The technology and methods of testing the properties of varnish coatings used in motor vehicles are constantly and successfully developed. However, in the case of automotive varnish renovation coatings used in the repair of car bodies, the problem of fitting the quality of these coatings to the quality and current condition of the coating applied to undamaged vehicle components is not definitely solved. The main goal of the research was to determine the thickness and gloss distribution of the varnish coatings. The thickness and gloss of the varnish coating on the entire body of the vehicle were measured. Classical methods of assessing these properties were used. Defects in the renovation coating were also simulated, to show their negative impact on the varnish quality. The performed tests allowed for development of a procedure and algorithm for evaluation of the quality of the car’s renovation coating after the repair of the car body. The proposed procedure, expressed with the presented algorithm, allows to fit the obtained renovation coating to the quality and condition of the coating manufactured in factory on the car body in the range of its thickness up to 270 µm and gloss in the range of 5–90 GU. The developed procedure for the assessment of renovation coatings can be used in workshops that repair vehicle bodies. This will allow to improve the quality of renovation coatings and bring their properties, such as thickness or gloss, closer to those applied to the vehicle’s body at the factory.

Non-destructive ultrasonic testing can be used to assess the properties and condition of real machine elements during their operation, with limited (one-sided) access to these elements. A methodological question then arises concerning the influence of the material properties of such elements and the condition of their surfaces on the result of ultrasonic testing. This paper attempts to estimate the influence of material hardness and surface roughness on the result of such testing study area testing machine or plant components of unknown exact thickness. Ultrasonic testing was carried out on specially prepared steel samples. These samples had varying surface roughness (Ra from 0.34 to 250.73 µm) of the reflection surface of the longitudinal ultrasonic wave (the so-called reflectors) and hardness (32 and 57 HRC). The ultrasonic measures were the attenuation of the wave, estimated by the decibel drop in the gain of its pulses, and the propagation velocity of the longitudinal ultrasonic wave. Ultrasonic transducers (probes) of varying frequencies (from 2 to 20 MHz), excited by a laboratory and industrial defectoscope were used as the source of such a wave. The results of our research provide a basis for the recommendation of two considered ultrasonic quantities for assessing the material properties of the tested element. This is of particular importance when testing machines or plant components of unknown exact thickness and unknown roughness of inaccessible surfaces, which are the reflectors of the longitudinal ultrasonic wave used for testing. It has been demonstrated that by using the ultrasonic echo technique, it is possible to evaluate the roughness and hardness of the tested elements.

Ultrasonic nondestructive testing is widely used not only in the laboratory, but also in industry. The tests use various types of ultrasonic waves, diverse measurement techniques and different apparatus. One of the problems encountered is the high susceptibility of the surface wave to interference. Some of the interference is random in nature and can be minimized (e.g., contamination of the surface or resting a finger on the surface under study). Some of the interference is permanent in nature, such as variable surface roughness. The aim of the conducted research was to evaluate the influence of roughness on ultrasonic wave propagation. The study used samples with surface roughness Sa from 0.28 to 219 µm, and ultrasonic surface wave probes with frequencies from 1.41 to 8.02 MHz. It was observed that roughness significantly affects the attenuation of the ultrasonic wave, and the differences in signal amplification reached more than 15 dB. Similarly, the effect of the ultrasonic wave’s transit time through surfaces of different roughness was noted. It was found that the difference in the ultrasonic wave transition time was more than 50 µs. The results of the study can be helpful for the ultrasonic testing of materials with different surface conditions.

The article presents the results of ultrasonic testing of Ti6Al4V material produced by the conventional method and the laser bed fusion method. Modern manufacturing techniques, such as additive manufacturing, allow the production of parts with complex shapes. It is important to control the condition of such components throughout their lifetime. The purpose of this article was to determine the basic acoustic properties of Ti6Al4V material produced by two different methods—bar drawing and the additive manufacturing method. On this basis, an inspection scheme was developed for adhesive joints, the components of which are made by additive manufacturing technology. The decibel drops in the amplitudes of pulses reflected from the boundary of the adhesive-Ti6Al4V-AM and adhesive-Ti6Al4V joints were determined. The decibel drops for the connection of materials made with additive technology are higher than for the material made in a conventional way. The difference in decibel drop in the amplitudes of the additive manufactured material versus the drawn rod, depending on the ultrasonic head, can be up to 60%. The results of the study provide an important practical guideline for testing adhesive joints of parts made with additive manufacturing technology.

Adhesive bonding is widely used in modern industry. It has many advantages—the main one being the reduction in production costs. It also has certain limitations. One of the limitations of adhesive bonds is the relatively long bonding time of the joints. The main objective of this research was to determine the possibility of studying the kinetics of adhesive bond formation using a non-destructive ultrasonic method. A research experiment was planned and carried out. Adhesive specimens were prepared, and their quality changes over time were evaluated. In addition, the change in ultrasonic measures during the testing of these bonds was evaluated, as well as the hardness of the adhesive. In this study, the choice of test apparatus was made, in particular ultrasonic probes for the adhesive used and the materials to be bonded. The choice of adhesive was also made, for one in which bonding phenomena occur uniformly throughout the volume. This work examined the changes in the mechanical strength and hardness with time. The tests showed that the greatest changes in mechanical strength occur within the first 24 h after the bond was made. With the mechanical strength reaching 12.6 Mpa after 216 h, the strength in the first 24 h was 10.36 (for bonded steel sheets). For bonded steel discs, the maximum tensile strength was 26.99 Mpa (after 216 h), with a hardness of 22.93 Mpa during the first 24 h. Also, significant changes were observed in the adhesive hardness during the first 24 h. The hardness of the adhesive after 216 h was 70.4 Shore’a on the D scale, while after 24 h it was 69.4 Shore’a on the D scale. Changes in the ultrasonic parameters of the adhesive bond quality were found to occur along with changes in the bond quality.

Ultrasonic nondestructive testing is widely used not only in the laboratory, but also in industry. The tests use various types of ultrasonic waves, diverse measurement techniques and different apparatus. One of the problems encountered is the high susceptibility of the surface wave to interference. Some of the interference is random in nature and can be minimized (e.g., contamination of the surface, resting a finger on the surface under study). Some of the interference is permanent in nature, such as variable surface roughness. The aim of the conducted research was to evaluate the influence of roughness on ultrasonic wave propagation. The study used samples with surface roughness Sa from 0.28 to 219µm, and ultrasonic surface wave probes with frequencies from 1.41 to 8.02 MHz. It was observed that roughness significantly affects the attenuation of the ultrasonic wave, and the differences in signal amplification reached more than 15dB. Similarly, the effect of the ultrasonic wave's transit time through surfaces of different roughness was noted. It was found that the difference in the ultrasonic wave transition time was more than 50 µs. The results of the study can be helpful, for ultrasonic testing of materials with different surface conditions.