The widespread use of single-use face masks during the recent epidemic has led to significant environmental challenges due to waste pollution. This study explores an innovative approach to address this issue by repurposing discarded face masks for hydrovoltaic energy harvesting. By coating the face masks with carbon black (CB) to enhance their hydrophilic properties, we developed mask-based hydrovoltaic power generators (MHPGs). These MHPGs were evaluated for their hydrovoltaic performance, revealing that different mask configurations and sizes affect their efficiency. The study found that MHPGs with smaller, more structured areas exhibited better energy output, with maximum open-circuit voltages (V_OC) reaching up to 0.39 V and short-circuit currents (I_SC) up to 65.6 μA. The integration of CB improved water absorption and transport, enhancing the hydrovoltaic performance. More specifically, MHPG-1 to MHPG-4, which represented different sizes and features, presented mean V_OC values of 0.32, 0.17, 0.19 and 0.05 V, as well as mean I_SC values of 16.57, 15.59, 47.43 and 3.02 μA, respectively. The findings highlight the feasibility of utilizing discarded masks in energy harvesting systems, offering both environmental benefits and a novel method for renewable energy generation. Therefore, this work provides a new paradigm for waste-to-energy (WTE) technologies and inspires further research into the use of unconventional waste materials for energy production.

Core–shell structured magnetic nanoparticles combine hard and soft phases to improve energy efficiency. The mutual interaction of the two phases can lead to the exchange spring effect, leading to higher magnetic energy. In this regard, synthesis of Nd₂Fe₁₄B-based core–shell-structured powders have proven to be elusive, due to the relatively reactive nature of this phase. In this study, a process has been established for successfully coating the surface of Nd₂Fe₁₄B powders with a FeCo layer using the galvanic displacement method. Initially, a binary phase magnetic powder was synthesized containing Nd₂Fe₁₄B and Nd₂Fe₁₇ phase. Subsequently, the powders were coated using a Co precursor at 303 K. During coating, the metastable Nd₂Fe₁₇ phase was dissolved, and the Fe ions were released into the solution. Subsequently, the Fe ions deposited together with the Co ions on the surface of Nd₂Fe₁₄B powder to form a FeCo shell. The deposited layer thickness and composition was confirmed using TEM analysis.

Hydroelectricity energy harvesting has emerged as a promising, eco-friendly alternative for addressing the growing demand for sustainable energy solutions. In this study, we present a hydroelectricity energy harvester fabricated from shredded waste printing paper (WPP), offering a novel waste-to-energy conversion strategy that requires neither material purification nor complex processing. The device leverages the randomly entangled fiber network of WPP to facilitate capillary-driven moisture diffusion and electric double layer (EDL) formation, thereby enabling efficient electrokinetic energy conversion. The random arrangement of WPP fibers increases the effective EDL area, allowing the waste printing paper generator (WPPG) to achieve an open-circuit voltage of 0.372 V and a short-circuit current of 135 μA at room temperature under optimized electrolyte conditions. This study demonstrates that carbon-black-coated WPP can be effectively upcycled into a high-performance hydroelectricity generator, exhibiting excellent electrical output at ambient conditions. By combining material recycling with efficient energy conversion, this system establishes a practical and sustainable pathway for distributed power generation. Overall, this work not only presents an environmentally responsible approach to device fabrication but also highlights that hydroelectricity energy harvesting using WPPG represents a promising alternative energy route for future applications.