proven by the Fourier-transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and elemental analysis. H-LS has a greater apparent molecular weight than those of Na-LS and softwood and hardwood kraft lignin (SKL and HKL). According to ³¹P nuclear magnetic resonance (NMR) analysis, H-LS has less phenolic OH than SKL and HKL, indicating that it has more polymeric chains. Furthermore, H-LS has substantially more native side chains, such as β-O-4 units, than SKL and HKL. Thermal analysis revealed that H-LS has a greater glass temperature (T_g) than SKL and HKL, although Na-LS has a lower T_g than SKL and HKL. In addition, H-LS degraded faster than Na-LS did because the acid condition accelerated degradation reaction.