The aim of this research is to determine the relaxation and creep modulus of 3D printed materials, and the numerical research is based on the finite volume method. The basic material for determining these characteristics is ABS (acrylonitrile butadiene styrene) plastic as one of the most widely used polymeric materials in 3D printing. The experimental method for determining the relaxation functions involved the use of a creep test, in which a constant increase of the stress of the material was performed over time to a certain predetermined value. In addition to this test, DMA (dynamic mechanical analysis) analysis was used. Determination of unknown parameters of relaxation functions in analytical form was performed on the basis of the expression for the storage modulus in the frequency domain. The influence of temperature on the values of the relaxation modulus is considered through the determination of the shift factor. Shift factor is determined on the basis of a series of tests of the relaxation function at different constant temperatures. The shift factor is presented in the form of the WLF (Williams-Landel-Ferry) equation. After obtaining such experimentally determined viscoelastic characteristics with analytical expressions for relaxation modulus and shift factors, numerical analysis can be performed. For this numerical analysis, a mathematical model with an incremental approach was used, as developed in earlier works although with a certain modification. In the experimental analysis, the analytical expression for relaxation modulus in the form of the Prony series is used, and since it is the sum of exponential functions, this enables the derivation of a recursive algorithm for stress calculation. Numerical analysis was performed on several test cases and the results were compared with the results of the experiment and available analytical solutions. A good agreement was obtained between the results of the numerical simulation and the results of the experiment and analytical solutions.

In this study, a modified 3D printer hotend equipped with a load cell, attached to the feeding system, was used to evaluate the effects of filament material composition and printing parameters on the extrusion force required. Four different materials (commercial PLA, pure PLA, wood-PLA with different ratios of wood particles, and wood-PLA with different ratios of thermally modified wood particles) were used for 3D printing, and the feeding resistance was measured. The filament feeder was connected to the extruder hotend via a load cell, which measured the forces required to push the filament through the extruder and the nozzle. Three printing nozzle temperatures of 200, 210, and 220 °C were used. The results show that the printing temperature and the material influence the required extrusion forces, which varied between 1 and 8 N, but the variation was high. With proper optimization and integration into the printer firmware, this setup could also be used to detect nozzle clogging during printing, modify printing parameters during the process, and prevent the uneven extrusion of composite filaments.

This paper explores the possibility of using recycled seashells from marine coasts of the Mali Ston Bay in Dubrovnik-Neretva County, Croatia, to create a novel bio material derived from waste seashells. In this research, two types of waste seashells, mussel (Mytilus galloprovincialis) and oyster...

The scarcity of high-quality wood encouraged the development of various technological processes for joining wood. The finger joint is one of the most widespread technological processes for wood joining. This study aimed to determine the effect of steaming and heat modification of beech wood, as well as the type of adhesive, on the mechanical characteristics of finger joints. Samples made from un-modified beech, steamed-treated, and heat-treated beech wood were bonded with polyvinyl acetate (PVAC), non-structural, and structural polyurethane (PUR) adhesives. Compressive tests on wood materials were used to evaluate their mechanical performance. The finger joint samples were tested for their bending performance. Modulus of rupture, modulus of elasticity, and compressive strength were calculated. An analysis of variance (ANOVA) was conducted to evaluate the impact of wood modification type and adhesive used on the mechanical characteristics of the finger joints. According to the results of this study, it can be concluded that the steaming process does not influence changes in the mechanical characteristics of the finger joints. Heat treatment of beech and the type of adhesive used significantly influence the tested mechanical characteristics of the finger joints and beech wood. Heat-treated beech had lower values of modulus of rupture (70 MPa) and density (690 kg/m³) and higher values of compression strength (59 MPa) in relation to un-modified (780 kg/m³) and steamed-treated (800 kg/m³) beech wood.

Using the RadSawSim simulator for radial sawing, a simulation of the radial sawing technique was used to saw Pedunculata oak (Quercus robur L.) logs. Simulation was implemented with a view to producing as many radially sawn boards as possible and took into account the influences of increasing volume yield, lumber value yield, and log-value yield. The methods that were analyzed were live sawing and radial sawing of third sections, fourth sections, fifth sections, and sixth sections of the log. Live sawing achieved the best results of volume yield during simulation, which was followed by radial sawing into the third, fourth, fifth, and sixth sections. The difference in volume yield with live sawing compared to the radial-sawing method is very large for logs up to a diameter of 45 cm. It becomes smaller when the log diameter is greater than 45 cm. A comparison of the radial method shows that the share of radially sawn boards and lumber value yield increased when the number of log sections during sawing simulation increased. If log-value yield is assumed to be the main criterion, and given the conditions used in this simulation, there is no justified reason to saw logs using the radial technique when the diameter is less than 45 cm. The live sawing technique is more efficient for these diameters of logs, and, therefore, the radial sawing technique is more efficient for logs with a diameter greater than 45 cm.