Al-Fouzan AF, et al. J Adv Prosthodont. 2017 Oct;9(5):402-408. https://doi.org/10.4047/jap.2017.9.5.402

Alfouzan AF, et al. J Adv Prosthodont. 2021 Jun;13(3):160-171. https://doi.org/10.4047/jap.2021.13.3.160

This study assessed the efficacy of five denture cleansers on the microbial adherence and surface topography of conventional and CAD/CAM denture base resins. Acrylic resin discs were fabricated using conventional, milling, and 3D printing methods (N = 180). The discs were contaminated with dual species of Candida albicans and Streptococcus mutans biofilm for 72 h and then disinfected with either of the denture cleansers (Fittydent cleansing tablets, 2% Chlorhexidine gluconate, 0.2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite (n = 10). Distilled water served as the control group. The colony-forming units of the microorganisms were calculated, followed by post-treatment surface roughness. Data were statistically analyzed using one-way ANOVA, paired t-test, and post hoc Tukey HSD test (α = 0.05). Among the denture cleansers, 2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite had the best cleansing effect on the resin discs and demonstrated zero growth of colonies for both the species. Comparing the material groups, the 3D-processed discs showed higher colony-forming units followed by the conventional and CAD/CAM milled group. The highest surface roughness was demonstrated by the 3D-printed discs (0.690 ± 0.08 μm), followed by the conventional (0.493 ± 0.11 μm) and the milled groups (0.301 ± 0.08 μm). The tested chemical denture cleansers affected the Candida albicans and Streptococcus mutans adhesion compared to control discs immersed in distilled water. The clinician may recommend to their patient to use 2% chlorhexidine gluconate for the disinfection of CAD/CAM PMMA denture base materials.

Denture wearers are advised to follow the protocol of using both mechanical and chemical hygiene methods. In this study, the in-vitro color stability of heat-cured, light-cured and newly developed pre-polymerized CAD/CAM acrylic resin base materials were evaluated after exposure to mechanical brushing and chemical denture cleansers. Two polymethyl methacrylate (PMMA) (heat-cured, and pre-polymerised CAD/CAM) and one urethane dimethacrylate based resin denture base material were subjected to mechanical brushing, followed by immersion in chemical denture cleansers (Corega, 5.25% Sodium hypochlorite (NaOCl), and 0.2% chlorhexidine gluconate (CHG)) and thermal-cycling to simulate one-year of normal prosthesis use. Baseline and final color measurements were determined and the difference in color was calculated using bench-top UV light visible spectrophotometer. The highest (29.69 ± 1.84) and lowest (19.03 ± 8.78) mean ΔE was observed with light-cured and CAD/CAM materials immersed in 0.2% CHG, respectively. Tukey’s post-hoc test showed that heat cured and light-cured resins immersed in either of the denture cleansers showed no significant differences (p > 0.05) in the mean ΔE values. On the contrary, CAD/CAM materials immersed in either of the denture cleansers demonstrated significant differences in the mean ΔE values (p ≤ 0.05). A statistically significant interaction between the combination of materials and denture cleansers (F = 4.890; p = 0.001) was observed. The color stability of the pre-polymerized CAD/CAM acrylic discs is comparatively better than the conventional acrylic resin materials. The changes in the color values of all the tested materials were above the clinically acceptable range, regardless of the type of denture cleanser used.