The aim of this work is to study the physical-chemical, mechanical, and biocompatible properties of hydroxyapatite obtained by hydrothermal synthesis, at relatively low temperatures and high pressures, starting from natural sources (Rapana whelk shells), knowing that these properties influence the behavior of nanostructured materials in cells or tissues. Thus, hydroxyapatite nanopowders were characterized by chemical analysis, Fourier-transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS), scanning electron microscopy (SEM), and X-ray diffraction (XRD). In vitro studies on osteoblast cell lines (cytotoxicity and cell proliferation), as well as preliminary mechanical tests, have been performed. The results showed that the obtained powders have a crystallite size below 50 nm and particle size less than 100 nm, demonstrating that hydrothermal synthesis led to hydroxyapatite nanocrystalline powders, with a Ca:P ratio close to the stoichiometric ratio and a controlled morphology (spherical particle aggregates). The tensile strength of HAp samples sintered at 1100 °C/90 min varies between 37.6–39.1 N/mm². HAp samples sintered at 1300 °C/120 min provide better results for the investigated mechanical properties. The coefficient of friction has an appropriate value for biomechanical applications. The results of cell viability showed that the cytotoxic effect is low for all tested samples. Better cell proliferation is observed for osteoblasts grown on square samples.

Microwave heating represents a modern technique to sintering the composites materials. The microwaves absorbance property of the materials is depending by the electrical permittivity of the materials. Researchers showed that the ceramic materials are suitable for sintering using microwave heating. The most important advantage of that sintering procedure is the reduced sintering time and temperatures. However, during the heating process these properties are changing and a pattern of the heating process cannot be established. The penetration depth of microwaves into materials depends on the electrical properties of them, and gives rise to a heat source. The electromagnetic wave absorption is responsible for the macro and micro structural changes in the materials morphology, and consequently for their electrical properties. Thermal runaway is one phenomenon which should be avoided during the microwave processing of the materials. The microwave heating consists in direct introduction of the energy in the volume of the material. If the absorbance properties of the material are increasing with temperature, than a critical phenomenon, called thermal runaway, appears during the heating process. This paper aims to study the thermal runaway of the BaCO₃ + Fe₂O₃ homogenous mixture and mechanical alloy in a mono-mode applicator, when the heat source is a microwave generator at 2,45 Ghz. A special mono-mode chamber has been designed with dimensions 140 x 140 x 70 mm and an active system for rotating the samples, in order to record the values of the temperature and to assure a uniform exposure of the samples to the high frequency electromagnetic field. The materials used in experiments were homogenous mixture of BaCO₃ + Fe₂O₃ which have been milled in a planetary ball mill for 5 and 20 hours. The experimental procedure consists in establishing the levels of the temperatures during the microwave heating process when the thermal runaway appears. These experiments have been done for fixed levels of microwave injected power from 0 1250 W. Numerical simulation for different heating conditions (microwave power, heating time, position of the samples inside the chamber) has been performed in order to elaborate a predictable mathematical model for continuous microwave heating and avoiding the thermal runaway of the homogenous mixture.

The solid waste of Rapana thomasiana seashells both from domestic activities and natural waste on seashore can be used to obtain viable products for medical applications. However, conventional technologies applied for sintering the materials require massive energy consumption due to the resistance heating. Microwave heating represents an advanced technology for sintering, but the stability of the process, in terms of thermal runaway and microwave plasma arc discharge, jeopardizes the quality of the sintered products. This paper aims to present the results of research focused on viable heating technology and the mechanical properties of the final products. A comparative analysis, in terms of energy efficiency vs. mechanical properties, has been performed for three different heating technologies: direct microwave heating, hybrid microwave heating and resistance heating. The results obtained concluded that the hybrid microwave heating led to final products from Rapana thomasiana solid waste with similar mechanical properties compared with resistance heating. In terms of energy efficiency, the hybrid microwave heating was 20 times better than resistance heating.

The inland navigation sector makes a significant contribution to the growth of the global economy as well as to climate change due to pollutants emitted by diesel engines. NOx emissions are very high in port areas where, due to traffic, the ships run at idling regimes. Selective catalytic reduction (SCR) represents one of the most suitable technologies, in terms of cost effectiveness, but does not perform well if the temperature during vessel operation is lower than 180 °C. Microwave technology can support preheating of the ceramic core of SCR in order to increase the temperature towards the optimal interval for the best NOx reduction. Research has focused on coupling a magnetron head to a SCR device in order to evaluate to what extent the technology can meet the requirements of Stage V of the European Directive related to NOx emissions. Measurements of NOx emitted have been performed on engines with 603.5 kW nominal power and 1500 rpm that operate at a lower engine speed (700–1200 rpm) and output power (58–418 kW). The values recorded for emissions using microwave heating of ceramic core of SCR have decreased by 89% for a constant load of engine and idling engine speed.