This study aims to establish the effects of equal channel angular pressing (ECAP) processing on the corrosion behavior and hardness values of the AZ31 Mg alloy. The AZ31 billets were processed through ECAP successfully at 250 °C and their microstructural evolution was studied using optical and field emission scanning electron microscopy. The corrosion resistance of the AZ31 alloy was studied before and after processing through ECAP. The homogeneity of the hardness distribution was studied using both sections cut parallel and perpendicular to the extrusion direction. ECAP processing resulted in highly deformed central regions with elongated grains aligned parallel to the extrusion direction, whereas the peripheral regions showed an ultra-fine-grain recrystallized structure. After processing, small ultra-fine secondary particles were found to be homogeneously dispersed alongside the grain boundaries of the α-Mg matrix. Regarding the corrosion properties, measurements showed that ECAP processing through 1-P and 2-Bc resulted in decreasing their corrosion rate to 67.7% and 78.3%, respectively, of their as-annealed counterpart’s. The corrosion resistance of the ECAPed Mg alloy increased with the number of processing passes. This was due to the refinement of the grain size of the α-Mg matrix and secondary phases till ultra-fine size, caused by the accumulation of strain during processing. On the other hand, ECAP processing through 2-Bc resulted in increasing the Vickers hardness values by 132% and 71.8% at the peripheral and central areas, respectively, compared to the as-annealed counterpart.

The current study presents a detailed investigation for the equal channel angular pressing of pure copper through two regimes. The first was equal channel angular pressing (ECAP) processing at room temperature and the second was ECAP processing at 200 °C for up to 4-passes of route Bc. The grain structure and texture was investigated using electron back scattering diffraction (EBSD) across the whole sample cross-section and also the hardness and the tensile properties. The microstructure obtained after 1-pass at room temperature revealed finer equiaxed grains of about 3.89 µm down to submicrons with a high density of twin compared to the starting material. Additionally, a notable increase in the low angle grain boundaries (LAGBs) density was observed. This microstructure was found to be homogenous through the sample cross section. Further straining up to 2-passes showed a significant reduction of the average grain size to 2.97 µm with observable heterogeneous distribution of grains size. On the other hand, increasing the strain up to 4-passes enhanced the homogeneity of grain size distribution. The texture after 4-passes resembled the simple shear texture with about 7 times random. Conducting the ECAP processing at 200 °C resulted in a severely deformed microstructure with the highest fraction of submicron grains and high density of substructures was also observed. ECAP processing through 4-passes at room temperature experienced a significant increase in both hardness and tensile strength up to 180% and 124%, respectively.

Magnesium (Mg) alloys have unique properties. However, their applications are limited in working environments due to their poor corrosion resistance. Plasma electrolytic oxidation (PEO) is one of the most environmentally friendly and cost-effective ways that has been promoted to treat Mg alloys. In this study, we investigated the effect of electrical parameters on the microstructure, as well as the mechanical and corrosion resistance of AM60 alloy coated with PEO. The electrical parameters studied were current mode (unipolar and bipolar), frequency and duty ratio. The microstructure evolution of the coated AM60 substrates was studied using X-ray diffraction and scanning electron microscopy. Subsequently, the mechanical properties were determined using compression tests and microhardness measurements. The potentiodynamic polarization curves indicated that the PEO-coated samples experienced a significant decrease of 99.9% in the corrosion rate compared to the base metal. The electrochemical impedance spectroscopy findings showed that PEO coating increased the corrosion resistance of the AM60 magnesium alloy by 1071870% compared to the base metal. On the other hand, the PEO coated samples showed superior adhesion to the substrate. Moreover, the PEO coating led to an improvement in the hardness value by 114% compared to base metal, coupled with insignificant change in the compressive properties.

Magnesium-Zinc-Zirconium (Mg-Zn-Zr) alloys have caught considerable attention in medical applications where biodegradability is critical. The combination of their good biocompatibility, improved strength, and low cytotoxicity makes them great candidates for medical implants. This research investigation is focused on providing further insight into the effects of equal channel angular processing (ECAP) on the corrosion behavior, microstructure evolution, and mechanical properties of a biodegradable ZK30 alloy. Billets of Mg-3Zn-0.6 Zr (ZK30) alloy were processed through ECAP up to 4 passes of route Bc (rotating the billets 90° in the same direction between the subsequent passes) at 250 °C. Electron back-scatter diffraction (EBSD) was utilized to investigate the microstructural evolution as well as the crystallographic texture. Several electrochemical measurements were carried out on both a simulated body fluid and a 3.5% sodium chloride (NaCl) solution. Mechanical properties such as Vicker’s hardness and tensile properties were also assessed. The as-annealed (AA) microstructure was dominated by equiaxed coarse recrystallized grains with an average grain size of 26.69 µm. After processing, a geometric grain subdivision took place due to the severe plastic deformation. Processed samples were characterized by grain refinement and high density of substructures. The 4-passes sample experienced a reduction in the grain size by 92.8% compared with its AA counterpart. The fraction of high-angle grain boundaries increased significantly after 4-passes compared to the 1-pass processed sample. With regards to the crystallographic texture, the AA condition had its {0001} basal planes mostly oriented parallel to the transversal direction. On the other hand, ECAP processing resulted in crystallographic texture changes, such as the shifting of the ZK30 shear plane to be aligned at 45° relative to the extrusion direction (ED). Furthermore, the maximum texture intensity was reduced from 14 times random (AA billets) to 8 times random after ECAP processing through 4-passes. The corrosion rate of the 4-passes sample was tremendously reduced by 99% and 45.25% compared with its AA counterpart in the simulated body fluid and the NaCl solution, respectively. The pitting corrosion resistance of ZK30 showed notable improvements in the simulated body fluid by 471.66% and 352% during processing through 1-pass and 4-passes, respectively, compared with the 3.5% NaCl findings. Finally, significant improvements in the tensile strength, hardness, and ductility were also achieved.

In this study, billets of the ZK30 (Mg-3Zn-0.6 Zr-0.4 Mn, wt%) alloy were Equal Channel Angle Pressing (ECAP) processed for up to four passes of routes Bc (with rotating the sample 90° in the same direction between the subsequent passes), A (without sample rotation), and C (with sample rotating 180°) after each pass at a temperature of 250 °C and a ram speed of 10 mm/min using a die with an internal channel angle of 90°. The microstructural evolution and the crystallographic texture were investigated using a Scanning Electron Microscope (SEM) equipped with the Electron Back-Scatter Diffraction (EBSD) technique. Corrosion measurements were conducted in ringer lactate which is a simulated body fluid. The Vickers microhardness test and tensile tests were conducted for the alloy before and after processing. The as-annealed billets exhibited a bimodal structure as fine grains (more than 3.39 µm) coexisted with almost-equiaxed coarse grains (less than 76.73 µm); the average grain size was 26.69 µm. Further processing until four passes resulted in enhanced grain refinement and full Dynamic Recrystallization (DRX). ECAP processing through 4-Bc, 4-A, and 4-C exhibited significant reductions in grain size until they reached 1.94 µm, 2.89 µm, and 2.25 µm, respectively. Four-pass processing also resulted in the transformation of low-angle grain boundaries into high-angle grain boundaries. The previous conclusion was drawn from observing the simultaneous decrease in the fraction of low-angle grain boundaries and an increase in the fraction of high-angle grain boundaries. The pole figures revealed that 4-Bc, 4-A, and 4-C reduced the maximum texture intensity of the as-annealed billets. The potentiodynamic polarization findings revealed that route Bc is the most effective route in improving the corrosion rate, whereas the Electrochemical Impedance Spectroscopy (EIS) revealed that routes A and Bc improved the corrosion resistance with nearly identical values. Finally, 4-Bc resulted in the highest increase in Vickers hardness, yield stress, and ultimate tensile strength with values of 80.8%, 19.3%, and 44.5%, alongside a 31% improvement in ductility, all compared to the AA condition.

This study comprehensively investigates the impact of various parameters on aluminum matrix composites (AMCs) fabricated using the powder metallurgy (PM) technique. An Al-Cu matrix composite (2xxx series) was employed in the current study, and Al₂O₃ was used as a reinforcement. The performance evaluation of the Al-4Cu/Al₂O₃ composite involved analyzing the influence of the Al₂O₃ weight percent (wt. %), the height-to-diameter ratio (H/D) of the compacted samples, and the compaction pressure. Different concentrations of the Al₂O₃ reinforcement, namely 0%, 2.5%, 5.0%, 7.5%, and 10% by weight, were utilized, while the compaction process was conducted for one hour under varying pressures of 500, 600, 700, 800, and 900 MPa. The compacted Al-4Cu/Al₂O₃ composites were in the form of cylindrical discs with a fixed diameter of 20 mm and varying H/D ratios of 0.75, 1.0, 1.25, 1.5, and 2.0. Moreover, the machine learning (ML), design of experiment (DOE), response surface methodology (RSM), genetic algorithm (GA), and hybrid DOE-GA methodologies were utilized to thoroughly investigate the physical properties, such as the relative density (RD), as well as the mechanical properties, including the hardness distribution, fracture strain, yield strength, and compression strength. Subsequently, different statistical analysis approaches, including analysis of variance (ANOVA), 3D response surface plots, and ML approaches, were employed to predict the output responses and optimize the input variables. The optimal combination of variables that demonstrated significant improvements in the RD, fracture strain, hardness distribution, yield strength, and compression strength of the Al-4Cu/Al₂O₃ composite was determined using the RSM, GA, and hybrid DOE-GA approaches. Furthermore, the ML and RSM models were validated, and their accuracy was evaluated and compared, revealing close agreement with the experimental results.