Corrosion inhibition of mild steel in hydrochloric acid solutions using electropolymerized Poly 2-aminobenzothiazole, P(2ABT), was evaluated using weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy measurements at different temperature. Results showed that the inhibition efficiency increases with increasing the concentration of P(2ABT) up to 12.7 × 10⁻⁶ mol L⁻¹ and decreases with raising the temperature. Polarization curves indicate that the studied compound acts as anodic inhibitor. Thermodynamic activation parameters for both dissolution and adsorption processes are calculated and discussed as well as the adsorption isotherms are calculated. Gibbs free energy value confirms the physical nature of the adsorption, also the mechanism of inhibition is discussed. Scanning electron microscopy is used to study the surface morphology of mild steel in hydrochloric acid solution in the absence and presence of 12.7 × 10⁻⁶ mol L⁻¹ P(2ABT). Data obtained from all techniques are in a good agreement with each other.

This investigation presents the influence of various types of nanoparticles on the performance of ultra high performance concrete (UHPC). Three nanoparticles from waste materials include nano-crushed glass, nano-metakaolin, nano-rice husk ash were prepared using the milling technique. In addition, nano-silica prepared using chemical method at the laboratory is implemented to compare the performance. Several UHPC mixes incorporating different dosages of nanoparticles up to 5% are prepared and tested. Mechanical properties, durability as well as the microstructure of UHPC mixes have been evaluated in order to study the influence of nanoparticles on the hardened characteristics of UHPC. The experimental results showed that early strength is increased by the incorporation of nanomaterials, as compared to the reference UHPC mix. The incorporation of 3% nano-rice husk ash produced the highest compressive strength at 91 day. Microstructural measurements using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDX), and Thermogravimetric Analysis (TGA) confirm the role of nanomaterials in densifying the microstructure, reducing calcium hydroxide content as well as producing more C-S-H, which improves the strength and reduces the absorption of UHPC. Nanoparticles prepared from waste materials by the milling technique are comparable to chemically prepared nanosilica in improving mechanical properties, refining the microstructure and reducing the absorption of UHPC.

Corrosion resistance of high strength steel (HHS) embedded in ultra-high performance concrete (UHPC) immersed in 3.5% NaCl solution is evaluated in the absence and presence of nano silica (NS), nano glass waste (NGW), nano rice husk ash (NRHA) and nano metakaolin (NMK) using open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) under normal and accelerated conditions. Data showed that the corrosion rate in the accelerated conditions is higher compared by the normal conditions due to the increasing in the rate of both anodic and cathodic reactions in the presence of anodic current. On the other hand, the presence of the studied nano materials decreases both the anodic and cathodic overpotentials, and shifts both the open circuit potential (E_ocp) and corrosion potential (E_corr) of HSS to more noble values, as well as decreases the values of the corrosion current densities (I_corr) in both normal and accelerated conditions. Furthermore, EIS analysis illustrates that the presence of these materials enhances both the concrete bulk resistance and the charge transfer resistance at HSS/UHPC interface, which retards the flow of the electrons between the anodic and cathodic sites, thus impeding the propagation of the corrosion process. The inhibitory effect of the studied nano materials for the corrosion of HSS is interpreted on the basis of the change in the microstructure and the compressive strength of the UHPC.