In high–strength concrete, the reinforcement concentration will cause some problems in the beam–column joints (BCJs) due to a large amount of transverse reinforcement. Hence, the main object of this paper is to prevent the reinforcement concentration and reduce the amount of transverse reinforcement in the BCJs through the ideal usage of steel fibers and reinforced high–strength concrete. Pseudo–static tests on seven specimens were carried out to investigate and evaluate the seismic performance of beam–column joints in steel fiber reinforced high–strength concrete (SFRHC). Test variables were steel fiber volume ratio, concrete strength, the stirrup ratio in the core area, and an axial compression ratio of the column end. During the test, the hysteresis curves and failure mode were recorded. The seismic indicators, such as energy dissipation, ductility, strength, and stiffness degradation, were determined. The experimental results indicated that the failure modes of SFRHC beam–column joints mainly included the core area failure and the beam end bending failure. With the increase in stirrup ratio, volume ratio of steel fiber, and axial compression ratio in the core area, both the ductility and energy consumption of beam–column joints increased, while the opposite was true for concrete strength.

This paper reports on the flexural behavior of nine steel fiber reinforced-recycled aggregate concrete (SFRAC) beams through combined experimental and finite element analysis. The test parameters in this study include the steel fiber volume fraction, recycled aggregate replacement ratio, and concrete strength. The failure modes, crack development, load-deflection curves, and flexural bearing capacity of SFRAC beams are investigated in detail. The test results indicated that cracks and concrete crushing are formed in the compression zone of all specimens. The flexural bearing capacity of SFRAC beams increases with the increase of steel fiber volume fraction and concrete strength and the decrease of recycled aggregate replacement ratio. In addition, the results are compared with those of the finite element analysis. Based on the uniaxial compressive constitutive model of SFRAC, a new model for calculating the flexural bearing capacity of SFRAC beams is proposed. The prediction and test results are compared to evaluate the accuracy of the developed formula. The studies may provide a considerable reference for designing this type of structure in engineering practice.

Rainfall usually leads to soil slope sliding and instability, which affects the safety of foundation pit, especially in the case of heavy rainfall. This study took the 7.20 Henan rainstorm as the background, where in the process of construction, after three days of rainstorm of 617.7 mm deep, the horizontal displacement of supporting structures of a foundation pit in Zhengzhou city increased by 6.3 mm. Therefore, it is of great significance to study the mechanism of deformation induced by rainstorm of foundation pits. Five numerical models considering different rainfall factors were developed to simulate the rainstorm process based on the monitoring data. The deformation mechanism and the effect factors of deformation on the foundation pit during rainstorm were analyzed, and some preventive measures were put forward for when the foundation pit engineering faces a heavy rainstorm. Under the action of the rainstorm, the supporting structure and the surface settlement had a signification deformation caused by the heavy rainfall on this typical foundation pit, and the maximum bending moment and maximum displacement of the supporting structure shifted up to different degrees. The main factors affecting the deep foundation pit of the metro by heavy rain are the steel strut falling off and the whole foundation pit filling with water, while the influence caused by the rise in the groundwater level, water standing load, and soil softening is small.

The present research study aims to investigate numerically the behavior of steel fiber-reinforced high-strength concrete (SFRHC) beam–column joints (BCJs) under seismic action. Based on the plastic damage constitutive model of concrete and elastic–plastic mixed-strengthen constitutive model of steel material, the finite element software ABAQUS was utilized to establish the 3D finite element (FE) model of BCJs. Additionally, the feasibility and accuracy of the numerical simulation were verified by comparing the computed results and experimental observations in terms of the hysteresis curves, skeleton curves, and failure mode. Furthermore, based on the validated FE modeling approach, load vs. displacement hysteresis curves of SFRHC–BCJs during the loading process were analyzed in detail; the failure process was also investigated. Furthermore, the effect of various parameters on the seismic behavior of BCJs was analyzed comprehensively, including the concrete strength, the volume ratio of steel fiber, and the stirrup ratio in the core area. Finally, parametric studies illustrated that increasing the concrete strength helps in enhancing the ultimate load, while the ductility decreased noticeably. Both adding the steel fiber and increasing the stirrup ratio can significantly improve the seismic performance of BCJs.

To improve the seismic behavior of shear walls, a new composite shear wall composed of a steel-fiber-reinforced high-strength concrete (SFRHC) web and two square concrete-filled steel tube (CFST) columns, namely a steel-fiber-reinforced concrete shear wall with CFST columns, is proposed in this paper. Therefore, the main purpose of this paper is to present an experimental investigation of the seismic behavior of the SFRHC shear wall with CFST columns. Pseudo-static tests were carried out on seven composite shear walls, and the seismic performance of the shear walls was studied and quantified in terms of the aspects of energy consumption, ductility and stiffness degradation. Furthermore, the experimental results indicated that adding steel fiber can effectively restrain the crack propagation of composite shear walls and further help to improve the ductility and energy dissipation capacity of composite shear walls and delay the degradation of their lateral stiffness and force. Moreover, the seismic behavior of the SFRHC shear wall with CFST columns was obviously superior to that of the conventionally reinforced shear wall, in terms of load-bearing capacity, ductility, stiffness and energy dissipation capacity, because of the confinement effect of the CFST columns on the web. Finally, the preliminary study demonstrated that the composite shear wall has good potential to be used in regions with high seismic risk.

Steel fiber reinforced concrete (SFRC) is a novel material of concrete, which has a great potential to be used in practical engineering. Based on the finite element software Opensees, the main objective of this paper presented a numerical simulation method on investigating the seismic behavior of SFRC–beam-column joints (BCJs) through modifying the calculation method of joint shear and longitudinal reinforcement slip deformations. The feasibility and accuracy of the numerical modeling method were verified by comparing the computed results with experimental data in terms of the hysteresis curves, skeleton curves, feature points, energy dissipation, and stiffness degradation. And then, the influences of some key parameters on the seismic behavior of BCJs were investigated and discussed in detail. The parametric studies clearly illustrated that both adding the steel fiber and increasing the stirrup amount of joint core area could significantly improve the seismic behavior of BCJs. The axial compression ratio had limited influence on the seismic behavior of BCJs. Finally, based on the main factors (steel fiber volume ratio, stirrup amount, and axial compression ratio), a formula for predicting ultimate shear capacity is derived.