Masonry units made of clay or Autoclaved Aerated Concrete (AAC) are widely used in constructions from Romania and other countries. Masonry units with superior mechanical and thermal characteristics can improve the energy efficiency of buildings, especially when they are used as the main solutions for building envelope construction. Their production in recent years has increased vertiginously to meet the increased demand. Manufactured with diversified geometries, different mechanical and/or thermal characteristics have a high volume in the mass of the building and a major influence in their carbon footprint. Starting from the current context regarding the target imposed by the long-term strategy of built environment decarbonization, the aim of the paper is to analyze the potential of reusing mining waste in the production of masonry units. Mining waste represents the highest share of waste generated at national level and may represent a valuable resource for the construction industry, facilitating the creation of new jobs and support for economic development. This review presents the interest in integrating mining wastes in masonry unit production and the technical characteristics of the masonry units in which they have been used as raw materials in different percentages. Critical assessment framework using SWOT analysis highlights the key sustainability aspects (technical, environmental, social, economic) providing a comprehensive and systematic analysis of the advantages and disadvantages regarding the integration of mining waste as secondary raw materials into masonry units production.

The urgent need for sustainable construction that corresponds to the three pillars of sustainable development is obvious and continuously requires innovative solutions. Cementitious composites with TiO₂ nanoparticles (NT) addition show potential due to their improved durability, physico–mechanical characteristics, and self-cleaning capacity. This study aimed to evaluate the influence of NT on cementitious composites by comparing those with 2%–5% nanoparticles with a similar control sample without nanoparticles, as well as an analysis of cost growth. The experimental results showed an increase in bulk density of the material (4.7%–7.4%), reduction in large pore sizes by min. 12.5%, together with an increase in cumulative volume and cumulative specific surface area of small pore sizes, indicating densification of the material, also supported by SEM, EDS, and XRD analyses indicating acceleration of cement hydration processes with formation of specific products. The changes at microstructural level support the experimental results obtained at macrostructural level, i.e., modest but existent increases in flexural strength (0.6%–7.9%) and compressive strength (0.2%–2.6%) or more significant improvements in abrasion resistance (8.2%–58%) and reduction in water absorption coefficient (37.5%–81.3%). Following the cost–benefit analysis, it was concluded that, for the example case considered of a pedestrian pavement with a surface area of 100 m², using 100 mm thick slabs, if these slabs were to be made with two layers, the lower layer made of cementitious composite as a reference and the upper layer with a thickness of 10 mm made of cementitious composite with 3% NT or 4% NT, the increase in cost would be acceptable, representing less than 15% compared to the cost for the exclusive use of cementitious composite without NT.

The present work examines an innovative manufacturing technique for fired clay bricks, using tuff as a secondary raw material. Samples were made of clay and tuff (0–30 wt.%) fired at 900 to 1100 °C. The chemical and mineralogical compositions and physical and thermal analyses of raw materials were investigated by using SEM-EDS, RX and DTA-TG curves. The samples were analysed from the mineralogical, technological and mechanical points of view. The result show that the tuff’s presence in the clay mixtures considerably reduced the shrinkage of the product during the firing process, and the manufactured samples were of excellent quality. The compressive strength of the bricks varied from 5–35.3MPa, being influenced by the tuff content, clay matrix properties and firing temperatures. Finally, the heat demand for increasing the temperature from room to the firing temperature of the sample with 10% tuff content was 22%.

This study investigates the effect of adding different size fractions of the same pore forming agent (sawdust) on the material’s compressive strength and heat transfer. The samples were dry pressed and fired at high temperature inside an oven. Phase transformations were evidenced by a combination of differential thermal analysis, thermogravimetry and mass spectrometry (DTA-TGA-MS) and X-ray diffraction (XRD) techniques, in the temperature range of 24-900 ºC. Image analysis (IA) and compression tests were performed to explain the mechanical behaviour of the samples. The thermal conductivity was obtained by using combined photopyroelectric calorimetry (PPE) and lock-in thermography (LIT) techniques. The pressing direction has an impact on the distribution of pores and the heat transfer by conduction.