For the purpose of studying compact strip production (CSP) funnel-shaped mold and flexible thin-slab rolling (FTSR) funnel-shaped mold, a three-dimensional (3D) multi-field coupling mathematical model was established to describe the electromagnetic braking (EMBr) continuous casting process. To investigate the metallurgical effect of EMBr in the CSP and FTSR funnel-shaped thin-slab molds, a Reynolds-averaged Navier–Stokes (RANS) turbulence model, together with an enthalpy–porosity approach, was established to numerically simulate the effect of ruler EMBr on the behaviors of melt flow, heat transfer, solidification, and inclusion movement in high-speed casting. The simulation results indicate that the application of ruler EMBr in the CSP and FTSR molds shows great potential to improve the surface temperature of molten steel and reduce the penetration depth of downward backflow. This contributes to the melting of the slag rim near the meniscus region and facilitates the floating removal of the inclusions in the molten pool. In addition, in comparison with the case of no EMBr, the parametric study shows that the braking effect of ruler EMBr with an electromagnetic parameter of 0.5 T can enhance the upward backflow in the two high-speed thin-slab molds. The enhanced upward backflow can successfully entrain the inclusions to the top of the mold and improve the activity of surface fluctuations to avoid the formation of the slag rim. For instance, for the ruler EMBr applied to the FTSR mold, the maximum amplitude of surface fluctuation and the floatation removal quantity of inclusions with a diameter of 100 μm are increased by 4.6 percent and 51 percent, respectively.

Electromagnetic braking (EMBr) technology, as one of the most effective technologies in the continuous casting process, provides an effective tool for improving the internal and external defects of steel products. Specifically, the EMBr technology takes the benefit of the generation of Lorentz force to decrease flow instability, mold powder entrapment, and surface defects, if applied properly. For this purpose, to gain a clear understanding of the effect of EMBr technology on the continuous casting process, a commonly used EMBr technology, namely ruler EMBr technology, is applied in the current work to investigate the dynamic behaviors of molten steel flow and steel–slag interface fluctuation inside a slab mold. Furthermore, to obtain a desirable braking effect of the ruler EMBr technology, operational parameters including the magnetic flux density, submerged entry nozzle (SEN) depth, and magnetic pole location are numerically investigated. The results demonstrate that the braking effect exerted by the ruler EMBr device is favorable for suppressing the impact of upward stream on the steel–slag interface with the magnetic flux density exceeding 0.3 T. For the influence of the SEN depth and magnetic pole location on the effect of ruler EMBr mold, the results show that a steady jet flow pattern can be obtained through the adjustment of a location between the ruler EMBr device and the SEN depth. For instance, when the ruler EMBr device installation position of 225 mm corresponds to the SEN depth of 150 mm, the upward deflection of jet stream is suppressed and a stable interface fluctuation profile is formed. With this adjustment, the possibility of mold flux entrapment is decreased.

To control well the surface fluctuation of liquid metal in a slab mold, a new type of combined permanent magnets braking system, namely a permanent magnet flow control mold (PMFC-Mold) is proposed by our research group, of which its main feature is that the device can control the flow of molten steel in the mold without additional energy. To observe the fluctuation state of the alloy with the PMFC-Mold, instantaneous surface fluctuations were recorded by a laser level meter and camera. To study the effect of various casting speeds and permanent magnet placement on surface fluctuations, the three measurement points, which were 7, 18, and 36 mm away from the narrow surface of the mold, were selected to record the trend of level fluctuation. Three types of permanent magnet placement were designed by setting the differences between the height center of the permanent magnet and the free surface in the slab mold, which were H₁ = 0 mm, H₂ = −25 mm, and H₃ = −75 mm. The experimental results indicated that with the acceleration of the casting speed, the average height and standard deviation of surface fluctuation at the measurement point increased, but the surface fluctuation pattern remained. When the permanent magnets were arranged at H₁ = 0 mm and H₂ = −25 mm, the position of the magnetic field was reasonable and the surface fluctuation could be effectively suppressed. In contrast, when the permanent magnets were arranged at H₃ = −75 mm, the level fluctuation was intensified.