The additive manufacturing of BaTiO₃ (BT) ceramics through stereolithography (SLA) 3D printing at 465 nm wavelength was demonstrated. After different milling times, different paste compositions with varied initial micron-sized powders were studied to find a composition suitable for 3D printing. The pastes were evaluated in terms of photopolymerization depth depending on the laser scanning speed. Furthermore, the microstructure and properties of the BT ceramic samples produced through SLA 3D printing were characterized and compared with those of ceramics fabricated through a conventional die semi-drying pressing method. Three-dimensional printed samples achieved relative densities over 0.95 and microhardness over 500 HV after sintering, nearly matching the relative density and microhardness attained by the pressed samples. Upon poling, the 3D-printed samples attained acceptable piezoelectric module d₃₃ = 148 pC/N and dielectric constants over 2000. At near full density, BT piezoceramics were successfully fabricated through SLA 3D printing at 465 nm wavelength, achieving photopolymerization depth of more than 100 microns. This work paves the relatively low-cost way for 3D printing of piezoelectric ceramics using conventional micron-sized powders and high printed layer thickness.

Additive manufacturing is a modern technique to produce parts with a complex geometry. However, the choice of the printing parameters is a time-consuming and costly process. In this study, the parameter optimization for the laser powder bed fusion process was investigated. Using state-of-the art multi-objective Bayesian optimization, the set of the most-promising process parameters (laser power, scanning speed, hatch distance, etc.), which would yield parts with the desired hardness and porosity, was established. The Gaussian process surrogate model was built on 57 empirical data points, and through efficient sampling in the design space, we were able to obtain three points in the Pareto front in just over six iterations. The produced parts had a hardness ranging from 224–235 HV and a porosity in the range of 0.2–0.37%. The trained model recommended using the following parameters for high-quality parts: 58 W, 257 mm/s, 45 µm, with a scan rotation angle of 131 degrees. The proposed methodology greatly reduces the number of experiments, thus saving time and resources. The candidate process parameters prescribed by the model were experimentally validated and tested.

The superimposed magnetic field affects the microstructure and mechanical properties of additively manufactured metal parts. In this work, the samples were fabricated from Inconel 718 superalloy by directed energy deposition under a 0.2 T static field. The magnetohydrodynamic 1D model is proposed for the estimation of a fluid flow inside a molten pool. According to the theoretical predictions, the fluid flow is slightly decreased by an applied field. The estimated thermoelectric magnetic convection in the mushy zone is shown to be negligible to change in subgrain size, but enough to reduce the hard-to-dissolve Nb-rich phase, thereby improving the average ultimate elongation from 23% to 27%. The obtained results confirm that an external static magnetic field can modify and enhance the mechanical properties of additively manufactured materials.

A piezoceramic BaTiO₃ material that is difficult for 3D printing was tested with a homemade laser-based stereolithography (SLA) setup. The high light absorbance of BaTiO₃ in the spectral range of 350–410 nm makes this material hardly usable with most commercial SLA 3D printers. The typical polymerization depth of BaTiO₃ ceramic pastes in this spectral range hardly reaches 30–50 µm for 40 vol % powder loading. A spectral change to 465 nm was realized in this work via a robot-based experimental SLA setup to improve the 3D printing efficiency. The ceramic paste was prepared from a preconditioned commercial BaTiO₃ powder and used for 3D printing. The paste’s polymerization was investigated with variation of powder fraction (10–55 vol %), speed of a laser beam (1–10 mm/s, at constant laser power), and a hatching spacing (100–1000 µm). The polymerization depths of over 100 µm were routinely reached with the 465 nm SLA for pastes having 55 vol % powder loading. The spectral shift from 350–410 nm spectral region to 465 nm reduced the light absorption by BaTiO₃ and remedied the photopolymerization process, emphasizing the importance of comprehensive optical analysis of prospective powders in SLA technology. Two multi-layered objects were 3D-printed to demonstrate the positive effect of the spectral shift.