The depletion of petroleum-based resources and the adverse environmental problems, such as pollution, have stimulated considerable interest in the development of environmentally sustainable materials, which are composed of natural fiber–reinforced polymer composites. These materials could be tailored for a broad range of sustainable industrial applications with new surface functionalities. However, there are several challenges and drawbacks, such as composites processing production and fiber/matrix adhesion, that need to be addressed and overcome. This review could provide an overview of the technological challenges, processing techniques, characterization, properties, and potential applications of NFRPC for sustainable industrial applications. Interestingly, a roadmap for NFRPC to move into Industry 4.0 was highlighted in this review.

Citric acid (CA) can be found naturally in fruits and vegetables, particularly citrus fruit. CA is widely used in many fields but its usage as a green modifying agent and binder for wood is barely addressed. Esterification is one of the most common chemical reactions applied in wood modification. CA contains three carboxyl groups, making it possible to attain at least two esterification reactions that are required for crosslinking when reacting with the hydroxyl groups of the cell wall polymers. In addition, the reaction could form ester linkages to bring adhesivity and good bonding characteristics, and therefore CA could be used as wood binder too. This paper presents a review concerning the usage of CA as a wood modifying agent and binder. For wood modification, the reaction mechanism between wood and CA and the pros and cons of using CA are discussed. CA and its combination with various reactants and their respective optimum parameters are also compiled in this paper. As for the major wood bonding component, the bonding mechanism and types of wood composites bonded with CA are presented. The best working conditions for the CA in the fabrication of wood-based panels are discussed. In addition, the environmental impacts and future outlook of CA-treated wood and bonded composite are also considered.

Wood is a versatile material that is used for various purposes due to its good properties, such as its aesthetic properties, acoustic properties, mechanical properties, thermal properties, etc. Its poor dimensional stability and low natural durability are the main obstacles that limit its use in mechanical applications. Therefore, modification is needed to improve these properties. The hydrothermal modification of wood exposes wood samples to elevated temperatures and pressure levels by using steam, water, or a buffer solution as the treating medium, or by using superheated steam. Abundant studies regarding hydrothermally treated wood were carried out, but the negative effect on the wood’s strength is one of the limitations. This is a method that boosts the dimensional stability and improves the decay resistance of wood with minimal decrements of the strength properties. As an ecofriendly and cost-effective method, the hydrothermal modification of wood is also a promising alternative to conventional chemical techniques for treating wood. Researchers are attracted to the hydrothermal modification process because of its unique qualities in treating wood. There are many scientific articles on the hydrothermal modification of wood, and many aspects of hydrothermal modification are summarized in review papers in this field. This paper reviews the hydrothermally modified mechanical properties of wood and their potential applications. Furthermore, this article reviews the effects of hydrothermal modification on the various properties of wood, such as the dimensional stability, chemical properties, and durability against termites and fungi. The merits and demerits of hydrothermal wood modification, the effectiveness of using different media in hydrothermal modification, and its comparison with other treating techniques are discussed.

The dimensional instability of rubberwood [Hevea brasiliensis (Willd. ex A. Juss.) Müll. Arg.] is one of the major drawbacks that limits its utilization. Therefore, treatment is needed to improve these properties. Hydrothermal treatment in different buffered media is one of the techniques that improve its dimensional stability. The physical properties of hydrothermally treated rubberwood in different buffered media (pH 4, 6, 8, 10) and tap water (pH 7.43) with different temperatures (160 °C, 180 °C and 200 °C) were studied. In this study, physical properties such as equilibrium moisture content (EMC), density (ρ), mass loss (ML), water absorption (WA), volumetric swelling coefficient (VSC), thickness swelling (TS) and anti-swelling efficiency (ASE) were investigated for both treated and untreated specimens. Both the buffered media and temperature significantly affected the physical properties. The results indicated that the EMC (%), ρ (kg/m³), ML (%), VSC (%), TS (%) of treated rubberwood samples reduced as the treatment temperature increased. With the exception of WA (%), as WA increased when the treatment temperature increased from 160 °C to 180 °C but started to decrease when the temperature was further increased to 200 °C. The research study also exhibited that hydrothermal treatment using buffered media at different temperatures enhanced the dimensional stability of the treated samples. Alkaline media gave the best results on the physical properties compared to other treatment medias.

Tannin-furanic foams were prepared with a good yield using the addition of relatively small proportions of a polyflavonoid tannin extract esterified with either palmitic acid, oleic acid, or lauric acid by its reaction with palmitoyl chloride, oleyl chloride, or lauryl chloride. FTIR analysis allowed us to ascertain the esterification of the tannin, and MALDI-TOF analysis allowed us to identify a number of multi-esterified flavonoid oligomers as well as some linked to residual carbohydrates related to the equally esterified tannin. These foams presented a markedly decreased surface friability or no friability at all, and at densities lower than the standard foam they were compared to. Equally, these experimental foams presented a much-improved water repellence, as indicated by their initial wetting angle, its small variation over time, and its stabilization at a high wetting angle value, while the wetting angle of the standard foam control went to zero very rapidly. This conclusion was supported by the calculation of the total surface energy of their surfaces as well as of their dispersive and polar components.

Hydrothermal treatment is an efficient and environmentally friendly method of enhancing the dimensional stability and durability of wood. The destructive effects of formic and acetic acids generated during thermal treatment, on the other hand, are known to have a negative impact on wood strength. As a result, hydrothermal treatment in different buffered media (acidic, neutral, and alkaline buffer) was performed in this study to mitigate the effects of the acids. As heating media, acidic buffer (pH 4 and 6), alkaline buffer (pH 8 and 10), and tap water (pH 7.43) were used to treat rubberwood at three different temperatures (160 °C, 180 °C, and 200 °C). The effects of different buffered media and treatment temperatures on the chemical components, crystallinity, and morphological changes in treated and untreated rubberwood were studied. The results of the experiments revealed that the chemical constituents of rubberwood changed along with the pH of the buffered media and treatment temperature. Rubberwood treated in alkaline media showed the least degradation, whereas water medium caused the most severe degradation. The crystallinity of wood increased initially (from 160 to 180 °C) and then decreased further at 200 °C. In addition, minimal damage to the wood cell was observed in an alkaline medium.