Making construction waste into raw materials for recycled concrete is beneficial for resource conservation and environmental protection. This paper investigated the effects of different recycled brick aggregate (RBA) replacement rates (30%, 50%, 70%, and 100%) and different contents of polypropylene fibers (PPFs) (0.08%, 0.10%, 0.12%, 0.16%, and 0.2%) on the mechanical properties of recycled brick concrete. Gray correlation was also used to analyze the degree of effect factors on the mechanical properties of concrete. The results showed that the mechanical properties decreased when the natural coarse aggregate (NCA) was replaced with RBA, while PPFs could better improve the mechanical properties of RBA concrete. The improvement of compressive and flexural properties was optimal when the PPF content was 0.12%; the improvement of tensile properties was optimal when the PPF content was 0.2%. In addition, PPFs significantly improved the toughness of RBA concrete. The gray correlation degrees between compressive strength (tensile strength, flexural strength) and NCA, RBA, and PPFs were 0.8964 (0.8691, 0.8935), 0.7301 (0.6530, 0.7074), and 0.5873 (0.5870, 0.5840), respectively.

Signal processing and analysis of structural vibration measurements are key components of structural damage detection (SDD) in structural health monitoring (SHM). The goal of signal processing is to extract subtle changes in the measured signals, which can be used to infer changes in structural parameters and damage. Time-frequency analysis is one of the most popular characterization methods for studying non-stationary vibration signals. In this article, the local time-frequency transform (LTFT) is applied and evaluated to calculate the time-domain signals because of its excellent time-frequency energy distribution properties. The LTFT matches the input data by the Fourier basis in an inverse problem framework and uses the least squares method to solve the time-varying Fourier coefficients. Subsequently, it defines the time-frequency spectrum as the calculated time-varying Fourier coefficients. While the LTFT has been used in the field of geophysics for seismic data processing, its application to structural vibration signals is novel. Both synthetic signals as well as signals collected from a large-scale laboratory test of a reinforced concrete girder were processed with the LTFT and compared with Rényi entropy for quantifying the time-frequency spectrum, the time-frequency resolution abilities of short time Fourier transform (STFT), and S transform (ST). The results show that the LTFT is superior to the traditional time-frequency analysis schemes, in that it is more effective in identifying the energy changes in the time-frequency spectrum before and after structural damage in the form of cracking has occurred. At the same time, it provides high-precision time-frequency resolution and excellent noise suppression abilities. The effectiveness and feasibility of the LTFT applied to the synthetic and experimental signals are verified.

A basalt fiber-reinforced asphalt mixture can improve the engineering properties of asphalt pavement and prolong the service life of the road. However, few studies have systematically examined the composition of asphalt mixtures or the optimal ratio of fiber asphalt mastic suitable for different structural types. The effects of fiber content, filler–asphalt ratio, and asphalt viscosity on the properties of fiber asphalt mastic were investigated by orthogonal experiments to explore the reinforcement effect of basalt fiber on asphalt mastic. The optimal ratio of fiber asphalt mastic suitable for gap-graded and dense-graded asphalt mixtures was obtained by the fuzzy comprehensive evaluation (FCE) method. Meanwhile, the reinforcement effects of bundled basalt fiber (BBF), flocculated basalt fiber (FBF), polyester fiber (PF), and lignin fiber (LF) on asphalt mastic were compared and analyzed based on the optimal ratio of FBF asphalt mastic. The results showed that the optimal fiber asphalt mastic ratio suitable for gap-graded and dense-graded asphalt mixtures were that fiber content, filler–asphalt ratio, and asphalt viscosity were 3%, 1.8, and 1.1 Pa·s and 2%, 1.0, and 0.7 Pa·s, respectively. Analyzing the properties of different types of fiber asphalt mastic revealed that FBF could effectively enhance the high-temperature rheological properties and low-temperature tensile properties of asphalt mastic compared with other fibers. FBF asphalt mastic improved the asphalt rutting factor by more than four times. The tensile fracture energy of fiber asphalt mastic was more than three times that of the corresponding asphalt. The reinforcement effect of BBF was poor; it was recommended to be broken up before use.

In order to improve the mechanical properties and deformation characteristics of permeable concrete, glass fiber was added to this type of concrete. Based on an unconfined compressive strength test, non-contact full-field strain measurement system, and scanning electron microscopy test, the effects of aggregate particle composition, shaking time, fly ash content, fiber length, and fiber content on the strength and permeability of permeable concrete were studied. The results show that the strength and water permeability of permeable concrete are negatively correlated with an increase in shaking time. When the aggregate particle size is 5–10 mm, the permeable concrete has both good strength and permeability. Proper incorporation of fly ash improves the compactness inside the structure. The influence of different lengths of glass fiber on the strength of permeable concrete first increases and then decreases, and the permeable property decreases. With the same fiber length, the strength increases first and then decreases with an increase in the content, while the porosity and water permeability coefficient decrease. Under the test conditions, when the length of glass fiber is 6 mm, and the dosage is 2 kg/m³, the strength performance of permeable concrete is the best, and the permeability effect is good at the same time.

In this paper, permeable geopolymer concrete with high compressive strength and permeability is prepared using alkali-activated metakaolin as a slurry, and its mechanical properties are reinforced by adding steel fibers. The influencing factors of the strength, porosity and permeability coefficient of the fiber-reinforced permeable geopolymer concrete, as well as its microstructure and curing mechanism, are determined by conducting an unconfined compressive strength test, scanning electron microscopy, energy-dispersive spectroscopy and X-ray diffraction. The test results show that, under the water permeability required to meet the specification conditions, when the alkali activator modulus is 1.4 and the activation-to-solid ratio is 0.9, the effect of metakaolin activation is the most obvious, and the unconfined compressive strength of the permeable geopolymer concrete is the highest. Moreover, the paste formed via the alkali activation of metakaolin contains a large number of silica–oxygen and aluminum–oxygen bonds with a dense and crack-free structure, which enables the paste to tightly combine with the aggregates; the strength of the permeable geopolymer concrete is early strength, and its strength at a curing age of 3 days is the highest. The strength at a curing age of 3 days can reach 43.62% of the 28-day strength; the admixture of steel fiber can effectively improve the strength of the permeable concrete, and with an increase in the amount of admixture, the strength of the fiber shows a trend of increasing, and then decreasing. Under the conditions of this test, a volume of steel fiber of 0.3% enables the optimum unconfined compressive strength to be reached.

Benefiting from low cost, high tensile strength, chemical stability, and great resistance to temperature, alkaline, and acids, it is a reasonable and valuable technology to use basalt fiber (BF) as an admixture to optimize building materials. So far, the challenge is still to master the engineering performance of BF-reinforced materials, especially poor subgrade soils. To this end, this paper carried out a series of unconfined compressive strength (UCS) tests, splitting tensile strength (STS) tests, and scanning environmental microscope (SEM) tests to study the mechanical properties and microstructure mechanism of BF-reinforced subgrade cemented silty sand with different fiber contents and curing times. The aims of this research were: (i) the UCS and STS of basalt fiber reinforced uncemented silty sand (BFUSM) and basalt fiber reinforced cemented silty sand (BFCSM) both increased with the increase of curing time and the strength reached the maximum value after curing for 28 days; (ii) the optimal fiber content was 0.2%, and a good linear correlation existed between UCS and STS; (iii) from the microscopic point of view, the combination of BF and cement could combine the physical action of fiber reinforcement and the chemical action of cement hydration reaction to form a fiber-cement-soil skeleton structure to improve the strength of silty sand and the improvement effect after working together was better than separately incorporated BF or cement; and (iv) the corresponding developed multiple nonlinear regression (MNLR) models which can well predict UCS and STS of BFUSM and BFCSM were established.