The steel industry is an important engine for sustainable growth, added value, and high-quality employment within the European Union. It is committed to reducing its CO₂ emissions due to production by up to 50% by 2030 compared to 1990′s level by developing and upscaling the technologies required to contribute to European initiatives, such as the Circular Economy Action Plan (CEAP) and the European Green Deal (EGD). The Clean Steel Partnership (CSP, a public–private partnership), which is led by the European Steel Association (EUROFER) and the European Steel Technology Platform (ESTEP), defined technological CO₂ mitigation pathways comprising carbon direct avoidance (CDA), smart carbon usage SCU), and a circular economy (CE). CE approaches ensure competitiveness through increased resource efficiency and sustainability and consist of different issues, such as the valorization of steelmaking residues (dusts, slags, sludge) for internal recycling in the steelmaking process, enhanced steel recycling (scrap use), the use of secondary carbon carriers from non-steel sectors as a reducing agent and energy source in the steelmaking process chain, and CE business models (supply chain analyses). The current paper gives an overview of different technological CE approaches as obtained in a dedicated workshop called “Resi4Future—Residue valorization in iron and steel industry: sustainable solutions for a cleaner and more competitive future Europe” that was organized by ESTEP to focus on future challenges toward the final goal of industrial deployment.

Super Duplex Stainless Steels (SDSSs) are composed of α-ferrite and γ-austenite grains, the simultaneous presence of which forms an optimal microstructure to achieve the best combination of mechanical and corrosion resistance properties. Moreover, international quality standards are strict about the phase fraction ratio. The purpose of this work is the achievement of a better description of the phase ratio evolution taking place during annealing at 1080 °C in the super duplex stainless steels F53–S32750 and F55–S32760. The experimental results show a damped sinusoidal trend in the α/γ phase ratio evolution with the increase of the soaking time of thermal treatment. This can be described by coupling both the competitive coarsening growth regime and the concept of the local equilibrium phase transformations, pointing out a good correspondence with the experimental data. Further, recrystallization phenomena also play a major role. Finally, the additivity character of the observed processes has been proven.