The interaction of water and air i.e. moisture regain, water vapor transmission, wicking and air permeability with woven textiles are tested to investigate the comfort of woven fabrics made of nylon, cotton, and cotton–nylon mixtures with different yarn counts. The fabrics porosity (based on equation 1 and 2), woven fabric sett (ASTM D3775-03), fabric thickness (ASTM D1777-96), fabric weight (ASTM D3776M - 20), fabric vapour transmission (ASTM E96-00), transfer wicking, and longitudinal wicking (DIN 53924), moisture regain (ASTM D2495-07), and air permeability (ASTM D737) were examined for investigations based on the standards in the brackets. The experimental results showed that fabric transfer wicking, longitudinal wicking, moisture regain and air permeability properties increase as the yarn goes to coarser for all woven fabric samples but the water vapor transmission property decrease. Additionally, fabric transfer and longitudinal wicking capabilities improved with increased nylon fiber blend ratios within fiber conformation. However, the nylon fiber composition has negative impact on air permeability, water vapor transfer rate, wicking and moisture capabilities of the woven fabrics. Generally, it can be concluded that the existence of nylon fiber, and yarn count coarseness improved wicking properties of the woven fabrics and decreased the air permeability property of woven fabrics.

Flexible supercapacitors are highly demanding due to their wearability, washability, lightweight property and rollability. In this paper, a comprehensive review on flexible supercapacitors based on conductive polymers such as polypyrrole (PPy), polyaniline (PANI) and poly(3,4-ethylenedioxtthiophne)-polystyrene sulfonate (PEDOT:PSS). Methods of enhancing the conductivity of PEDOT:PSS polymer using various composites and chemical solutions have been reviewed in detail. Furthermore, supercapacitors based on carbonized banana peels and methods of activation have been discussed in point. This review covers the up-to-date progress achieved in conductive polymer-based materials for supercapacitor electrodes. The effect of various composites with PEDOT:PSS have been discussed. The review result indicated that flexible, stretchable, lightweight, washable, and disposable wearable electronics based on banana peel and conductive polymers are highly demanding.

The use of hydrogel in tissue engineering is not entirely new. In the last six decades, researchers have used hydrogel to develop artificial organs and tissue for the diagnosis of real-life problems and research purposes. Trial and error dominated the first forty years of tissue generation. Nowadays, biomaterials research is constantly progressing in the direction of new materials with expanded capabilities to better meet the current needs. Knowing the biological phenomenon at the interaction among materials and the human body has promoted the development of smart bio-inert and bio-active polymeric materials or devices as a result of vigorous and consistent research. Hydrogels can be tailored to contain properties such as softness, porosity, adequate strength, biodegradability, and a suitable surface for adhesion; they are ideal for use as a scaffold to provide support for cellular attachment and control tissue shapes. Perhaps electrical conductivity in hydrogel polymers promotes the interaction of electrical signals among artificial neurons and simulates the physiological microenvironment of electro-active tissues. This paper presents a review of the current state-of-the-art related to the complete process of conductive hydrogel manufacturing for tissue engineering from cellulosic materials. The essential properties required by hydrogel for electro-active-tissue regeneration are explored after a short overview of hydrogel classification and manufacturing methods. To prepare hydrogel from cellulose, the base material, cellulose, is first synthesized from plant fibers or generated from bacteria, fungi, or animals. The natural chemistry of cellulose and its derivatives in the fabrication of hydrogels is briefly discussed. Thereafter, the current scenario and latest developments of cellulose-based conductive hydrogels for tissue engineering are reviewed with an illustration from the literature. Finally, the pro and cons of conductive hydrogels for tissue engineering are indicated.

Skin wound management is a very difficult undertaking in the medical field. There is no information available concerning the wound beneath the bandages. Electrospun nanofibrous wound dressings stand out for their resemblance to extracellular matrix (ECM), increased surface-to-volume ratio, porousness, and capacity to encapsulate or load medications, among other distinctive qualities. Traditional antibacterial loaded electrospun nanofibrous wound dressings do not indicate the state of the wound and constantly release antibacterial chemicals even when there are no bacteria in the wound area. As a result, dressings that can track the condition of the wound and dispense medications as needed are crucial. Self-responsive wound dressings can release medications based on bacterial, oxygen spectra, pH, or infection responsiveness, reducing the need for antibacterial agents. Self-responsive mats, which are wound dressings that can release medications based on response to bacteria, oxygen species, and pH or infections, are required to reduce the overuse of antibacterial agents. Self-responsive electrospun nanofibrous mats can be used to monitor the condition of a wound by altering its color in response to an infection or a change in the pH of the wound. Electrospun nanofibrous wound dressings that are stimulus-responsive (self-responsive) are discussed in this review paper. Self-responsive electrospun nanofibrous wound dressings that are triggered by pH, temperature, light, bacteria, and oxygen species are discussed in detail after self-responsive smart materials or polymers used for electrospun nanofibrous wound dressings are covered in the first section of the review.

Treating wound is challenging if there is microbial colonization. In this paper, we tried to review comparison of bacterial inhibition zone of different herbal plant bioactive loaded polymer electrospun nanofibrous wound dressings. A systematic literature search called preferred reporting items for systematic reviews and meta-analyses (PRISMA) was used to review bacterial inhibition zone of the different herbal plant bioactive loaded polymer electrospun nanofibrous mats used for wound dressing applications. The literatures were searched from PubMed, Scopus, Web of Science, and Google Scholar databases published in English from 2010 to 2021. Two hundred articles were searched out; from these, 93 articles are selected and studied their bacterial inhibition zone, among them eight have the highest bacterial inhibition zone greater than or equal to 20 mm. From the studied plant bioactive extract loaded polymer electrospun nanofibrous mat wound dressings, PVA/ Tridax procumbensviz have the highest antibacterial property (42 mm and 35 mm bacterial inhibition zone to Staphylococcus aureus and Escherichia coli, respectively). The second highest antibacterial property is PVA /honey/Curcuma longa with bacterial inhibition zone of 38 mm to S. aureus and the third one is PCL/carboxyethyl chitosan/PVA/ Matricaria chamomile L. with an inhibition zone of 37.5 mm to E. coli bacteria.

The tensile properties such as tensile strength which is measured as breaking force in Newton (N) and elongation percent (%) at break of single jersey and 1×1 rib (knitted with full needles) knitted fabrics made from 100% cotton and cotton/Lycra yarns (5% Lycra yarn content in 95% combed cotton yarn) are investigated in this research. The sample fabrics are conditioned for 24 hours at20±1°C temperature and65±2% relative humidity before testing. Ten specimens (five for lengthwise and five for widthwise) have been taken from each of the two knitted structures, those made from 100% cotton and cotton/Lycra (at 95/5 percent ratio blend) yarns. According to the discussion and as found from the investigations, the tensile properties of single jersey and 1×1 rib knitted fabrics made from 100% cotton and cotton/Lycra yarns are significantly different from each other and both of the knitted fabrics have high elongation percent at break with cotton/Lycra blend yarns as compared to 100% cotton yarn. Knitted fabrics made from cotton/Lycra blended yarn have low breaking force and high elongation percent at break relative to knitted fabrics made from 100% cotton yarns.