In order to improve the mechanical properties and deformation characteristics of permeable concrete, glass fiber was added to this type of concrete. Based on an unconfined compressive strength test, non-contact full-field strain measurement system, and scanning electron microscopy test, the effects of aggregate particle composition, shaking time, fly ash content, fiber length, and fiber content on the strength and permeability of permeable concrete were studied. The results show that the strength and water permeability of permeable concrete are negatively correlated with an increase in shaking time. When the aggregate particle size is 5–10 mm, the permeable concrete has both good strength and permeability. Proper incorporation of fly ash improves the compactness inside the structure. The influence of different lengths of glass fiber on the strength of permeable concrete first increases and then decreases, and the permeable property decreases. With the same fiber length, the strength increases first and then decreases with an increase in the content, while the porosity and water permeability coefficient decrease. Under the test conditions, when the length of glass fiber is 6 mm, and the dosage is 2 kg/m³, the strength performance of permeable concrete is the best, and the permeability effect is good at the same time.

In this study, research on a pile group system was conducted using shaking table tests under four working conditions: a natural foundation and pile-spacing conditions of 3D, 3.5D, and 4D (D is the diameter of the pile). The time histories of the excess pore pressure ratio and settlement were analyzed. It was determined that pile foundations improved the anti-liquefaction performance of the soil, and the effect was much greater when the pile spacing was 3D. In addition, the settlement dynamic amplification factor (SDAF) was proposed and calculated at different vibration times. The result was fitted with a linear relationship, and the correlation coefficient was relatively high. During the aseismic design of the pile foundation bearing capacity, the SDAF was multiplied by the static load, and the results showed that in the dynamic design of the pile foundation, the dynamic problem can be transformed into a static analysis, which can provide a reference for the design of the vertical bearing capacity of pile foundations under seismic force.

Composite pile foundation has been widely used in ground engineering. This composite pile foundation system has complex pile-soil interactions under seismic loading. The calculation of vertical bearing capacity of composite pile foundation is still an unsolved problem if the soil around piles is partially or completely liquefied under seismic loading. We have completed indoor shaking table model tests to measure the vertical bearing capacity in a liquefiable soil foundation under seismic loading. This paper will use a numerical approach to analyze the change of this vertical bearing capacity under seismic loading. Firstly, the Goodman contact element is improved to include the Rayleigh damping. Such an improvement can well describe the reflection and absorption of seismic waves at the interface of soil and piles. Secondly, the Biot’s dynamic consolidation theory incorporated an elastoplastic model is applied to simulate the soil deformation and the generation and accumulation of pore water pressure under seismic loading. Thirdly, after verification with our indoor shaking table test data, this approach is used to investigate the effects of pile spacing on liquefaction resistance of the composite pile foundation in liquefiable soil. The time histories of pore water pressure ratio (PPR′) are calculated for the liquefiable soil and the vertical bearing capacity in partially liquefied soil is calculated and compared with our indoor shaking table test data at the 3D, 3.5D, 4D, 5D and 6D cases (D is the pile diameter). It is found that the pile spacing has some influence on the extent of soil liquefaction between piles. The vertical bearing capacity varies with liquefaction extent of inter-pile soil. The optimization of pile spacing varies with liquefaction extent. These results may provide some reference for the design of composite pile foundation under seismic loading.

In this paper, permeable geopolymer concrete with high compressive strength and permeability is prepared using alkali-activated metakaolin as a slurry, and its mechanical properties are reinforced by adding steel fibers. The influencing factors of the strength, porosity and permeability coefficient of the fiber-reinforced permeable geopolymer concrete, as well as its microstructure and curing mechanism, are determined by conducting an unconfined compressive strength test, scanning electron microscopy, energy-dispersive spectroscopy and X-ray diffraction. The test results show that, under the water permeability required to meet the specification conditions, when the alkali activator modulus is 1.4 and the activation-to-solid ratio is 0.9, the effect of metakaolin activation is the most obvious, and the unconfined compressive strength of the permeable geopolymer concrete is the highest. Moreover, the paste formed via the alkali activation of metakaolin contains a large number of silica–oxygen and aluminum–oxygen bonds with a dense and crack-free structure, which enables the paste to tightly combine with the aggregates; the strength of the permeable geopolymer concrete is early strength, and its strength at a curing age of 3 days is the highest. The strength at a curing age of 3 days can reach 43.62% of the 28-day strength; the admixture of steel fiber can effectively improve the strength of the permeable concrete, and with an increase in the amount of admixture, the strength of the fiber shows a trend of increasing, and then decreasing. Under the conditions of this test, a volume of steel fiber of 0.3% enables the optimum unconfined compressive strength to be reached.

Pile foundation is a commonly recognized form of foundation, and earthquakes are a common seismic damage phenomenon. Accidents resulting from reduction in pile bearing capacity due to earthquakes pose a great threat to people’s lives and safety. This article investigates the interaction between soil and piles under earthquake action. Utilizing the MIDAS GTS NX finite element software, the vertical bearing characteristics of piles under earthquake action are studied. Obtained acceleration of piles, pile settlement, pile axial force, pile top horizontal displacement, soil pore water pressure, and pore pressure ratio under different earthquake magnitudes. The research results indicate that as the depth increases, the acceleration at the pile top is significantly greater than that at the pile bottom, with an average increase of 20% in acceleration at three different earthquake magnitudes; Both the beginning of the pore pressure ratio growth and the ultimate reaching of its stable pore pressure ratio coincide with a rise in earthquake magnitude. Additionally, the axial force of the pile body also increases with the magnitude of the earthquake, and the maximum axial force of the pile body can increase by 40% at the same time. Simultaneously, the magnitude of the earthquake influences both the displacement of the pile body and the settling of the pile top. This article can provide reference for pile foundation design and engineering construction in liquefaction sites.

In this article, the ABAQUS finite element software is used to simulate the bond behavior of the steel bar in salt–frost-damaged recycled coarse aggregate concrete, and the influence of the steel bar diameter and the concrete cover thickness on the bond strength is investigated. The result shows that the calculated bond–slip curve is in good agreement with the experimental bond–slip curve; the mean value of the ratio of the calculation results of ultimate bond strength to the experiment results of ultimate bond strength is 1.035, the standard deviation is 0.0165, and the coefficient of variation is 0.0159, which proves that the calculation results of the ultimate bond strength are in good agreement with the experimental results; with the increase of steel bar diameter and the concrete cover thickness, the ultimate bonding strength of RAC and steel increases; the calculation formulas for the ultimate bond strength of specimens with different steel bar diameters (concrete cover thickness) after different salt–frost cycles are obtained.