This study assessed the efficacy of five denture cleansers on the microbial adherence and surface topography of conventional and CAD/CAM denture base resins. Acrylic resin discs were fabricated using conventional, milling, and 3D printing methods (N = 180). The discs were contaminated with dual species of Candida albicans and Streptococcus mutans biofilm for 72 h and then disinfected with either of the denture cleansers (Fittydent cleansing tablets, 2% Chlorhexidine gluconate, 0.2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite (n = 10). Distilled water served as the control group. The colony-forming units of the microorganisms were calculated, followed by post-treatment surface roughness. Data were statistically analyzed using one-way ANOVA, paired t-test, and post hoc Tukey HSD test (α = 0.05). Among the denture cleansers, 2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite had the best cleansing effect on the resin discs and demonstrated zero growth of colonies for both the species. Comparing the material groups, the 3D-processed discs showed higher colony-forming units followed by the conventional and CAD/CAM milled group. The highest surface roughness was demonstrated by the 3D-printed discs (0.690 ± 0.08 μm), followed by the conventional (0.493 ± 0.11 μm) and the milled groups (0.301 ± 0.08 μm). The tested chemical denture cleansers affected the Candida albicans and Streptococcus mutans adhesion compared to control discs immersed in distilled water. The clinician may recommend to their patient to use 2% chlorhexidine gluconate for the disinfection of CAD/CAM PMMA denture base materials.

This study assesses the retreatability of TotalFill bioceramic (TFBC) and AH Plus (AHP) sealers and their impact on retreatment force and torque. Twenty-six premolar teeth with single oval canals were instrumented, obturated using the matched gutta-percha cone technique with one of the tested sealers, and then temporized. After a 6-month incubation at 37 °C and 100% humidity, the canals were retreated with the XP Shaper system. During retreatment, the generated force and torque were measured. Micro-CT scanning was run before and after the retreatment procedure to analyze the remaining obturating materials in the canals. The apically directed maximum force in AHP was higher than that in TFBC. The coronally directed maximum force and the maximum torque were comparable between the groups. A higher amount of remaining obturating materials was found in the AHP compared to that in the TFBC. Based on these findings, endodontic sealer had an influence on retreatability, and the TFBC showed less remaining obturating materials and lower retreatment forces in the apical direction compared to the AHP in extracted teeth with oval canals.