The application of a novel Poly(3,4-ethylenedioxythiophene)-Tyrosinase/Sonogel-Carbon electrode (PEDOT-Tyr/SNGC) biosensor to beers and wines analysis is proposed. This biosensor implies a new Sinusoidal Current (SC) electrodeposition method to immobilize the enzyme generating a nanostructure surface. The biosensors were characterized electrochemically, employing cyclic voltammetry and electrochemical impedance spectroscopy. Sensitivity, limit of detection, and correlation coefficients of the linear fitting were 2.40 × 10⁻⁴ µA·µM⁻¹, 4.33 µM, and R² = 0.9987, respectively. Caffeic acid is used as the reference polyphenol. A sampling of nine beers (four lager, three stout, and two non-alcoholic beers), and four wines (three red and one white wine) purchased in a local store was performed. The Polyphenol indeces for beers and wines have been assessed using the proposed biosensor, and the obtained values are in agreement with the literature data. Antioxidant properties of the samples using the 2,2′-azino-bis(3-ethylbenzothiazoline-6-sulphonic acid (ABTS) radical spectrophotometric method were also evaluated. The correlation between the polyphenol index and the antioxidant capacity was obtained for beers and wines.

Conducting polymers (CPs) are extensively studied due to their high versatility and electrical properties, as well as their high environmental stability. Based on the above, their applications as electronic devices are promoted and constitute an interesting matter of research. This review summarizes their application in common electronic devices and their implementation in electronic tongues and noses systems (E-tongues and E-noses, respectively). The monitoring of diverse factors with these devices by multivariate calibration methods for different applications is also included. Lastly, a critical discussion about the enclosed analytical potential of several conducting polymer-based devices in electronic systems reported in literature will be offered.

In this paper, we report for the first time a novel, simple and fast method for the synthesis of magnetic molecularly imprinted polymers (Mag-MIPs) based on high-energy ultrasound probe. Sulfamethoxazole (SMX) was used as template molecule, methacrylic acid as functional monomer, ethylene glycole dimethacrylate as crosslinking agent and magnetic nanoparticles (NPs) as the supporting core. The effects of time (5, 7.5 and 10 min) and the applied amplitude (20, 30, 40, 50 and 60%) using the ultrasound probe for the synthesis of Mag-MIPs were studied and optimized. By applying the proposed synthesis method, the US-magMIPs synthesis time was satisfactorily reduced from several hours to a few minutes (7.5 min) in a simple way. For comparison purposes, the Mag-MIP and the non imprinted polymer (MagNIP) were also synthesized employing an ultrasound bath assisted approach (2 h, 65 °C). Magnetic NPs and US-magMIPs synthesized by both ways were investigated by means of several characterization techniques such as Fourier Transform Infrared (FT-IR) spectroscopy, Scanning/Transmission electron microscopy (SEM and STEM modes), X-Ray Diffraction (XRD), Vibrating Sample Magnetometer (VSM) and Dynamic Light Scattering (DLS). The results obtained confirms clearly the formation of magnetic NPs and their successful decoration by the imprinted polymer in both synthesis ways. The sulfonamide binding efficiency of US-magMIPs synthesized by the ultrasound probe and ultrasound bath were investigated according to the adsorption isotherm. The obtained results showed that the US-magMIP synthesized with the probe has more binding capacity compared to the one synthesized with US bath. The adsorption time was studied and both synthesized US-magMIPs reached the maximum adsorption capacity toward SMX after 1 h and the US-magMIP probe tends to have more easiness to bind SMX in less time. The selectivity studies of the synthesized US-magMIPs based on probe and bath showed a high affinity for SMX compared to its structural analogues such as sulfadiazine, sulfamerazine and sulfacetamide.