The influence of varying the manganese (Mn) contents of high-strength copper-containing hull steel on its microstructural evolution and mechanical properties was investigated. With increasing Mn content from 2 to 5%, the tensile strength of the steel increased by ~100 MPa, while the elongation of steel remained at ~23.5%, indicating good plasticity. However, the 2Mn sample had 128 J higher low-temperature (−84 °C) impact work than the 5Mn sample. The microstructures of different Mn steels were composed of fresh martensite (FM), ferrite/tempered martensite (F/TM), and reversed austenite (RA). The increase in Mn content markedly increased the presence of RA and intensified the work hardening caused by the transformation-induced plasticity (TRIP) effect during the tensile process. However, as the phase transformation in different Mn steels occurred in the early stage of strain and did not extend throughout the entire plastic deformation process, increasing plasticity via phase transformation was difficult. In addition, although the volume fraction of RA increased significantly in 4Mn and 5Mn steels, the stability of RA significantly decreased. The presence of numerous metastable blocks and coarse lath-like RA contributed little to low-temperature impact work and was even detrimental to toughness. The substantial fresh martensite resulting from phase transformation facilitated microcrack generation, owing to rapid volume expansion and mutual impacts, thus reducing the work required for crack formation. Additionally, the abundance of deformation twins significantly reduced the work needed for crack propagation. These combined actions significantly reduced the low-temperature toughness of 4Mn and 5Mn steels.

The present study investigates the microstructure and mechanical properties of ultra-low carbon bainitic steel (UCBS) under different cold rolling reductions. When the rolling reduction ratios were increased to 80%, the microstructure was refined, and the lath width of the bainite decreased from 601 nm to 252 nm. The ultimate tensile strength and yield strength increased from 812 MPa and 683 MPa to 1195 MPa and 1150 MPa, respectively, whereas the elongation decreased from 15.9% to 7.9%. In addition, the dislocation density increased from 8.3 × 10¹³ m⁻² to 4.87 × 10¹⁴ m⁻² and a stronger γ-fiber texture was obtained at the 80% cold rolling reduction ratio. The local stress distribution and kernel average misorientation were not uniform and became more severe with increased rolling reduction ratios. The strength increment of UCBS was primarily due to boundary strengthening and dislocation strengthening. The theoretical strength increment agreed well with the experimental measurements, which can be helpful for the design and production of UCBS for broad engineering applications.

This study examined the effect of boron (B) on the microstructure and toughness of the simulated coarse-grained heat-affected zone (CGHAZ) of normalized vanadium microalloyed offshore steel by using the welding thermal simulation method under different heat inputs for welding. The results showed that when t_8/5 (the cooling time from 800 to 500 ${}^{\circ }$C) increased from 14 s to 24 s, In the range of t_8/5 of 24–44 s, the impact energy of the CGHAZ rose initially and then remained constant at around 125 J at −40 ${}^{\circ }$C, and dropped to 79 J when t_8/5 increased to 64 s. The particles (Ti,V)(C,N)-BN and BN contributed in the generation of acicular ferrite, which minimized the loss of CGHAZ toughness due to the presence of carbon. Furthermore, the microstructural parameters controlling CGHAZ toughness were the contents of the high misorientation grain boundaries and effective grain size at a tolerance angle of 15${}^{\circ }$ at varied heat inputs.

This study investigated the effects of reheating temperature on the microstructure and mechanical properties of Cu-containing 440 MPa grade non-tempered ship plate steel. The mechanical properties test, thermodynamic simulation, optical microscopy, scanning electron microscopy, transmission electron microscopy, and other tests were performed. The results revealed that with increasing reheating temperature, the ferrite grain size of Cu-containing 440 MPa non-tempered ship plate steel increased. Also, with increasing reheating temperature, the size of copper particles and niobium–titanium composite precipitates in the original austenite decreased. Consequently, this led to a weakening of the pinning effect on the original austenite and an increase in the size of the transformed ferrite grains. Moreover, with increasing reheating temperature, the number of Cu precipitates in the test steel after air cooling and rolling increased, while the size of the precipitates decreased, thereby weakening the solid solution strengthening effect of Cu, and precipitation was enhanced. Additionally, as the reheating temperature increased, the tensile strength and yield strength of the air-cooled test steel after rolling increased, while the impact toughness decreased.

This paper presents a comprehensive study of the impact of quenching roll speed on enhancing the low-temperature toughness of a low-carbon copper-containing steel. The microstructure characteristics, such as the prior austenite grains, and the distribution and volume fraction of precipitates, are observed using optical microscopy, scanning electron microscopy, transmission electron microscopy, and small-angle scattering X-ray. The results show that a decrease in the quenching roller speed (2 m/min) contributes to the achievement of more excellent low-temperature toughness (the average value is 232 J), although the prior austenite grains exhibit a relatively larger size in this case. The tempering treatment results in the precipitation of a large amount of 9R-type Cu-rich particles, regardless of the quenching roller speed. Reducing the quenching roller speed contributes to the increase in the volume fraction of Cu-rich particles, which is considered to be the main factor contributing to the achievement of excellent low-temperature toughness.