The study investigated the effects of laboratory ageing on the fluxed and water-foamed asphalt binders in scope of Fourier transform infrared spectroscopic measurements of ageing indicators and changes in their chemical composition. The investigated binders included two paving grades, two polymer modified asphalt binders, and a highly modified asphalt binder. The bio-flux additive was produced from rapeseed methyl esters in an oxidation reaction in the presence of a metal catalyst and organic peroxide. The use of the bio-origin additive, in particular oil derivatives, was aimed at softening and better foaming of asphalt binders. This modification is possible due to the good mixability of vegetable oils with an asphalt binder, which gives a homogeneous product with reduced stiffness. The study involved the rolling thin film oven, short-term, and the pressure ageing vessel, long term, and ageing to induce oxidation on the evaluated asphalt binders. The addition of the bio-flux additive has significantly decreased the measured content of ketone compounds related to oxidation in both non-aged and aged asphalt binders, although this effect after ageing were far smaller in magnitude. Additionally, both ageing processes decreased significantly the absorbances in the ester spectral bands specific to the bio-flux additive. All mentioned effects were similar in magnitude in all tested asphalt binders.

Pavement is one of the basic elements of a bridge structure. In Europe and Poland pavements for engineering objects are made in the asphalt technology. Requirements for ensuring the sustainability of the entire object also refer to pavement. Fatigue life is one of the parameter that must be satisfy but there is no requirements connected with it. It is directly related to the stresses and strains which occur in the pavement. Based on a state of art and using calculation results of software with finite element method (FEM) the strains in characteristic points of the bridge pavement were presented. Strains in pavements on the soil, concrete and steel deck were compared. One of the classic and one of the modern criteria for fatigue life were described. Calculation models for fatigue life of asphalt pavement does not classify separately bridge pavements. A typical technology and materials used in the bridge deck pavements were presented. Fatigue life of asphalt bridge pavements were estimated. The analysis of the results and evaluation of the adequacy of fatigue life models were made

The present paper investigates the effects of simultaneous mechanical foaming using water and fluxing with a bio-derived agent on the properties of three distinct asphalt binders: 50/70 paving-grade bitumen, 45/80–55 polymer-modified bitumen, and 45/80–80 highly modified asphalt binder. The testing involved classical tests for assessing binder consistency (penetration at 25 °C, ring and ball softening point, Fraass breaking point, and dynamic viscosity) as well as performance tests (high and low Superpave critical temperatures and multiple stress creep recovery). The tests included assessment directly after asphalt binder foaming and were repeated after a 14-day period. It was shown that bitumen foaming had only short-term effects on the asphalt binders, which did not persist in the repeated tests after 14 days. The fluxing agent that was utilized caused significant changes in the consistency of all asphalt binders. The changes in the performance characteristics of the 50/70 and 45/80–55 binders were severe and amounted to a significant decrease in high-temperature performance of these binders. On the other hand, an improvement in all performance characteristics in the case of the 45/80–80 asphalt binder was observed as a result of the applied processes, particularly when measured 14 days after foaming. This study shows that the simultaneous use of foaming and the fluxing additive decreased the dynamic viscosity of the 45/80–80 binder, while improving its properties relating the pavement performance.

This paper presents the results of an analysis of the changes in the stiffness of asphalt binders modified with a bio-flux additive and subjected to the processes of foaming and short-term ageing. The purpose of the analyses was to determine changes in the rheological properties of asphalt binder as a result of technological processes characteristic of hot and warm mix asphalt technology. Three asphalt binders with similar penetration but varying degrees of polymer modification were tested: 50/70, 45/80–55 polymer-modified bitumen, and 45/80–80 highly modified bitumen. Tests were carried out on four groups of binders: original binders, foamed binders after 14 days of storage, non-foamed binders after Rolling Thin Film Oven Test (RTFOT) ageing, and foamed binders after 14 days of storage subjected to RTFOT ageing. The master curves of the complex shear modulus G* were analysed, and three indexes of binder stiffening were determined, characterising the investigated effects. The tests showed that some of the stiffening indices significantly depended on the degree of polymer modification and the content of the bio-flux additive. Moreover, it was found that the foaming process in the case of paving-grade bitumen and polymer-modified bitumen did not contribute to the additional stiffening of the binders.

Asphalt mixtures are commonly used for the pavement construction for national roads with a high traffic load, as well as local roads with low traffic load. The constructions of local road pavement consisting of thinner, more flexible layers located on less stable subbase than the pavement of national roads, require reinforcement with asphalt layers characterized by increased fatigue life. Technologies that allow quick repairs and reinforcements, while improving the durability of the road pavement are being sought. Such technologies include the use of modifications of asphalt mixtures with special fibers. The paper presents the results of investigations of the properties of asphalt mixtures modified with innovative basalt-polymer fibers FRP. On the basis of the obtained test results according to the Marshall method, stiffness modulus and fatigue durability, the technical properties of asphalt mixtures with FRP fibers addition were improved. This technology significantly increases the fatigue life of asphalt concrete dedicated for repairs and reinforcements of road pavements.

The benefits of the use of cold recycling mixtures (CRMs) in pavement rehabilitation are associated with both the reduction of natural resource consumption by replacing them with recycled materials and the reduction of energy consumption during their production and paving. The evolution of the stiffness of CRMs in road construction and the fatigue life of pavements with CRM base layers are still being investigated. In this paper, CRMs with 1% cement content, called bitumen-stabilized materials with bitumen emulsion (BSM-Es), were examined. Mixtures that were differentiated in terms of Reclaimed Asphalt Pavement (RAP) content, as well as the amount and type of bitumen emulsions, were subjected to indirect tensile stiffness modulus (ITSM) tests at 5 °C, 13 °C, and 20 °C. The thermal sensitivities of the BSM-E mixtures were analyzed. BSM-E mixture stiffness modulus levels at various temperatures were determined using a statistical approach. On the basis of the results obtained, a discussion on the mechanistic-empirical design of flexible pavements with BSM-E base layers is presented. The potential benefits of using BSM-E materials in road construction in certain aspects of pavement life are indicated.