In this study, chitosan was chemically modified with 2-methylpyridine. Subsequently, the modified chitosan was cross-linked to cellulose using succinic anhydride. Additionally, the capacity of cellulose derivatives to adsorb Pb(II) ions in an aqueous solution was studied through the determination of Pb(II) ions concentration in water, using microwave plasma atomic emission spectroscopy (MP-AES). A maximum adsorption capacity of 6.62, 43.14, 60.6, and 80.26 mg/g was found for cellulose, cellulose-succinic acid, cellulose-chitosan, and cellulose-chitosan-pyridine, respectively. The kinetic data analysis of the adsorption process showed a pseudo-second-order behavior. The increase in metal removal from water is possibly due to metal chelation with the carbonyl group of succinic acid, and the pyridine groups incorporated into chitosan.

Conventional cancer therapies suffer from nonspecificity, drug resistance, and a poor bioavailability, which trigger severe side effects. To overcome these disadvantages, in this study, we designed and evaluated the in vitro potential of paclitaxel-loaded, PLGA-gold, half-shell nanoparticles (PTX-PLGA/Au-HS NPs) conjugated with cyclo(Arg-Gly-Asp-Phe-Lys) (cyRGDfk) as a targeted chemo-photothermal therapy system in HeLa and MDA-MB-231 cancer cells. A TEM analysis confirmed the successful gold half-shell structure formation. High-performance liquid chromatography showed an encapsulation efficiency of the paclitaxel inside nanoparticles of more than 90%. In the release study, an initial burst release of about 20% in the first 24 h was observed, followed by a sustained drug release for a period as long as 10 days, reaching values of about 92% and 49% for NPs with and without near infrared laser irradiation. In in vitro cell internalization studies, targeted nanoparticles showed a higher accumulation than nontargeted nanoparticles, possibly through a specific interaction of the cyRGDfk with their homologous receptors, the ανβ3 y ανβ5 integrins on the cell surface. Compared with chemotherapy or photothermal treatment alone, the combined treatment demonstrated a synergistic effect, reducing the cell viability to 23% for the HeLa cells and 31% for the MDA-MB-231 cells. Thus, our results indicate that these multifuncional nanoparticles can be considered to be a promising targeted chemo-photothermal therapy system against cancer.

The versatile combination of metal nanoparticles with chemotherapy agents makes designing multifunctional drug delivery systems attractive. In this work, we reported cisplatin’s encapsulation and release profile using a mesoporous silica-coated gold nanorods system. Gold nanorods were synthesized by an acidic seed-mediated method in the presence of cetyltrimethylammonium bromide surfactant, and the silica-coated state was obtained by modified Stöber method. The silica shell was modified first with 3-aminopropyltriethoxysilane and then with succinic anhydride to obtain carboxylates groups to improve cisplatin encapsulation. Gold nanorods with an aspect ratio of 3.2 and silica shell thickness of 14.74 nm were obtained, and infrared spectroscopy and ζ potential studies corroborated surface modification with carboxylates groups. On the other hand, cisplatin was encapsulated under optimal conditions with an efficiency of ~58%, and it was released in a controlled manner over 96 h. Furthermore, acidic pH promoted a faster release of 72% cisplatin encapsulated compared to 51% in neutral pH.

In the present study, arsenic, cadmium, lead, and manganese contamination in propolis was assessed. A total of 12 raw propolis samples were analysed using atomic emission spectrometry with inductively coupled plasma (ICP-OES) for each of the metals. The analyses revealed that the samples were contaminated with each of the following metals: arsenic (ranging from <0.21 to 0.4 ppm), cadmium (<0.008 to 0.123 ppm), lead (0.580 to 117.01 ppm), and manganese (4.22 to 47.57 ppm). Lead levels exceeded the acceptable limits for consumption. A chemometric characterization was performed, looking at the correlation between elemental contamination, showing high correlation between cadmium and manganese levels (r = 0.80). Furthermore, the samples with the highest contamination levels were in areas with high industrial and agricultural activity. A risk assessment for toxic metals indicated a risk associated with lead. While the amount of lead present in the propolis samples was deemed to pose a low carcinogenic risk, it is noteworthy that the levels of the other metals detected do not pose any discernible health risk associated with the consumption of propolis. This conclusion is crucial for understanding the safety profile of propolis as a dietary supplement or natural product.