In this work, we investigated the viability of established hot cracking models for numerically based development of crack-resistant nickel-base superalloys with a high γ′ volume fraction for additive manufacturing. Four cracking models were implemented, and one alloy designed for reduced cracking susceptibility was deduced based on each cracking criterion. The criteria were modeled using CALPHAD-based Scheil calculations. The alloys were designed using a previously developed multi-criteria optimization tool. The commercial superalloy Mar-M247 was chosen as the reference material. The alloys were fabricated by arc melting, then remelted with laser and electron beam, and the cracking was assessed. After electron beam melting, solidification cracks were more prevalent than cold cracks, and vice versa. The alloys exhibited vastly different crack densities ranging from 0 to nearly 12 mm⁻¹. DSC measurements showed good qualitative agreement with the calculated transition temperatures. It was found that the cracking mechanisms differed strongly depending on the process temperature. A correlation analysis of the measured crack densities and the modeled cracking susceptibilities showed no clear positive correlation for any crack model, indicating that none of these models alone is sufficient to describe the cracking behavior of the alloys. One experimental alloy showed an improved cracking resistance during electron beam melting, suggesting that further development of the optimization-based alloy design approach could lead to the discovery of new crack-resistant superalloys.

In the current work we employ multi-phase-field simulations to understand the effect of remelting on microstructure evolution, especially on nucleation of new grains during selective electron beam melting (SEBM) of Ni-based super alloy. The phase-field model is coupled to both mass and heat transport phenomena including release of latent heat of solidification. We run remelting simulations in both as cast and homogenized conditions. Experimental observations show that remelting triggers the nucleation of new grains at the melt pool border. The simulation results shed more light on the local conditions at the melt pool border thereby enhancing our understanding of the mechanisms responsible for the nucleation. The simulation results are validated with experimental results obtained for the Ni–20.5 mol pct Al model binary alloy.

Additive manufacturing (AM) of superalloys has been attracting increasing interest. While most studies focus on the processability and mechanical properties of the finished product, it is also necessary to understand the phase transformations during the consecutive melting processes. Herein, the precipitation and dissolution of the γ′ phase in the Ni‐base superalloy CMSX‐4 in a selective laser melting process is reported. These phase transformations are studied in situ by small‐angle X‐ray scattering (SAXS) during AM. Concurrent wide‐angle X‐ray scattering (WAXS) provides information on the evolution of lattice parameters and temperature during the process. Additional thermal and thermodynamic simulations are carried out to support the experiments. The investigations are focused on the influence of different beam scanning strategies as well as the effect of laser power and scanning speed on the phase transformation dynamics. Due to the high cooling and heating rates inherent to AM, phase transformations occur far off equilibrium. Both precipitation and dissolution of γ′ phase are observed. The scan strategies are shown to have a considerable effect on the phase transformation dynamics, which exceed the impact of the beam parameters. The capability of combined SAXS and WAXS for the in situ study of phase transformations in AM processes is demonstrated.

The development of a sample environment for in situ x-ray characterization during metal Electron Beam Powder Bed Fusion (PBF-EB), called MiniMelt, is presented. The design considerations, the features of the equipment, and its implementation at the synchrotron facility PETRA III at Deutsches Elektronen-Synchrotron, Hamburg, Germany, are described. The equipment is based on the commercially available Freemelt ONE PBF-EB system but has been customized with a unique process chamber to enable real-time synchrotron measurements during the additive manufacturing process. Furthermore, a new unconfined powder bed design to replicate the conditions of the full-scale PBF-EB process is introduced. The first radiography (15 kHz) and diffraction (1 kHz) measurements of PBF-EB with a hot-work tool steel and a Ni-base superalloy, as well as bulk metal melting with the CMSX-4 alloy, using the sample environment are presented. MiniMelt enables time-resolved investigations of the dynamic phenomena taking place during multi-layer PBF-EB, facilitating process understanding and development of advanced process strategies and materials for PBF-EB.