The reuse of rubber in concrete results in two major opposing effects: an enhancement in durability and a reduction in mechanical strength. In order to strengthen the mechanical properties of rubber concrete, steel fibers were added in this research. The compressive strength, the four-point bending strength, the mass loss rate, and the relative dynamic elastic modulus of steel fiber reinforced rubber concrete, subjected to cyclic freezing and thawing, were tested. The effects of the content of steel fibers on the freeze–thaw resistance are discussed. The microstructure damage was captured and analyzed by Industrial Computed Tomography (ICT) scanning. Results show that the addition of 2.0% steel fibers can increase the compressive strength of rubber concrete by 26.6% if there is no freeze–thaw effect, but the strengthening effect disappears when subjected to cyclic freeze–thaw. The enhancement of steel fibers on the four-point bending strength is effective under cyclic freeze–thaw. The effect of steel fibers is positive on the mass loss rate but negative on the relative dynamic elastic modulus.

The market demand for manufactured sand has grown rapidly, and the solution to the problem of optimum stone powder content from manufactured sand concrete is imminent. The workability, early age shrinkage strain and cracking, strength, chloride ion penetration, and pore structures of concrete with different stone powder contents were tested to study the influence of stone powder content from manufactured sand concrete. The test results show that the addition of stone powder is beneficial in improving the working performance of manufactured sand concrete. But at the same time, it will increase the amount of concrete water reducer and the total shrinkage strain at an early age. The workability and durability of manufactured sand concrete can be significantly improved by adding an appropriate stone powder. However, excessive stone powder will lead to a reduction in the strength and durability of manufactured sand concrete. It is suggested that the best stone powder content of concrete with a water/cement ratio of 0.32 is 10%, and that of concrete with a water/cement ratio of 0.45 should be less than 20%.

The exposure of recycled concrete (RCA) to a sulphate environment in cold regions makes it crucial to overcome the freeze–thaw cycling effects of recycled concrete. Based on steel and basalt fiber reinforced recycled concrete, the freeze–thaw cycle resistance of recycled concrete was studied by exposure to a sulphate environment. The mass loss, dynamic elastic modulus loss and compressive strength loss of the specimens were studied through freeze–thaw cycle experiments. SEM techniques were used to explore the effect of fiber distribution on the freeze–thaw resistance of recycled concrete. The freeze–thaw mechanism of the basalt fiber and steel fiber recycled concrete exposed to a sulphate environment has also been summarized. The results show that, based on the sulphate environment, the composite fiber recycled concrete has a higher stability in terms of mass loss and relative dynamic modulus of elasticity than single fiber concrete. The compressive strength of S_0.9RC (recycled concrete with 0.9% steel fibers) and BF_5.5RC (recycled concrete containing 5.5 kg/m³ basalt fibers) increased by 8.62% and 13.62%, respectively, compared to normal recycled concrete after 28 days of maintenance; and after 150 freeze–thaw cycles, the compressive strength increased by 41.39% and 47.54%, respectively; compared to ordinary natural aggregate concrete, the compressive strength of S_0.9RC and BF_5.5RC increased by 32.90% and 27.36%, respectively. The compressive strength of the S_1.5BF_7.5RC (recycled concrete with 1.5% steel fibers and 7.5 kg/m³ basalt fibers) composite basalt fiber–steel fiber concrete also increased by 42.82%. SEM techniques indicated that the basalt fiber in the recycled concrete exhibited fracture damage, which inhibited the development of microcracks within the concrete. When the recycled concrete is subjected to coupled sulphate and freeze–thaw cycles, freezing occurs from the outside in, with ice crystals extending along the cracks into the matrix. Prior to freezing, a negative pressure is created by the compression of the air and the contraction of the salt solution, which pulls the external solution inwards. The brine is in a state where ice and water coexist during the continuous cooling process. The salt solution migrates from the inside to the outside during heating and melting.

The addition of graphene oxide (GO) and fly ash (FA) to SFRC (steel fiber reinforced concrete) increases frost resistance. Based on the analysis of the amelioration of GO on the frost resistance of SFRC, the improvement mechanism and the effects of GO and FA on the durability of SFRC were studied in depth. The test blocks’ compressive strength, relative dynamic modulus of elasticity, and mass-loss rate were tested through experiments. The pore distribution and morphological characteristics of concrete were captured by industrial CT scanning technology. The effects of GO and FA on the pore distribution and morphology of the SFRC are discussed. The results show that the compressive strength of GO-SFRC(graphene oxide and steel fiber reinforced concrete)with GO proportion of 0.03% is 28.20% higher than that of ordinary SFRC without freezing and thawing; after 100 freeze-thaw cycles, the compressive strength of the G_0.03S₂₅ increased by 31.70% compared with the compressive strength of the G_0.00S₂₅, and pore shape of G_0.03S₂₅ presents a spherical shape and an elliptical spherical shape; based on the data analysis of the strength loss, relative dynamic elastic modulus loss and mass-loss rate, it is considered that the properties of ordinary SFRC are the worst under freezing and thawing; as FA admixture increases, the porosity decreases; with FA of 30% and GO of 0.03%, the GO-FA-SFRC has the best frost resistance, as well as most of the pores are closed which resemble spheres and ellipsoids.

In order to investigate the effect of phase change materials on the frost resistance of concrete in cold regions, hollow steel balls were used in this paper for the macroscopic encapsulation of the phase change material to replace some of the coarse aggregates in the preparation of phase change concrete. On the premise of ensuring reasonable mechanical properties, concrete mixed with different contents and different surface treatments of grouting steel balls were tested for the compressive strength and splitting tensile strength to determine the optimum content of phase change steel balls and investigate the frost resistance of phase change concrete. At the same time, industrial CT was used to explore the internal pore evolution pattern of concrete during the freeze–thaw period. The test results show that the optimum content of steel balls is 75%; during the freeze–thaw process, the mass loss, relative dynamic elastic modulus loss, and strength loss of phase change concrete are all lower than those of ordinary concrete, and the increase in porosity of phase change concrete is also significantly lower than that of ordinary concrete; the addition of phase change materials can optimise the distribution of the internal pore in concrete, improve its internal pore structure, and enhance its frost resistance.

The metro engineering is in an environment rich in stray current and groundwater, which will accelerate concrete corrosion. In this study, the corrosion of cement-based materials, under stray current, consisting of direct current, was investigated, and the effects of stray current magnitude, water-binder ratio, fly ash, and silica fume on its corrosion were analyzed. The results show that, as the energisation duration of the stray current increases, the mass of the cathode side leachables increases, and the compressive strength of the cement-based materials decreases overall; at 120 d of stray current, the water-binder ratio of 0.50 shows the least reduction in strength, compared to the others; the mass of cathode side leachables decrease significantly with the increase in fly ash content; when fly ash content is 15%, the mass of cathode side leachables is the least, and the decrease in the compressive strength at 120 d of stray current is the smallest. At 10% silica fume content, the mass of the cathode side leachables is the least, and the decrease in the compressive strength of the cement-based materials at 120 d of stray current is the smallest. In general, the corrosion resistance is relatively good at 15% fly ash content and 10% silica fume content under stray current.