This paper presents the results of tests on the railway disc brake with regard to the weight wear of friction pads. The tests were carried out at a certified brake test bench where the friction-mechanical characteristics of the railway brake were determined. The test stand was additionally equipped with a thermal imaging camera to observe the contact between the brake pads and the brake disc. The scientific goal of the test is to evaluate the relationship between the weight wear of friction pads and the quantities characterizing the braking process. The quantities characterizing the braking process included pad-to-disc contact area, friction pad thickness, pad-to-disc pressure, and braking speed. A regression model to estimate the friction pad wear on the basis of a single braking with the given input quantities was determined. The greatest influence on the increase in weight wear of friction pads has the braking velocity, which was confirmed by the value of the correlation coefficient of the regression model at value 0.81. The pressure of the friction pad to the disc and the friction pad thickness do not have a significant effect on the weight wear described by the regression model, and the obtained correlation coefficient for these parameters was lower than the value of 0.2.

The article presents the results of friction and vibroacoustic tests of a railway disc brake carried out on a brake stand. The vibration signal generated by the friction linings provides information on their wear and offers evaluation of the braking process, i.e., changes in the average friction coefficient. The algorithm presents simple regression linear and non-linear models for the thickness of the friction linings and the average coefficient of friction based on the effective value of vibration acceleration. The vibration acceleration signals were analyzed in the amplitude and frequency domains. In both cases, satisfactory values of the dynamics of changes above 6 dB were obtained. In the case of spectral analysis using a mid-band filter, more accurate models of the friction lining thickness and the average coefficient of friction were obtained. However, the spectral analysis does not allow the estimation of the lining thickness and the friction coefficient at low braking speeds, i.e., 50 and 80 km/h. The analysis of amplitudes leads to the determination of models in the entire braking speed range from 50 to 200 km/h, despite the lower accuracy compared to the model, based on the spectral analysis. The vibroacoustic literature presents methods of diagnosis of the wear of various machine elements such as bearings or friction linings, based on amplitude or frequency analysis of vibrations. These signal analysis methods have their limitations with regard to their scope of use and the accuracy of diagnosis. There are no cases of simultaneous use of different methods of analysis. This article presents the simultaneous application of the amplitude and frequency methods in the analysis of vibroacoustic signals generated by brake linings. Moreover, algorithms for assessing the wear of friction linings and the average coefficient of friction were presented. The algorithm enables determination of the time at which the friction linings should be replaced with new ones. The final algorithm analyzes the vibration acceleration signals using both amplitude analysis for low braking speeds, as well as spectral analysis for medium and high braking speeds.

The article presents the state of knowledge and research in the field of surface cracks occurring in disc braking systems of rail and car vehicles. The craze formed during the operation of vehicles is particularly dangerous and leads to breaking the disc into several pieces. It may lead to a loss of braking force and damage to the entire disc brake caliper. The main aim of the research is to identify surface cracks in brake discs made of cast iron and use experimental methods to estimate their depth. Research were conducted on the disc braking system developed by the authors. In examining the location and depth of cracks, the penetration method, ultrasound, as well as a special probe were used. This device measures the crack depth based on the electrical resistance between two points on the surface of the metallic object. The tests showed that the first microcracks on the brake discs appeared after 309 braking tests on the test stand. In addition, it was observed that the surface cracks length of the disc increased linearly to depth until they reached about 11.5–12 mm with corresponded to crack lengths in the range of 65–70 mm. However, determination of the regression functions presented in the article allows to estimate the depth of surface cracks up to 70 mm long on cast iron brake discs by measuring their length.

Increasing the speed of trains forces the application of a greater braking power, i.e. the capability of the brake system of rapidly absorbing and dispersing the stored heat energy. The instability of operation results from the occurrence of vibrations on the friction component, which affects the efficiency of the braking process. In practice, it means that when braking, the vehicle variable friction resistance may lead to an uneven braking process. The effects of such changes can be manifested in the form of vibrations with high input amplitude. The vibrations generated by the working components are distributed throughout the vehicle, which also adversely affects the driving comfort. The purpose of this paper is to determine the resonant frequencies of selected components of the railway disc brake. This paper presents a method of assessing the thickness of the brake pads of a railway disc brake based on the results of parameterization of the time-frequency map a(t, f) of vibrations generated by the brake components. Methods of time-frequency analysis were suggested as a tool of time-frequency selection of the vibration signal. The authors described an algorithm of the method and presented an example illustrating the application of the synchronously averaged short-time Fourier transform for the extraction of the signal components related to the braking process. As a result of parameterization of the map a(t, f) signal parameters, values covariant with the thickness of the disc brake were obtained.

This article presents the results of tests conducted on the average and instantaneous friction coefficients of railway vehicle disc brakes. The tests were carried out independently of various states of wear on the friction linings and the brake disc. The requirements of the International Union of Railways (UIC) regarding the approval of brake linings for use were taken into account. Based on many years of research using a brake bench to test railway disc brakes, the authors developed multiple regression models for the average friction coefficient and fluctuations (tolerances) in the instantaneous friction coefficient and achieved 870 results. The models proposed three types of variables: the input braking parameters (speed, pressure, and mass to be braked), operational parameters (the wear on the friction linings and the brake disc), and design parameters (perforations in the form of holes on the disc surface). The above two models were validated on the basis of 384 brakes, and in subsequent stages a further evaluation was performed. The coefficients were determined to be, respectively, 0.99 for the model of the average friction coefficient and 0.71 for the model of tolerance (fluctuations) of the instantaneous friction coefficient.

The technology and methods of testing the properties of varnish coatings used in motor vehicles are constantly and successfully developed. However, in the case of automotive varnish renovation coatings used in the repair of car bodies, the problem of fitting the quality of these coatings to the quality and current condition of the coating applied to undamaged vehicle components is not definitely solved. The main goal of the research was to determine the thickness and gloss distribution of the varnish coatings. The thickness and gloss of the varnish coating on the entire body of the vehicle were measured. Classical methods of assessing these properties were used. Defects in the renovation coating were also simulated, to show their negative impact on the varnish quality. The performed tests allowed for development of a procedure and algorithm for evaluation of the quality of the car’s renovation coating after the repair of the car body. The proposed procedure, expressed with the presented algorithm, allows to fit the obtained renovation coating to the quality and condition of the coating manufactured in factory on the car body in the range of its thickness up to 270 µm and gloss in the range of 5–90 GU. The developed procedure for the assessment of renovation coatings can be used in workshops that repair vehicle bodies. This will allow to improve the quality of renovation coatings and bring their properties, such as thickness or gloss, closer to those applied to the vehicle’s body at the factory.