The FeCoNiCrMo_0.5Al_x system with x up to 2.13 was analyzed from the point of view of evolution of the phase composition and microstructure. Cast samples were synthesized by induction melting and analyzed by X-ray diffraction, energy dispersive spectroscopy, scanning electron microscopy, and Vickers microhardness test methods. Phase compositions of these alloys in dependance on Al concentration consist of FCC solid solution, σ-phase, NiAl-based B2 phase, and BCC solid solution enriched with Mo and Cr. Phase formation principles were studied. Al dissolves in a FeCoNiCrMo_0.5 FCC solid solution up to 8 at.%.; at higher concentrations, Al attracts Ni, removing it from FCC solid solution and forming the B2 phase. Despite Al not participating in σ-phase formation, an increase in Al concentration to about 20 at.% leads to a growth in the σ-phase fraction. The increase in the σ-phase was caused by an increase in the amount of B2 because the solubility of σ-forming Mo and Cr in B2 was less than that in the FCC solution. A further increase in Al concentration led to an excess of Mo and Cr in the solution, which formed a disordered BCC solid solution. The hardness of the alloys attained the maximum of 630 HV at 22 and 32 at.% Al.

Triboelectric nanogenerators (TENGs), as novel electronic devices for converting mechanical energy into electrical energy, are better suited as signal-testing sensors or as components within larger wearable Internet of Things (IoT) or Artificial Intelligence (AI) systems, where they handle small-device power supply and signal acquisition. Consequently, TENGs hold promising applications in self-powered sensor technology. As global energy supplies become increasingly tight, research into self-powered sensors has become critical. This study presents a self-powered sport sensor system utilizing a triboelectric nanogenerator (TENG), which incorporates a thermoplastic polyurethane (TPU) film doped with graphene and polytetrafluoroethylene (PTFE) as friction materials. The graphene-doped TPU nanocomposite film-based TENG (GT-TENG) demonstrates excellent working durability. Furthermore, the GT-TENG not only consistently powers an LED but also supplies energy to a sports timer and an electronic watch. It serves additionally as a self-powered sensor for monitoring human movement. The design of this self-powered motion sensor system effectively harnesses human kinetic energy, integrating it seamlessly with sport sensing capabilities.

The pursuit of eco-friendly and renewable power generation has driven technological breakthroughs in nanoscale engineering, particularly regarding triboelectric nanogenerators (TENGs). These devices have become a focus of interest due to their capacity to effectively transform kinetic energy into electrical power via combined triboelectrification and electrostatic charge separation mechanisms. TENGs now find expanding implementations across multiple fields including in flexible electronics, autonomous sensing systems, and ambient energy conversion technologies. Enhancing TENG performance critically depends on the strategic design and application of nanostructures and nanomaterials. Nonetheless, challenges such as material selection, compatibility, homogeneous dispersion, interfacial stability, and production scalability must be overcome to advance TENG technology. Moreover, the mechanisms by which nanomaterials contribute to the triboelectric effect remain insufficiently understood, underscoring the necessity for systematic theoretical models. This review provides a comprehensive overview of recent advancements in integrating nanostructures and nanomaterials into TENGs, elucidating their roles, advantages, and underlying mechanisms in enhancing energy conversion efficiency, while identifying key challenges and proposing future research directions.

In the present study, powder of FeCoCrNiMo_0.5Al_1.3 HEA was manufactured by gas atomization process, and then used for laser powder bed fusion (L-PBF) and microplasma spraying (MPS) technologies. The processes of phase composition and microstructure transformation during above mentioned processes and subsequent heat treatment were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and differential thermal analysis (DTA) methods. It was found that gas atomization leads to a formation of dendrites of body centered cubic (BCC) supersaturated solid solution with insignificant Mo-rich segregations on the peripheries of the dendrites. Annealing leads to an increase of element segregations till to decomposition of the BCC solid solution and formation of σ-phase and B2 phase. Microstructure and phase composition of L-PBF sample are very similar to those of the powder. The MPS coating has a little fraction of face centered cubic (FCC) phase because of Al oxidation during spraying and formation of regions depleted in Al, in which FCC structure becomes more stable. Maximum hardness (950 HV) is achieved in the powder and L-PBF samples after annealing at 600 °C. Elastic modulus of the L-PBF sample, determined by nanoindentation, is 165 GPa, that is 12% lower than that of the cast alloy (186 GPa).

An important direction in the development of additive technologies is associated with the addition of ceramic particles (oxide, carbide, boride, and nitride ceramics) to metal powders. The prediction of the physical and mechanical characteristics of SiC-particle-reinforced composite materials (PRCMs) in comparison with experimental results was studied. A near-α Ti-4.25Al-2V titanium-alloy-based composite reinforced by 1 vol.% of SiC ceramic particles was produced using laser direct energy deposition. A multiscale modeling approach at the micro and macro levels was applied. At the micro level, the toughness and strength characteristics for a temperature interval of T = 20–450 °C were predicted using a representative volume element of PRCM with the nearly real shape of SiC particles. At the macro level, the features of plastic deformation and fracture of the PRCM were predicted by numerical modeling using the commercial software Digimat Student Edition ver. 2022.4 and Ansys Student 2023 R2. The addition of SiC particles was found to improve the physical and mechanical properties in the whole temperature range. The results of the numerical modeling were consistent with the experimental data (the deviation did not exceed 10%). The proposed approach for predicting the physical and mechanical properties of Ti-4.25Al-2V/SiC can also be used for other PRCMs obtained by laser direct energy deposition.