This research investigates the effects of steel (ST) and synthetic (SYN) fibers on the workability and mechanical properties of HPFRC. It also analyzes their influence on the material’s microstructural characteristics. ST fibers improve tensile strength, fracture toughness, and post-cracking performance owing to their rigidity, mechanical interlocking, and robust adhesion with the matrix. SYN fibers, conversely, mitigate shrinkage-induced micro-cracking, augment ductility, and enhance concrete performance under dynamic stress while exerting negative effects on workability. Hybrid fiber systems, which include ST and SYN fibers, offer synergistic advantages by enhancing fracture management at various scales and augmenting ductility and energy absorption capability. Scanning electron microscopy (SEM) has been crucial in investigating fiber–matrix interactions, elucidating the effects of ST and SYN fibers on hydration, crack-bridging mechanisms, and interfacial bonding. ST fibers establish thick interfacial zones that facilitate effective stress transfer, whereas SYN fibers reduce micro-crack formation and enhance long-term durability. Nonetheless, research deficiencies persist, encompassing optimal hybrid fiber configurations, the enduring performance of fiber-reinforced concrete (FRC), and sustainable fiber substitutes. Future investigations should examine multi-scale reinforcing techniques, intelligent fibers for structural health assessment, and sustainable fiber alternatives. The standardization of testing methodologies and cost–benefit analyses is essential to promote industrial deployment. This review offers a thorough synthesis of the existing knowledge, emphasizing advancements and potential to enhance HPFRC for high-performance and sustainable construction applications. The findings facilitate the development of new, durable, and resilient fiber-reinforced concrete systems by solving current difficulties.

This investigation presents the influence of various types of nanoparticles on the performance of ultra high performance concrete (UHPC). Three nanoparticles from waste materials include nano-crushed glass, nano-metakaolin, nano-rice husk ash were prepared using the milling technique. In addition, nano-silica prepared using chemical method at the laboratory is implemented to compare the performance. Several UHPC mixes incorporating different dosages of nanoparticles up to 5% are prepared and tested. Mechanical properties, durability as well as the microstructure of UHPC mixes have been evaluated in order to study the influence of nanoparticles on the hardened characteristics of UHPC. The experimental results showed that early strength is increased by the incorporation of nanomaterials, as compared to the reference UHPC mix. The incorporation of 3% nano-rice husk ash produced the highest compressive strength at 91 day. Microstructural measurements using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDX), and Thermogravimetric Analysis (TGA) confirm the role of nanomaterials in densifying the microstructure, reducing calcium hydroxide content as well as producing more C-S-H, which improves the strength and reduces the absorption of UHPC. Nanoparticles prepared from waste materials by the milling technique are comparable to chemically prepared nanosilica in improving mechanical properties, refining the microstructure and reducing the absorption of UHPC.

This research investigates the simultaneous impact of two different types of steel fibers, nanometakaolin, and nanosilica on the mechanical properties of geopolymer concrete (GPC) mixes. To achieve this aim, different geopolymer concrete mixes were prepared. Firstly, with and without nanomaterials (nanosilica and nanometakaolin) of 0, 2%, 4%, 6%, and 8% from ground granulated blast furnace slag (GGBFS) were used. Secondly, steel fiber (hooked end and crimped) content of (0, 0.5%, 1, and 1.5%) was used. Thirdly, optimum values of nanomaterials with the optimum values of steel fiber were used. Crimped and hooked‐end steel fibers were utilized with an aspect ratio of 60 and a length of 30 mm. Geopolymer mixes were manufactured by using a constant percentage of alkaline activator to binder proportion equal to 0.45 with GGBFS cured at ambient conditions. For alkaline activator, sodium hydroxide molar (NaOH) and sodium hydroxide solution (NaOH) were used according to a proportion (Na₂SiO₃/NaOH) of 2.33. The hardened concrete tests were performed through the usage of splitting tensile strength, flexural, and compressive experiments to determine the impact of steel fibers, nanometakaolin, and nanosilica individually and combined on performance of GPC specimens. The results illustrated that using a mix composed of the optimum steel fibers (1% content) accompanied by an optimum percentage of 6% nanometakaolin or 4% nanosilica demonstrated a significant enhancement in the mechanical properties of GPC specimens compared to all other mixtures. Besides, the impact of using nanomaterials individually was found to be predominant on compressive strength on GPC specimens especially with the usage of the optimum values. However, using nanomaterials individually compared to using the steel fibers individually was found to have approximately the same splitting tensile strength and flexural performance.

Integrating class-C and class-F fly ash (FA) as supplementary cementitious materials (SCMs) in concrete offers a promising pathway for sustainable construction practices. This study explores the pivotal role of FA in reducing carbon dioxide (CO₂) emissions and improving concrete’s durability and mechanical properties through a comprehensive life cycle analysis (LCA). By blending FA with cement, significant reductions in CO₂ emissions are achieved, alongside enhancements in the workability, compressive strength, and permeability resistance of the concrete matrix. This research elucidates the pozzolanic reaction between FA and calcium hydroxide (CH) during cement hydration, highlighting its contribution to concrete strength and durability. Through a range of comprehensive analysis techniques, including mechanical testing and environmental impact assessment, this study demonstrates the substantial benefits of prioritizing the utilization of class-C and class-F FA in sustainable construction. The findings underscore the industry’s commitment to environmentally conscious practices, promoting structural integrity and reducing ecological impacts. Overall, this research emphasizes class-C and class-F FA as critical components in achieving sustainable construction goals and advancing towards a more environmentally responsible built environment.