Cementation of germanium from sulphate solution obtained after the leaching of GeIn dross using zinc dust was investigated. The composition of the examined solution was 5.15 Ge, 1.52 In, and 5.81 g/dm³ Zn. In order to resemble the solution before detinning, Sn concentration between 2–10 g/dm³ was also investigated. It was found that >99% of germanium may be precipitated from the solution. In order to achieve high selectivity, a detinned solution should be used because the precipitation yields of germanium and tin from the solution containing Sn were similar. For cementation with Zn powder at 75 °C for 2 h with a final pH of 2.0, over 99% of the germanium was removed from the solution, while the indium precipitation yield was 12%. The obtained cementate contained 50% Ge, mainly in elementary form.

Rhenium is an element that exhibits a broad range of oxidation states. Synthesis paths of selected rhenium compounds in its seventh oxidation state, which are common precursors for organic reaction catalysts, were presented in this paper. Production technologies for copper perrhenate, aluminum perrhenate as well as the ammonia complex of cobalt perrhenate, are thoroughly described. An ion exchange method, based on Al or Cu metal ion sorption and subsequent elution by aqueous perrhenic acid solutions, was used to obtain perrhenates. The produced solutions were neutralized to afford the targeted aluminum perrhenate and copper perrhenate products in high purity. The developed technologies allow one to manage the wastes from the production of these perrhenates as most streams were recycled. Hexaamminecobalt(III) perrhenate was produced by a newly developed method enabling us to produce a high purity compound in a reaction of spent hexaamminecobalt(III) chloride solution with a perrhenic acid. All prepared compounds are the basis for precursor preparation in organic catalysis.

This research aimed to evaluate the effectiveness of new organic substances, including a novel ionic liquid based on polyhexamethylenebiguanidine, polyhexamethyleneguanidine, and safranin in the copper electrorefining process. Experiments were conducted on a small laboratory scale using industrial copper anodes. Single doses of new additives did not improve process indicators (current efficiency, average cell voltage, specific energy consumption) or the quality of copper cathode deposits. However, a combination of a new ionic liquid based on polyhexamethylenebiguanidine and thiourea resulted in a satisfactory current efficiency of 97%, an average cell voltage of 0.110 V, a low specific energy consumption index of approximately 100 kWh/t_Cu, and smooth cathode surfaces. These results were superior to those obtained with industrial additives (bone glue and thiourea). The findings enhance our understanding of how these substances influence the electrorefining process and suggest the potential for more efficient and sustainable methods. Further research is recommended to validate these findings and explore their industrial applications.

This paper presents a method for obtaining cobalt(II) perrhenate from waste derived from two types of materials, i.e., Li-ion battery scrap, or more precisely, battery mass, and superalloy scrap. Both of the above-mentioned materials are a source of Co. However, a source of rhenium is perrhenic acid produced from ammonium perrhenate (recycled) by the ion exchange method using resins. Co(OH)₂ can be precipitated from solutions resulting from the leaching of Li-ion battery mass, sludge from the Zn-Pb industry and superalloy scrap. The compound, after proper purification, can be used in a reaction with perrhenic acid to form Co(ReO₄)₂. The reaction should be conducted under the following conditions: time 1 h, room temperature, 30% excess of cobalt(II) hydroxide, and rhenium concentration in HReO₄ from about 20 g/dm³ to 300 g/dm³. This work shows that with the use of Co(OH)_2, obtained from waste, an anhydrous form of cobalt(II) perrhenate can be obtained, containing < 1000 ppm of the cumulative metal impurities.

Lead can be efficiently electrodeposited from a number of common leaching agents such as mineral acids, carboxylic acids, and bases (hydroxides and ammonia). This paper reports the possibility to deposit lead from a triethylenetetramine solution, which is also a powerful extracting agent for lead sulfate. The high affinity of triethylenetetramine towards lead sulfate molecules makes it a promising candidate for lead recovery from various solid materials, including industrial secondary resources, sewages, and wastes. A popular methodology that can be found in the literature to recover metal from amine is based on purging a solution with carbon dioxide, resulting in lead carbonate precipitation. Here, the direct electrodeposition of lead from an amine solution was reported. The effects of the main process parameters, i.e., current density, temperature, and presence of additives, were examined to enhance the product quality. Bone glue, ethylene glycol, and polyvinylpyrolidone were used as perspective inhibitors of dendritic lead formation. It was shown that the addition of ethylene glycol can significantly reduce their formation as well as discoloration resulting from amine, producing lead metal with a 99.9% purity.

This work focused on purifying copper electrolytes from a bismuth impurity on a laboratory scale. The electrolyte came from Polish copper electrorefineries with the content of main components, g/dm³: 49.6 Cu, 160 H₂SO₄. The electrolyte was enriched in bismuth by Bi₂O₃ addition. Purification of bismuth contamination was carried out using selected agents with adsorbing effects, such as barium hydroxide octahydrate, strontium carbonate, barium carbonate, barium and lead sulfates. The trials were performed until achieving the Bi level—below 0.1 g/dm³. During the experiments, it was noticed that electrolyte purification degree depends on initial Bi concentration in electrolyte, time and temperature, as well as on the type and amount of the bismuth-lowering agent. The most satisfactory results of Bi impurity removal were with additions of barium hydroxide octahydrate, strontium carbonate and barium carbonate to electrolyte at 60 °C for 1 h. These parameters revealed the highest electrolyte purification degree. Bismuth is not removed effectively from electrolytes by barium sulfate or lead sulfate addition. The efficiency of the purification process is much higher when the agents are added to the solution in the form of carbonates or hydroxides. Extending the electrolyte purification process time may cause dissolution of bismuth from the resulting precipitate and increase of bismuth concentration in electrolytes.