The demand of lattice structures for medical applications is increasing due to their ability to accelerate the osseointegration process, to reduce the implant weight and the stiffness. Selective laser melting (SLM) process offers the possibility to manufacture directly complex lattice applications, but there are a few studies that have focused on biocompatible Ti6Al7Nb alloy. The purpose of this work was to investigate the physical–mechanical properties and the microstructure of three dissimilar lattice structures that were SLM-manufactured by using Ti6Al7Nb powder. In particular, the strut morphology, the fracture characterization, the metallographic structure, and the X-ray phase identification were analyzed. Additionally, the Gibson-Ashby prediction model was adapted for each lattice topology, indicating the theoretical compressive strength and Young modulus. The resulted porosity of these lattice structures was approximately 56%, and the pore size ranged from 0.40 to 0.91 mm. Under quasi-static compression test, three failure modes were recorded. Compared to fully solid specimens, the actual lattice structures reduce the elastic modulus from 104 to 6–28 GPa. The struts surfaces were covered by a large amount of partial melted grains. Some solidification defects were recorded in struts structure. The fractographs revealed a brittle rupture of struts, and their microstructure was mainly α’ martensite with columnar grains. The results demonstrate the suitability of manufacturing lattice structures made of Ti6Al7Nb powder having unique physical–mechanical properties which could meet the medical requirements.

To manufacture custom medical parts or scaffolds with reduced defects and high mechanical characteristics, new research on optimizing the selective laser melting (SLM) parameters are needed. In this work, a biocompatible powder, 316L stainless steel, is characterized to understand the particle size, distribution, shape and flowability. Examination revealed that the 316L particles are smooth, nearly spherical, their mean diameter is 39.09 μm and just 10% of them hold a diameter less than 21.18 μm. SLM parameters under consideration include laser power up to 200 W, 250–1500 mm/s scanning speed, 80 μm hatch spacing, 35 μm layer thickness and a preheated platform. The effect of these on processability is evaluated. More than 100 samples are SLM-manufactured with different process parameters. The tensile results show that is possible to raise the ultimate tensile strength up to 840 MPa, adapting the SLM parameters for a stable processability, avoiding the technological defects caused by residual stress. Correlating with other recent studies on SLM technology, the tensile strength is 20% improved. To validate the SLM parameters and conditions established, complex bioengineering applications such as dental bridges and macro-porous grafts are SLM-processed, demonstrating the potential to manufacture medical products with increased mechanical resistance made of 316L.

This study introduces an artificial neural network (ANN) model for optimizing process parameters to reduce the chances of delamination in carbon fiber-reinforced polymer (CFRP) materials during abrasive water jet (AWJ) piercing. AWJ is a proper method for cutting CFRP. The initial step in this process is AWJ piercing, which creates entry holes in the material to facilitate further cutting operations. However, AWJ piercing is particularly challenging due to the high energy applied to the material. If it is not properly controlled, this high-energy impact can cause material delamination. Avoiding CFRP delamination is a critical aspect when expensive parts are processed with AWJ, particularly in the aerospace and automotive industries. This can compromise the CFRP workpiece, and this induces extra costs for rework. The ANN model was trained using backpropagation to predict delamination. It features a feed-forward architecture that balances model complexity and performance. Validation showed that the ANN model effectively predicted optimal process parameters, eliminating delamination in machined CFRP parts. This study underscores the potential of ANNs in enhancing AWJ piercing processes and provides a robust and reliable method of improving the quality of CFRP parts.

Traditional vulcanization mold manufacturing is complex, costly, and under pressure due to shorter product lifecycles and diverse variations. Additive manufacturing using Fused Filament Fabrication and high-performance polymers like PEEK offer a promising future in this industry. This study assesses the compressive strength of various infill structures (honeycomb, grid, triangle, cubic, and gyroid) when considering two distinct build directions (Z, XY) to enhance PEEK’s economic and resource efficiency in rapid tooling. A comparison with PETG samples shows the behavior of the infill strategies. Additionally, a proof of concept illustrates the application of a PEEK mold in vulcanization. A peak compressive strength of 135.6 MPa was attained in specimens that were 100% solid and subjected to thermal post-treatment. This corresponds to a 20% strength improvement in the Z direction. In terms of time and mechanical properties, the anisotropic grid and isotropic cubic infill have emerged for use in rapid tooling. Furthermore, the study highlights that reducing the layer thickness from 0.15 mm to 0.1 mm can result in a 15% strength increase. The study unveils the successful utilization of a room-temperature FFF-printed PEEK mold in vulcanization injection molding. The parameters and infill strategies identified in this research enable the resource-efficient FFF printing of PEEK without compromising its strength properties. Using PEEK in rapid tooling allows a cost reduction of up to 70% in tool production.

This paper presents a new method of process parameter optimization, adequate for 3D printing of PLA (Polylactic Acid) components. The authors developed a new piece of Hybrid Manufacturing Equipment (HME), suitable for producing complex parts made from a biodegradable thermoplastic polymer, to promote environmental sustainability. Our new HME equipment produces PLA parts by both additive and subtractive techniques, with the aim of obtaining accurate PLA components with good surface quality. A design of experiments has been applied for optimization purposes. The following manufacturing parameters were analyzed: rotation of the spindle, cutting depth, feed rate, layer thickness, nozzle speed, and surface roughness. Linear regression models and neural network models were developed to improve and predict the surface roughness of the manufactured parts. A new test part was designed and manufactured from PLA to validate the new mathematical models, which can now be applied for producing complex parts made from polymer materials. The neural network modeling (NNM) allowed us to obtain much better precision in predicting the final surface roughness ($R_a$), as compared to the conventional linear regression models (LNM). Based on these modelling methods, the authors developed a practical methodology to optimize the process parameters in order to improve the surface quality of the 3D-printed components and to predict the actual roughness values. The main advantages of the results proposed for hybrid manufacturing using polymer materials like PLA are the optimized process parameters for both 3D printing and milling. A case study has been undertaken by the authors, who designed a specific test part for their new hybrid manufacturing equipment (HME), in order to test the new methodology of optimizing the process parameters, to validate the capability of the new HME. At the same time, this new methodology could be replicated by other researchers and is useful as a guideline on how to optimize the process parameters for newly developed equipment. The innovative approach holds potential for widespread equipment functionality enhancement among other users.

This paper introduces an Acoustic Emission (AE)-based monitoring method designed for supervising the Abrasive Waterjet Cutting (AWJC) process, with a specific focus on the precision cutting of Carbon Fiber-Reinforced Polymer (CFRP). In industries dealing with complex CFRP components, like the aerospace, automotive, or medical sectors, preventing cutting system malfunctions is very important. This proposed monitoring method addresses issues such as reductions or interruptions in the abrasive flow rate, the clogging of the cutting head with abrasive particles, the wear of cutting system components, and drops in the water pressure. Mathematical regression models were developed to predict the root mean square of the AE signal. The signal characteristics are determined, considering key cutting parameters like the water pressure, abrasive mass flow rate, feed rate, and material thickness. Monitoring is conducted at both the cutting head and on the CFRP workpiece. The efficacy of the proposed monitoring method was validated through experimental tests, confirming its utility in maintaining precision and operational integrity in AWJC processes applied to CFRP materials. Integrating the proposed monitoring technique within the framework of digitalization and Industry 4.0/5.0 establishes the basis for advanced technologies such as Sensor Integration, Data Analytics and AI, Digital Twin Technology, Cloud and Edge Computing, MES and ERP Integration, and Human-Machine Interface. This integration enhances operational efficiency, quality control, and predictive maintenance in the AWJC process.