This paper presents the results of tests on the railway disc brake with regard to the weight wear of friction pads. The tests were carried out at a certified brake test bench where the friction-mechanical characteristics of the railway brake were determined. The test stand was additionally equipped with a thermal imaging camera to observe the contact between the brake pads and the brake disc. The scientific goal of the test is to evaluate the relationship between the weight wear of friction pads and the quantities characterizing the braking process. The quantities characterizing the braking process included pad-to-disc contact area, friction pad thickness, pad-to-disc pressure, and braking speed. A regression model to estimate the friction pad wear on the basis of a single braking with the given input quantities was determined. The greatest influence on the increase in weight wear of friction pads has the braking velocity, which was confirmed by the value of the correlation coefficient of the regression model at value 0.81. The pressure of the friction pad to the disc and the friction pad thickness do not have a significant effect on the weight wear described by the regression model, and the obtained correlation coefficient for these parameters was lower than the value of 0.2.

The analysis of the reliability parameters of a technical object and the determination of the change in the reliability of the object over time, requires the knowledge of the functional characteristics and reliability parameters of the elements included in a system. On the basis of the failure data of the selected element of the object, in this case the vehicle, it is possible to determine the average working time to failure of the element and the appropriate form of distribution that characterizes the reliability and durability parameters of the tested element. The main purpose of the research presented in the article was to develop a method of assessing the reliability of an electronic component of a vehicle-a boot lid contactor. This paper also presents three possible methods of repairing the boot lid contactor (sealing the housing with adhesive with better way, replacing the element with a new one or the most time-consuming solution, changing the shape of the boot lid). The authors also decided to determine the reliability and cost parameters that will allow preventive replacement of this element. The tests were carried out on a fleet of 61 vehicles of the same model, but with different body structures. Contactor failures were reported in 41 cases, of which 29 were in the hatchback construction and 12 in the estate type. The analysis of the distribution selection for the tested part of the passenger car-the boot lid contactor-was performed using the Likelihood Value (LKV) test to determine the rank of distributions. Also the maximum likelihood (MLE) method was used to estimate the distribution parameters. The three-parameter Weibull distribution was the best-fitted distribution in both cases. It was clearly defined that one model of car with two different types of body have vastly different reliability characteristic. Based on the reliability characteristic and parameters, the appropriate preventive actions can be taken, minimizing the risk of damage, thus avoiding financial losses and guaranteeing an appropriate level of vehicle safety.

The article presents the results of friction and vibroacoustic tests of a railway disc brake carried out on a brake stand. The vibration signal generated by the friction linings provides information on their wear and offers evaluation of the braking process, i.e., changes in the average friction coefficient. The algorithm presents simple regression linear and non-linear models for the thickness of the friction linings and the average coefficient of friction based on the effective value of vibration acceleration. The vibration acceleration signals were analyzed in the amplitude and frequency domains. In both cases, satisfactory values of the dynamics of changes above 6 dB were obtained. In the case of spectral analysis using a mid-band filter, more accurate models of the friction lining thickness and the average coefficient of friction were obtained. However, the spectral analysis does not allow the estimation of the lining thickness and the friction coefficient at low braking speeds, i.e., 50 and 80 km/h. The analysis of amplitudes leads to the determination of models in the entire braking speed range from 50 to 200 km/h, despite the lower accuracy compared to the model, based on the spectral analysis. The vibroacoustic literature presents methods of diagnosis of the wear of various machine elements such as bearings or friction linings, based on amplitude or frequency analysis of vibrations. These signal analysis methods have their limitations with regard to their scope of use and the accuracy of diagnosis. There are no cases of simultaneous use of different methods of analysis. This article presents the simultaneous application of the amplitude and frequency methods in the analysis of vibroacoustic signals generated by brake linings. Moreover, algorithms for assessing the wear of friction linings and the average coefficient of friction were presented. The algorithm enables determination of the time at which the friction linings should be replaced with new ones. The final algorithm analyzes the vibration acceleration signals using both amplitude analysis for low braking speeds, as well as spectral analysis for medium and high braking speeds.

The article presents the state of knowledge and research in the field of surface cracks occurring in disc braking systems of rail and car vehicles. The craze formed during the operation of vehicles is particularly dangerous and leads to breaking the disc into several pieces. It may lead to a loss of braking force and damage to the entire disc brake caliper. The main aim of the research is to identify surface cracks in brake discs made of cast iron and use experimental methods to estimate their depth. Research were conducted on the disc braking system developed by the authors. In examining the location and depth of cracks, the penetration method, ultrasound, as well as a special probe were used. This device measures the crack depth based on the electrical resistance between two points on the surface of the metallic object. The tests showed that the first microcracks on the brake discs appeared after 309 braking tests on the test stand. In addition, it was observed that the surface cracks length of the disc increased linearly to depth until they reached about 11.5–12 mm with corresponded to crack lengths in the range of 65–70 mm. However, determination of the regression functions presented in the article allows to estimate the depth of surface cracks up to 70 mm long on cast iron brake discs by measuring their length.

The article presents the results of research on abrasive and tribocorrosion wear of boron steel. This type of steel is used in the automotive and agricultural industries for the production of tools working in soil. The main goal of the article is the evaluation of tribocorrosion and abrasive wear for hot-formed 22MnCrB5 steel and a comparison of the obtained results with test results for steel in a cold-formed state. The spinning bowl method to determine the wear of samples working in the abrasive mass was used. Furthermore, a stand developed based on the ball-on-plate system allows to determine the wear during the interaction of friction and corrosion. After the hot-forming process, 22MnCrB5 steel was three times more resistant for the abrasive wear than steel without this treatment. The average wear intensity for 22MnCrB5 untreated steel was 0.00046 g per km, while for 22MnCrB5 hot-formed steel it was 0.00014 g per km. The tribocorrosion tests show that the wear trace of hot-formed 22MnCrB5 steel was about 7.03 µm, and for cold-formed 22MnCrB5 steel a 12.11 µm trace was noticed. The hot-forming method allows to obtain the desired shape of the machine element and improves the anti-wear and anti-corrosion properties for boron steel.

This article presents the application of the ring-on-ring test to investigate some of the important factors affecting the abrasive and corrosion wear of a face seal used in the sugar industry. The test involves the sliding contact between two steel rings working in different conditions such as mechanic, abrasive, corrosive extortions and its combination. Rings were made of the C45 steel and the surface layers were modified by heat and thermochemical treatment such as normalizing, flame hardening, nitriding and chrome diffusion. Maximum wear of the sample after tests under mechanic, abrasive and corrosion extortion were obtained. For C45 steel without surface modification the biggest wear was obtained for mechanical, abrasive and corrosive extortion and equals 0.0138 g. This value was three times bigger than the result for the mechanical extortion and ten times than for the corrosive conditions. For individual research options the percentage increase or decrease in wear resistance in relation to the normalized surface layer was determined. In the corrosive extortion the highest increase (90%) of wear resistance was recorded for the chrome layer relative to normalizing sample. The main conclusion of the paper is that the wear effect caused by all factors—mechanical, abrasive and corrosive—is not a straight sum of values of wear.