In this paper, inorganic silica microspheres with interconnected macroporosity are tested as a platform for designing robust and efficient photocatalytic systems for a continuous flow reactor, enabling a low cost and straightforward purification of wastewater through solar‐driven photocatalysis. The photocatalytically active microspheres are prepared by wet impregnation of porous silica scaffolds with Trizma‐functionalized anatase titania (TiO₂) nanoparticles (NPs). NPs loading of 22 wt% is obtained in the form of a thin and well‐attached layer, covering the external surface of the microspheres as well as the internal surface of the pores. The TiO₂ loading leads to an increase of the specific surface area by 26%, without impacting the typically interconnected macroporosity (≈60%) of the microspheres, which is essential for an efficient flow of the pollutant solution during the photocatalytic tests. These are carried out in a liquid medium for the decomposition of methyl orange and paracetamol. In addition to photocatalytic activity under continuous flow, the microspheres offer the advantage that they can be easily removed from the reaction medium, which is an appealing aspect for industrial applications. In this work, the typical issues of TiO₂ NPs photocatalysts are circumvented, without the need for elaborate chemistries, and for low availability and expensive raw materials.

Polyurea/polyurethane (PUa/PU) shell microcapsules (MCs), containing high loadings of isophorone diisocyanate (IPDI) in the core, were developed to enable the production of mono-component, eco-friendly and safer adhesive formulations for the footwear industry. IPDI microencapsulation was obtained via oil–in–water (O/W) microemulsion combined with interfacial polymerization. A methylene diphenyl diisocyanate (MDI) compound (a commercial blend of monomeric and polymeric species), with higher reactivity than IPDI and low viscosity, was added to the O phase to competitively contribute to the shell formation, improving its quality. Four different active H sources were tested, aimed at achieving a high encapsulation yield. The successful encapsulation of IPDI was confirmed by Fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA), while the MCs’ morphology and size distribution were assessed by scanning electron microscopy (SEM). The incorporation of a multifunctional isocyanate silane in the O phase, as “latent” active H source, led to the formation of impermeable PUa/PU-silica hybrid shell MCs with more than 60 wt.% of pure encapsulated IPDI. A proof-of-concept study shows high peeling strength and a structural type of failure of the adhesive joint, revealing an effective IPDI release. These new engineered MCs are found to be promising crosslinkers for mono-component adhesives for high demanding applications.