For environmental applications, nanosized TiO₂-based materials are known as the most important photocatalyst and are intensively studied for their advantages such as their higher activity, lower price, and chemical and photoresist properties. Zn or Cu doped TiO₂ nanoparticles with anatase crystalline structure were synthesized by sol−gel process. Titanium (IV) butoxide was used as a TiO₂ precursor, with parental alcohol as a solvent, and a hydrolysing agent (ammonia-containing water) was added to obtain a solution with pH 10. The gels were characterized by TG/DTA analysis, SEM, and XPS. Based on TG/DTA results, the temperature of 500 °C was chosen for processing the powders in air. The structure of the samples thermally treated at 500 °C was analysed by XRD and the patterns show crystallization in a single phase of TiO₂ (anatase). The surface of the samples and the oxidation states was investigated by XPS, confirming the presence of Ti, O, Zn and Cu. The antibacterial activity of the nanoparticle powder samples was verified using the gram−positive bacterium Staphylococcus aureus. The photocatalytic efficiency of the doped TiO₂ nanopowders for degradation of methyl orange (MO) is here examined in order to evaluate the potential applications of these materials for environmental remediation.

The tin-doped TiO₂ powders obtained by sol-gel and microwave-assisted sol-gel methods were investigated. The synthesis took place in a basic medium (pH 10, ammonium hydroxide, 25%) starting from tetrabutyl orthotitanate in its parental alcohol. In the case of the dopant, Tin(II) 2-ethylhexanoate as SnO₂ precursor was used in the amount of 1, 2, or 4 mol % SnO₂. Based on thermal analysis data, the powders were thermally treated in air, at 500 °C. The comparative investigation of the structure and morphology of the nanopowders annealed at 500 °C was performed by scanning electron microscopy (SEM), high-resolution transmission electron microscopy with selected area electron diffraction (HRTEM/SAED), scanning transmission electron microscopy (STEM) coupled with EDX mapping, Fourier transmission infrared (FTIR), UV–Vis, Raman and photoluminescence (PL) spectroscopy, X-ray diffraction (XRD), and X-ray florescence spectroscopy (XRF). The obtained materials were tested for the photocatalytic removal of methyl orange dye from aqueous solutions. High degradation efficiencies (around 90%) were obtained by Sn doping after 3 h of UV light irradiation.

Multifunctional composite coatings composed of metal oxide nanoparticles dispersed in polymer matrices are an advanced solution to solve the problem of stone heritage deterioration. Their innovative design is meant to be stable, durable, transparent, easy to apply and remove, non-toxic, hydrophobic, and permeable. Coating formulations for the protection of buildings and monuments have been intensively researched lately. Such formulations are based on multifunctional composite coatings incorporating metal oxides. The present work aims to combine the hydrophobic properties of sodium polyacrylate (NaPAC₁₆) with the antimicrobial effectiveness, with promising antimicrobial results even in the absence of light, and good compatibility of MgO (a safe to use, low cost and environmentally friendly material) and TiO₂ (with antibacterial and antifungal properties), in order to develop coatings for stone materials protection. MgO (pure phase periclase) and TiO₂ (pure phase anatase) nanopowders were prepared through sol–gel method, specifically routes. Aqueous dispersions of hydrophobically modified polymer (NaPAC₁₆, polyacrylic acid sodium salt) and MgO/TiO₂ nanopowders were deposited through layer-by-layer dip coating technique on glass slides and through immersion on stone fragments closely resembling the mosaic stone from the fourth century AD Roman Mosaic Edifice, from Constanta, Romania. The oxide nanopowders were characterized by: Thermal analysis (TG/DTA), scanning electron microscopy (SEM), X-ray diffraction (XRD), BET specific surface area and porosity, and UV–Vis spectroscopy for band gap determination. An aqueous dispersion of modified polyacrylate polymer and oxide nanopowders was deposited on different substrates (glass slides, red bricks, gypsum mortars). Film hydrophobicity was verified by contact angle measurements. The colour parameters were evaluated. Photocatalytic and antimicrobial activity of the powders and composite coatings were tested.

Magnesium oxide (MgO) was synthesized by three different methods: the sol–gel (SG), microwave-assisted sol–gel (MW), and hydrothermal (HT) methods for comparing the influence of the preparation conditions on the properties of the products. The powders were annealed at 450 °C. The samples were characterized by X-ray diffraction, scanning electron microscopy (SEM), transmission electron microscopy (TEM/HRTEM), selected area electron diffraction (SAED), energy-dispersive X-ray spectroscopy (EDX), BET specific surface area and porosity, photoluminescence, and UV–Vis spectroscopy. The samples consisted mainly of periclase as a crystalline phase, and the MW and HT preparation methods generated particles with higher specific surface areas. The powders had less-defined morphologies and high levels of aggregation. The optical band gaps of the samples were determined from UV DRS, and the photocatalytic activities of the magnesium oxides obtained by the three methods towards the degradation of methyl orange (MO) under UV light irradiation was evaluated.